상용 아트리아 안정화 정방정 지르코니아 분말의 소결 물성
Sintered properties of commercial yttria-stabilized tetragonal zirconia polycrystals
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Tetragonal zirconia polycrystals (Y-TZP) with 3 to 5 mol% of yttria are mainly used as a dental zirconia implant material. For good mechanical properties and thermal stability, high sintered density over 99.5% and the particle size under 0.3 ㎛ are required. In this study, commercially available 3Y-TZP powders for zirconia implants were analyzed, and investigated the sintered properties, for examples, phase composition, sintered density, and microstructural evolution. The primary particles and granules of the commercial 3Y-TZP powders showed the different morphology and size, depending on the powder manufacturing company, and powder type caused the difference of phase composition, sintered density and microstructure. After the sintering at 1500℃ for 2 hours, each specimen showed a particle size of 0.23~0.33 ㎛, which was suitable for implant materials, but the sintered density varied from 98.5% to 99.3%.
Abstract
Tetragonal zirconia polycrystals (Y-TZP) with 3 to 5 mol% of yttria are mainly used as a dental zirconia implant material. For good mechanical properties and thermal stability, high sintered density over 99.5% and the particle size under 0.3 ㎛ are required. In this study, commercially available 3Y-TZP powders for zirconia implants were analyzed, and investigated the sintered properties, for examples, phase composition, sintered density, and microstructural evolution. The primary particles and granules of the commercial 3Y-TZP powders showed the different morphology and size, depending on the powder manufacturing company, and powder type caused the difference of phase composition, sintered density and microstructure. After the sintering at 1500℃ for 2 hours, each specimen showed a particle size of 0.23~0.33 ㎛, which was suitable for implant materials, but the sintered density varied from 98.5% to 99.3%.
참고문헌 (13)
- Luthardt, RG., , J. Dent. Res, 81(7), pp.487~491 (2002)
- 서다원, "지르코니아의 생체적합성과 임플란트로서의 생체활성에 대한 연구: In vivo 실험 문헌 고찰", 대한치과보철학회지, 57(1), pp.88~94 (2019), 대한치과보철학회[DOI]
- 남기우, "SiC와 TiO2 첨가에 따르는 ZrO2의 기계적 특성 및 균열 치유", 대한기계학회논문집 A, 40(3), pp.267~273 (2016), 대한기계학회
- Kim, D. J., , J. Kor. Ceram. Soc, 8(2), pp.157~165 (1993)
- Kim, M. J., , J. Kor. Ceram. Soc, 10(2), pp.122~127 (2000)
- Xiwen, S., , J. Rare. Earths, 29(2), pp.155~159 (2011)
- Kaplan, M., , Ceram. Int, 44(2), pp.2413~2418 (2018)
- leugels, J., , J. Euro. Ceram. Soc, 22(6), pp.873~881 (2002)
- Kosmač, T., , J. Biomed. Mater. Res, 53(4), pp.304~313 (2000)
- 이정환, "저온열화에 따른 치과용 지르코니아의 전자현미경 관찰 연구", 대한치과기공학회지, 33(1), pp.15~24 (2011), 대한치과기공학회
- Stawarczyk, B., , Clin Oral Invest, 17(4), pp.269~274 (2013)
- Gahlert, M., , Clin. Oral. Impl. Res, 23(3), pp.287~293 (2012)
- 정현도, "Influence of Solid Loading on the Granulation of 3Y-TZP Powder by Two-Fluid Spray Drying", 한국세라믹학회지, 55(4), pp.337~343 (2018), 한국세라믹학회