Translucency and masking ability of translucent zirconia; comparison with conventional zirconia and lithium disilicate
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
PURPOSE. The purpose of this study is to evaluate translucency and masking ability of translucent zirconia compared to conventional zirconia and lithium disilicate materials. MATERIALS AND METHODS. Three types of zirconia blocks with different yttria contents (3Y, 4Y, 5.5Y) and LS blocks (Rosetta SM) were used. Ten specimens for each group were fabricated with 10 mm diameter, with both 0.8 mm and 1.5 mm thicknesses (± 0.02 mm). All groups of zirconia specimens were sintered and polished according to the manufacturer’s instructions. To calculate the translucency parameter (TP), CIELAB value was measured with a spectrophotometer on black and white backgrounds. To investigate the color masking abilities, background shades of A2, normal dentin, discolored dentin, and titanium were used. The color difference (ΔE) was calculated with the CIELAB values of A2 shade background as a reference compared with the values in the various backgrounds. One-way ANOVA and Bonferroni tests were conducted (P < .05). RESULTS. The TP values of zirconia specimens increased as the yttria content increased. All materials used in the study were able to adequately mask normal dentin shade (ΔE < 5.5), but were incapable of masking severely discolored dentin (ΔE > 5.5). On the titanium background, all materials of 1.5 mm thickness were able to mask the background shade, but with a thickness of 0.8 mm, only 3Y-TZP and 4Y-PSZ were able to mask titanium background. CONCLUSION. All zirconia materials and lithium disilicate specimens used in this study were unable to adequately mask the shade of severely discolored dentin. It is recommended to use 3Y-TZP or 4Y-PSZ with a sufficient thickness of 0.8 mm or more to mask titanium.
Abstract
PURPOSE. The purpose of this study is to evaluate translucency and masking ability of translucent zirconia compared to conventional zirconia and lithium disilicate materials. MATERIALS AND METHODS. Three types of zirconia blocks with different yttria contents (3Y, 4Y, 5.5Y) and LS blocks (Rosetta SM) were used. Ten specimens for each group were fabricated with 10 mm diameter, with both 0.8 mm and 1.5 mm thicknesses (± 0.02 mm). All groups of zirconia specimens were sintered and polished according to the manufacturer’s instructions. To calculate the translucency parameter (TP), CIELAB value was measured with a spectrophotometer on black and white backgrounds. To investigate the color masking abilities, background shades of A2, normal dentin, discolored dentin, and titanium were used. The color difference (ΔE) was calculated with the CIELAB values of A2 shade background as a reference compared with the values in the various backgrounds. One-way ANOVA and Bonferroni tests were conducted (P < .05). RESULTS. The TP values of zirconia specimens increased as the yttria content increased. All materials used in the study were able to adequately mask normal dentin shade (ΔE < 5.5), but were incapable of masking severely discolored dentin (ΔE > 5.5). On the titanium background, all materials of 1.5 mm thickness were able to mask the background shade, but with a thickness of 0.8 mm, only 3Y-TZP and 4Y-PSZ were able to mask titanium background. CONCLUSION. All zirconia materials and lithium disilicate specimens used in this study were unable to adequately mask the shade of severely discolored dentin. It is recommended to use 3Y-TZP or 4Y-PSZ with a sufficient thickness of 0.8 mm or more to mask titanium.
