Objectives: This study evaluated the effects of different surface conditioning methods on the bond strength of orthodontic brackets to glazed full-zirconia surfaces. Materials and Methods: Glazed zirconia (except for the control, Zirkonzahn Prettau) disc surfaces were pre-treated: PO (control), polishing; BR, bur roughening; PP, cleaning with a prophy cup and pumice; HF, hydrofluoric acid etching; AA, air abrasion with aluminum oxide; CJ, CoJet-Sand. The surfaces were examined using profilometry, scanning electron microscopy, and electron dispersive spectroscopy. A zirconia primer (Z-Prime Plus, Z) or a silane primer (Monobond-S, S) was then applied to the surfaces, yielding 7 groups (PO-Z, BR-Z, PP-S, HF-S, AA-S, AA-Z, and CJ-S). Metal bracket-bonded specimens were stored in water for 24 hr at 37℃, and thermocycled for 1,000 cycles. Their bond strengths were measured using the wire loop method (n = 10). Results: Except for BR, the surface pre-treatments failed to expose the zirconia substructure. A significant difference in bond strengths was found between AA-Z (4.60 ± 1.08 MPa) and all other groups (13.38 ± 2.57 - 15.78 ± 2.39 MPa, p < 0.05). For AA-Z, most of the adhesive remained on the bracket. Conclusions: For bracket bonding to glazed zirconia, a simple application of silane to the cleaned surface is recommended. A zirconia primer should be used only when the zirconia substructure is definitely exposed.
Abstract
Objectives: This study evaluated the effects of different surface conditioning methods on the bond strength of orthodontic brackets to glazed full-zirconia surfaces. Materials and Methods: Glazed zirconia (except for the control, Zirkonzahn Prettau) disc surfaces were pre-treated: PO (control), polishing; BR, bur roughening; PP, cleaning with a prophy cup and pumice; HF, hydrofluoric acid etching; AA, air abrasion with aluminum oxide; CJ, CoJet-Sand. The surfaces were examined using profilometry, scanning electron microscopy, and electron dispersive spectroscopy. A zirconia primer (Z-Prime Plus, Z) or a silane primer (Monobond-S, S) was then applied to the surfaces, yielding 7 groups (PO-Z, BR-Z, PP-S, HF-S, AA-S, AA-Z, and CJ-S). Metal bracket-bonded specimens were stored in water for 24 hr at 37℃, and thermocycled for 1,000 cycles. Their bond strengths were measured using the wire loop method (n = 10). Results: Except for BR, the surface pre-treatments failed to expose the zirconia substructure. A significant difference in bond strengths was found between AA-Z (4.60 ± 1.08 MPa) and all other groups (13.38 ± 2.57 - 15.78 ± 2.39 MPa, p < 0.05). For AA-Z, most of the adhesive remained on the bracket. Conclusions: For bracket bonding to glazed zirconia, a simple application of silane to the cleaned surface is recommended. A zirconia primer should be used only when the zirconia substructure is definitely exposed.
