3Y-TZP/WC 복합체의 소결 방식에 따른 특성비교
Comparison of Properties with Different Sintering Process of 3Y-TZP/WC Composites
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
3Y-TZP ceramics obtained by doping 3 mol.% of Y2O3 to ZrO2 to stabilize the phase transition are widely used in the engineering ceramic industry due to their excellent mechanical properties such as high strength, fracture toughness, and wear resistance. An additional increase in mechanical properties is possible by manufacturing a composite in which a high-hardness material such as oxide or carbide is added to the 3Y-TZP matrix. In this study, composite powder was prepared by dispersing a designated percentage of WC in the 3Y-TZP matrix, and the results were compared after manufacturing the composite using the different processes of spark plasma sintering and HP. The difference between the densification behavior and porosity with the process mechanism was investigated. The correlation between the process conditions and phase formation was examined based on the crystalline phase formation behavior. Changes to the microstructure according to the process conditions were compared using field-emission scanning electron microscopy. The toughness-strengthening mechanism of the composite with densification and phase formation was also investigated.
Abstract
3Y-TZP ceramics obtained by doping 3 mol.% of Y2O3 to ZrO2 to stabilize the phase transition are widely used in the engineering ceramic industry due to their excellent mechanical properties such as high strength, fracture toughness, and wear resistance. An additional increase in mechanical properties is possible by manufacturing a composite in which a high-hardness material such as oxide or carbide is added to the 3Y-TZP matrix. In this study, composite powder was prepared by dispersing a designated percentage of WC in the 3Y-TZP matrix, and the results were compared after manufacturing the composite using the different processes of spark plasma sintering and HP. The difference between the densification behavior and porosity with the process mechanism was investigated. The correlation between the process conditions and phase formation was examined based on the crystalline phase formation behavior. Changes to the microstructure according to the process conditions were compared using field-emission scanning electron microscopy. The toughness-strengthening mechanism of the composite with densification and phase formation was also investigated.
참고문헌 (22)
- A. G. Evans, , J. Am. Ceram. Soc, 73, pp.187~ (1990)
- M. Rühle, , Progr. Mater. Sci, 33, pp.85~ (1989)
- F. F. Lange, , J. Am. Ceram. Soc, 69, pp.240~ (1986)
- W. H. Rhodes, , J. Am. Ceram. Soc, 64, pp.19~ (1981)
- P. Duwez, , J. Am. Ceram. Soc, 35, pp.107~ (1952)
- K. Tsukuma, , J. Mater. Sci, 20, pp.1178~ (1985)
- N. Ünal, , J. Eur. Ceram. Soc, 31, pp.2267~ (2011)
- A. Maji, , Mater. Today: Proceedings, 5, pp.7457~ (2018)
- 최재형, "고온가압소결을 이용한 YSZ-TiC 세라믹스 복합체의 제조와 특성", 한국분말재료학회지, 28(5), pp.381~388 (2021), 한국분말재료학회
- D. Liu, , J. Eur. Ceram. Soc, 36, pp.2051~ (2016)
- J. Chevalier, , J. Am. Ceram. Soc, 92, pp.1901~ (2009)
- P. Angerer, , Int. J. Refract. Met. Hard Mater, 25, pp.280~ (2007)
- R. Yamanoglu, , Powder Metall, 61, pp.178~ (2018)
- M. N. Rahaman, "Ceramic Processing and Sintering" (2003), Marcel Dekker
- S. Lee, , Ceramist, 22, pp.170~ (2019)
- J. Luo, , J. Am. Ceram. Soc, 82, pp.1922~ (1999)
- J. Chevalier, , Biomaterials, 25, pp.5539~ (2004)
- B. Cales, , J. Am. Ceram. Soc, 82, pp.2150~ (1999)
- M. Taya, , J. Am. Ceram. Soc, 73, pp.1382~ (1990)
- 조동율, "WC-Co 초고속 화염용사코팅 표면특성에 미치는 분말입자의 크기", 대한금속·재료학회지, 55(4), pp.227~231 (2017), 대한금속·재료학회[DOI]
- S. K. Yang, , J. Korean Ceram. Soc, 42, pp.411~ (2005)
- D. J. Kim, , Bull. Korean Ceram. Soc, 8, pp.157~ (1993)