참고문헌 (35)
- Stawarczyk B, "Three generations of zirconia: From veneered to monolithic. Part I", Quintessence Int, 48, pp.369~380 (2017)
- Christensen GJ, "Choosing an all-ceramic restorative material : porcelain-fused-to-metal or zirconia-based?", J Am Dent Assoc, 138, pp.662~665 (2007)
- Vagkopoulou T, "Zirconia in dentistry: Part 1. Discovering the nature of an upcoming bioceramic", Eur J Esthet Dent, 4, pp.130~151 (2009)
- Shahmiri R, "Optical properties of zirconia ceramics for esthetic dental restorations : A systematic review", J Prosthet Dent, 119, pp.36~46 (2018)
- Denry I, "State of the art of zirconia for dental applications", Dent Mater, 24, pp.299~307 (2008)
- Stawarczyk B, "Comparison of four monolithic zirconia materials with conventional ones: Contrast ratio, grain size, four-point flexural strength and two-body wear", J Mech Behav Biomed Mater, 59, pp.128~138 (2016)
- Stawarczyk B, "Zirconia ceramics, their contrast ratio and grain size depending on sintering parameters", Dent Mater J, 33, pp.591~598 (2014)
- Stawarczyk B, "Three generations of zirconia:From veneered to monolithic. Part II", Quintessence Int, 48, pp.441~450 (2017)
- Church TD, "Translucency and strength of high-translucency monolithic zirconium oxide materials", Gen Dent, 65, pp.48~52 (2017)
- Kallaya Suputtamongkol, "Effect of the shades of background substructures on the overall color of zirconiabased all-ceramic crowns", The Journal of Advanced of Prosthodontics, 5(3), pp.319~325 (2013), 대한치과보철학회[DOI]
- Vichi A, "Color related to ceramic and zirconia restorations : a review", Dent Mater, 27, pp.97~108 (2011)
- Della Bona A, "Optical properties of CAD-CAM ceramic systems", J Dent, 42, pp.1202~1209 (2014)
- Bayindir F, "The effect of restoration thickness and resin cement shade on the color and translucency of a high-translucency monolithic zirconia", J Prosthet Dent, 123, pp.149~154 (2020)
- Huh YH, "In vitro evaluation of the polishing effect and optical properties of monolithic zirconia", J Prosthet Dent, 119, pp.994~999 (2018)
- Kwon SJ, "Comparison of the mechanical properties of translucent zirconia and lithium disilicate", J Prosthet Dent, 120, pp.132~137 (2018)
- Elsayed A, "Influence of the yttrium content on the fracture strength of monolithic zirconia crowns after artificial aging", Quintessence Int, 50, pp.344~348 (2019)
- Carrabba M, "Translucent zirconia in the ceramic scenario for monolithic restorations : A flexural strength and translucency comparison test", J Dent, 60, pp.70~76 (2017)
- Patel N, "Effect of Different Implant Abutment Materials on Optical Properties of Translucent Monolithic Zirconia Crowns", Master, pp.2019
- Zhang F, "Strength, toughness and aging stability of highly-translucent Y-TZP ceramics for dental restorations", Dent Mater, 32, pp.e327~e337 (2016)
- Arif R, "In vitro color stainability and relative translucency of CAD-CAM restorative materials used for laminate veneers and complete crowns", J Prosthet Dent, 122, pp.160~166 (2019)
- 이용근, "Criteria for clinical translucency evaluation of direct esthetic restorative materials", Restorative Dentistry and Endodontics, 41(3), pp.159~166 (2016), 대한치과보존학회
- Johnston WM, "Translucency parameter of colorants for maxillofacial prostheses", Int J Prosthodont, 8, pp.79~86 (1995)
- Chaiyabutr Y, "Effect of abutment tooth color, cement color, and ceramic thickness on the resulting optical color of a CAD", CAM glass-ceramic lithium disilicate-reinforced crown, 2011, pp.105, 83~90
- Douglas RD, "Intraoral determination of the tolerance of dentists for perceptibility and acceptability of shade mismatch", J Prosthet Dent, 97, pp.200~208 (2007)
- Jiang L, "Effects of sintering temperature and particle size on the translucency of zirconium dioxide dental ceramic", J Mater Sci Mater Med, 22, pp.2429~2435 (2011)
- Zhang Y, "Making yttria-stabilized tetragonal zirconia translucent", Dent Mater, 30, pp.1195~1203 (2014)
- Alraheam IA, "Fracture load of two thicknesses of different zirconia types after fatiguing and thermocycling", J Prosthet Dent, 123, pp.635~640 (2020)
- Wang F, "Translucency of dental ceramics with different thicknesses", J Prosthet Dent, 110, pp.14~20 (2013)
- Yan J, "Load-bearing capacity of lithium disilicate and ultra-translucent zirconias", J Mech Behav Biomed Mater, 88, pp.170~175 (2018)
- Yu B, "Measurement of translucency of tooth enamel and dentin", Acta Odontol Scand, 67, pp.57~64 (2009)
- Sun T, "Load-bearing capacity and the recommended thickness of dental monolithic zirconia single crowns", J Mech Behav Biomed Mater, 35, pp.93~101 (2014)
- Fabbri G, "Anterior discolored teeth restored with Procera all-ceramic restorations : a clinical evaluation of the esthetic outcome based on the thickness of the core selected", Eur J Esthet Dent, 6, pp.76~86 (2011)
- Sulaiman TA, "Optical Properties and light irradiance of monolithic zirconia at variable thicknesses", Dent Mater, 31, pp.1180~1187 (2015)
- "ISO 6872. Dentistry-Ceramic materials", International Standard Organization (ISO), ~ (2008)
- Gómez-Polo C, "Comparison of the CIELab and CIEDE 2000Color Difference Formulas on Gingival Color Space", J Prosthodont, 29, pp.401~408 (2020)