Characterization of the Manufacturing Process and Mechanical Properties of CoCrFeMnNi High-Entropy Alloys via Metal Injection Molding and Hot Isostatic Pressing
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
High-entropy alloys (HEAs) have been reported to have better properties than conventional materials; however, they are more expensive due to the high cost of their main components. Therefore, research is needed to reduce manufacturing costs. In this study, CoCrFeMnNi HEAs were prepared using metal injection molding (MIM), which is a powder metallurgy process that involves less material waste than machining process. Although the MIM-processed samples were in the face-centered cubic (FCC) phase, porosity remained after sintering at 1200°C, 1250°C, and 1275°C. In this study, the hot isostatic pressing (HIP) process, which considers both temperature (1150°C) and pressure (150 MPa), was adopted to improve the quality of the MIM samples. Although the hardness of the HIP-treated samples decreased slightly and the Mn composition was significantly reduced, the process effectively eliminated many pores that remained after the 1275°C MIM process. The HIP process can improve the quality of the alloy.
Abstract
High-entropy alloys (HEAs) have been reported to have better properties than conventional materials; however, they are more expensive due to the high cost of their main components. Therefore, research is needed to reduce manufacturing costs. In this study, CoCrFeMnNi HEAs were prepared using metal injection molding (MIM), which is a powder metallurgy process that involves less material waste than machining process. Although the MIM-processed samples were in the face-centered cubic (FCC) phase, porosity remained after sintering at 1200°C, 1250°C, and 1275°C. In this study, the hot isostatic pressing (HIP) process, which considers both temperature (1150°C) and pressure (150 MPa), was adopted to improve the quality of the MIM samples. Although the hardness of the HIP-treated samples decreased slightly and the Mn composition was significantly reduced, the process effectively eliminated many pores that remained after the 1275°C MIM process. The HIP process can improve the quality of the alloy
참고문헌 (43)
- M. Yue, , Renew. Sustain. Energy Rev, 146, pp.111180~ (2021)
- B. Gludovatz, , Science, 6201, pp.1153~ (2014)
- E. P. George, , Nat. Rev. Mater, 4, pp.515~ (2019)
- H. Luo, , Corros. Sci, 136, pp.403~ (2018)
- Y. Fu, , J. Mater. Sci. Technol, 80, pp.217~ (2021)
- Z. Pu, , Mater. Sci. Eng. A, 736, pp.156~ (2018)
- R. B. Mane, , Powder Metallurgy, 61, pp.131~ (2018)
- F. Otto, , Acta Mater, 112, pp.40~ (2016)
- E. S. Kim, , J. Alloys Compd, 942, pp.169062~ (2023)
- J. H. Kim, , Mater. Sci. Eng. A, 712, pp.108~ (2018)
- G. H. Gu, , Mater. Sci. Eng. A, 836, pp.142718~ (2022)
- S. Y. Ahn, , J. Alloys Compd, 960, pp.170602~ (2023)
- A. Piglione, , Mater. Lett, 224, pp.22~ (2018)
- G. M. Karthik, , Addit. Manuf, 59, pp.103131~ (2022)
- Z. Xu, , Addit. Manuf, 35, pp.101441~ (2020)
- G. M. Karthik, , Scr. Mater, 195, pp.113722~ (2021)
- Y. Zhang, , J. Alloys Compd, 868, pp.158711~ (2021)
- E. S. Kim, , J. Powder Mater, 30, pp.1~ (2023)
- A. O. Araoyinbo, , AIP Conf. Proc, 2437, pp.020153~ (2022)
- Injection Molding of Metals and Ceramics, "S. V. Atre", SAE, ~, pp.SAE Technical Paper (1998)982417 (1998)
- F. Ternero, , Metals, 11, pp.730~ (2021)
- D. F. Heaney, "Handbook of metal injection molding" (2018), Woodhead Publishing
- J. O. Andersson, , Calphad, 26, pp.273~ (2002)
- B. -J. Lee, "TCFE2000: The Thermo-Calc Steels Database" (1999), KTH
- W. -M. Choi, , J. Phase Equilibria Diffus, 39, pp.694~ (2018)
- W. -M. Choi, , Calphad, 66, pp.101624~ (2019)
- H. -S. Do, , J. Mater. Sci, 57, pp.1373~ (2022)
- H. -S. Do, , Mater. Sci. Eng. A, 859, pp.144220~ (2022)
- J. Čapek, , Mater. Sci. Eng. C, 43, pp.494~ (2014)
- E. S. Kim, , J. Alloys Compd, 907, pp.164415~ (2022)
- G. M. Karthik, , Addit. Manuf, 47, pp.102314~ (2021)
- M. J. Sagong, , Mater. Sci. Eng. A, 847, pp.143318~ (2022)
- E. S. Kim, , J. Mater. Sci, 57, pp.17967~ (2022)
- H. Kwon, , Intermetallics, 135, pp.107212~ (2021)
- A. E. Tekkaya, , CIRP Annals, 49, pp.205~ (2000)
- Z. Shen, , Acta Metall, 36, pp.3231~ (1988)
- F. Haftlang, , J. Mater. Process. Technol, 309, pp.117733~ (2022)
- H. Zhao, , Acta Mater, 156, pp.318~ (2018)
- E. Hryha, , Metall. Mater. Trans. A, 41, pp.2880~ (2010)
- M. Vaidya, , J. Alloys Compd, 774, pp.856~ (2019)
- M. Vaidya, , J. Alloys Compd, 791, pp.1114~ (2019)
- K. Guruvidyathri, , J. Alloys Compd, 768, pp.358~ (2018)
- S. Yang, , J. Alloys Compd, 916, pp.165477~ (2022)