Ellipso-Microscopic Observation of Titanium Surface under UV-Light Irradiation
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The ellipso-microscopic observation of a titanium surface undergoing anodization in 0.05 mol dm-3 of H2SO4was conducted. During irradiation by ultra-violet (UV) light with a wavelength of 325 nm, the titaniumsurface allowed for the flow of a photo-induced current and showed up as a bright, patch-like image onan ellipso-microscopic view. The brightness and patch-pattern in the image changed with flowing photo-inducedcurrent. The changes in the brightness and the image corresponded to the formation and/or degradationof titanium oxide due to the photo-electrochemical reaction of the oxide. An in situ monitoring using theellipso-microscope revealed that the film change was dependent on the irradiation light power, by UV-lightincreases the anodic current and results in the initiation of pitting at lower potentials as compared withthe non-irradiated condition.
Abstract
The ellipso-microscopic observation of a titanium surface undergoing anodization in 0.05 mol dm-3 of H2SO4was conducted. During irradiation by ultra-violet (UV) light with a wavelength of 325 nm, the titaniumsurface allowed for the flow of a photo-induced current and showed up as a bright, patch-like image onan ellipso-microscopic view. The brightness and patch-pattern in the image changed with flowing photo-inducedcurrent. The changes in the brightness and the image corresponded to the formation and/or degradationof titanium oxide due to the photo-electrochemical reaction of the oxide. An in situ monitoring using theellipso-microscope revealed that the film change was dependent on the irradiation light power, by UV-lightincreases the anodic current and results in the initiation of pitting at lower potentials as compared withthe non-irradiated condition.
참고문헌 (8)
- J. W. Schultze, , Ber. Bunsen. Phys. Chem, 86, pp.276~ (1982)
- T. Ohtsuka, , J. Electroanal. Chem, 473, pp.272~ (1999)
- K. Fushimi, , Electrochim. Acta, 144, pp.56~ (2014)
- T. Ohtsuka, , J. Electrochem. Soc, 132, pp.787~ (1985)
- T. Ohtsuka, , J. Electrochem. Soc, 133, pp.2473~ (1986)
- S. Kudelka, , Electrochim. Acta, 41, pp.863~ (1996)
- S. Kudelka, , Electrochim. Acta, 42, pp.2817~ (1997)
- K. Fushimi, , J. Electrochem. Soc, 147, pp.524~ (2000)