참고문헌 (27)
- Lifshitz AB, "A comparison between the shear bond strength of brackets bonded to glazed and deglazed porcelain surfaces with resin-reinforced glassionomer cement and a bis-GMA resin adhesive", World J Orthod, 7, pp.134~137 (2006)
- Trakyali G, "Effects of different silanes and acid concentrations on bond strength of brackets to porcelain surfaces", Eur J Orthod, 31, pp.402~406 (2009)
- Maryanchik I, "Shear bond strength of orthodontic brackets bonded to various esthetic pontic materials", Am J Orthod Dentofacial Orthop, 137, pp.684~689 (2010)
- Blakey R, "Effects of surface conditioning on the shear bond strength of orthodontic brackets bonded to temporary polycarbonate crowns", Am J Orthod Dentofacial Orthop, 138, pp.72~78 (2010)
- Abu Alhaija ES, "Shear bond strength of orthodontic brackets bonded to different ceramic surfaces", Eur J Orthod, 29, pp.386~389 (2007)
- Wang C, "Influence of surface treatments on the shear bond strength of orthodontic brackets to porcelain", Appl Surf Sci, 255, pp.416~418 (2008)
- Özcan M, "Bonding polycarbonate brackets to ceramic: effects of substrate treatment on bond strength", Am J Orthod Dentofacial Orthop, 126, pp.220~227 (2004)
- Kim MJ, "Shear bond strengths of various luting cements to zirconia ceramic:surface chemical aspects", J Dent, 39, pp.795~803 (2011)
- Shahin Kasraei, "Bond strength of resin cement to CO2 and Er:YAG laser-treated zirconia ceramic", Restorative Dentistry and Endodontics, 39(4), pp.296~302 (2014), 대한치과보존학회
- Komine F, "Bonding between layering materials and zirconia frameworks", Jpn Dent Sci Rev, 48, pp.153~161 (2012)
- Guess PC, "All-ceramic systems: laboratory and clinical performance", Dent Clin North Am, 55, pp.333~352 (2011)
- Zhang Y, "Graded structures for damage resistant and aesthetic all-ceramic restorations", Dent Mater, 25, pp.781~790 (2009)
- Fabianelli A, "The effect of different surface treatments on bond strength between leucite reinforced feldspathic ceramic and composite resin", J Dent, 38, pp.39~43 (2010)
- Victor Hugo dos Santos, "Bond strength of self-adhesive resin cements to composite submitted to different surface pretreatments", Restorative Dentistry and Endodontics, 39(1), pp.12~16 (2014), 대한치과보존학회[DOI]
- 하정윤, "Effect of Heat Treatment of Dental Zirconia Ceramic Treated with Three Different Primers on the Bonding Durability of Resin Cement", Macromolecular Research, 21(1), pp.71~77 (2013), 한국고분자학회[DOI]
- Shon WJ, "The effects of primer precuring on the shear bond strength between gold alloy surfaces and metal brackets", Eur J Orthod, 34, pp.72~76 (2012)
- Zachrisson YO, "Surface preparation for orthodontic bonding to porcelain", Am J Orthod Dentofacial Orthop, 109, pp.420~430 (1996)
- Goracci C, "Shear bond strength of orthodontic brackets bonded with a new self-adhering flowable resin composite", Clin Oral Investig, 17, pp.609~617 (2013)
- Mojtahedzadeh F, "Comparison of wire loop and shear blade as the 2 most common methods for testing orthodontic shear bond strength", Am J Orthod Dentofacial Orthop, 130, pp.385~387 (2006)
- Ryou DB, "Use of flowable composites for orthodontic bracket bonding", Angle Orthod, 78, pp.1105~1109 (2008)
- Magne P, "New zirconia primer improves bond strength of resin-based cements", Dent Mater, 26, pp.345~352 (2010)
- Al-Hity R, "In vitro orthodontic bracket bonding to porcelain", Eur J Orthod, 34, pp.505~511 (2012)
- Chaiyabutr Y, "The effect of hydrofluoric acid surface treatment and bond strength of a zirconia veneering ceramic", J Prosthet Dent, 100, pp.194~202 (2008)
- Preis V, "In vitro failure and fracture resistance of veneered and full-contour zirconia restorations", J Dent, 40, pp.921~928 (2012)
- Mitov G, "Wear behavior of dental Y-TZP ceramic against natural enamel after different finishing procedures", Dent Mater, 28, pp.909~918 (2012)
- de Oliveira AS, "A modified photoactivation protocol using two simultaneous light-curing units for bonding brackets to enamel", Braz Dent J, 26, pp.393~397 (2015)
- Ahn HB, "Analysis of surface roughness and surface free energy characteristics of various orthodontic materials", Am J Orthod Dentofacial Orthop, 136, pp.668~674 (2009)