Relationship Between the Initiation and Propagation of SCC and the Electrochemical Noise of Alloy 600 for the Steam Generator Tubing of Nuclear Power Plants
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
Since nuclear power plants are being operated under high temperature and high pressure, on-line monitoring technique to detect corrosion could be more effective than off-line method in shut-off period. In this operating condition, electrochemical noise method may be suitable to monitor the corrosion. This paper aims the analysis on the relation between the cracking and electrochemical noise signal of Alloy 600 under U-bending. When electrochemical noise monitoring technique was used during SCC test, it was judge to be obvious that if cracks generate, its generation can be detected by electrochemical current noise. Cracking-related noise was defined as the noise showing 5~10 times greater than the average value of background noise bands. On the base of crack noise, crack initiation time was determined. From SCC test and electrochemical noise monitoring in 25 ℃, 0.1 M Na2S4O6 solution (Reverse U-Bended Alloy 600 SE+), average crack initiation time was obtained as 9,046 seconds and from its initiation time, it could be defined that net crack propagation rate is the crack length divided by ΔT(= total test period - crack initiation time). Therefore, average net crack propagation rate was obtained to be 1.18x10-9 m/s.
Abstract
Since nuclear power plants are being operated under high temperature and high pressure, on-line monitoring technique to detect corrosion could be more effective than off-line method in shut-off period. In this operating condition, electrochemical noise method may be suitable to monitor the corrosion. This paper aims the analysis on the relation between the cracking and electrochemical noise signal of Alloy 600 under U-bending. When electrochemical noise monitoring technique was used during SCC test, it was judge to be obvious that if cracks generate, its generation can be detected by electrochemical current noise. Cracking-related noise was defined as the noise showing 5~10 times greater than the average value of background noise bands. On the base of crack noise, crack initiation time was determined. From SCC test and electrochemical noise monitoring in 25 ℃, 0.1 M Na2S4O6 solution (Reverse U-Bended Alloy 600 SE+), average crack initiation time was obtained as 9,046 seconds and from its initiation time, it could be defined that net crack propagation rate is the crack length divided by ΔT(= total test period - crack initiation time). Therefore, average net crack propagation rate was obtained to be 1.18x10-9 m/s.
참고문헌 (25)
- S. S. Hwang, , Corros. and Protect., 6, pp.65~ (2007)
- 김지현, "In-situ Raman Spectroscopic Study of Nickel-base Alloys in Nuclear Power Plants and Its Implications to SCC", CORROSION SCIENCE AND TECHNOLOGY, 3(5), pp.198~208 (2004), 한국부식방식학회
- 황성식, "Study on Leak Rate of SCC Degraded Alloy 600 Tubings of PWRs", CORROSION SCIENCE AND TECHNOLOGY, 3(6), pp.233~239 (2004), 한국부식방식학회
- Seong Sik Hwang, "SCC Mechanism of Ni Base alloys in Lead Contaminated Water", CORROSION SCIENCE AND TECHNOLOGY, 7(3), pp.189~193 (2008), 한국부식방식학회
- 황성식, "누설 및 파열실험용 SCC 결함 전열관 제작 및 누설거동 평가", CORROSION SCIENCE AND TECHNOLOGY, 8(5), pp.188~192 (2009), 한국부식방식학회
- H. S. Chung, , J. Corros Sci. Soc. of Kor., 25, pp.391~ (1996)
- D. H. Hur, , J. Corros Sci. Soc. of Kor., 29, pp.108~ (2000)
- Y. R. Yoo, , Mater. Sci. Forum, 475, pp.4227~ (2005)
- H. P. Kim, , J. Corros Sci. Soc. of Kor., 27, pp.491~ (1998)
- H. Y. Ha, , 석사, pp.2003
- J. R. Kearns, "American Society for Testing and Materials", ASTM STP 1227, ~ (1996)
- Jung Jip Kim, "Stress Corrosion Cracking in the Pre-Cracked Specimens of Type 403 stainless Steel", CORROSION SCIENCE AND TECHNOLOGY, 3(1), pp.14~19 (2004), 한국부식방식학회
- D. S. Seo, , 석사, pp.2005
- D. A. Eden, "UK Patent App.861158, US Patent 5139627", ~ (1986)
- Y. J. Tan, , Corros. Sci., 40, pp.513~ (1998)
- F. Mansfeld, , Corros. Sci., 39, pp.255~ (1997)
- C. C. Lee, , Corros. Sci., 40, pp.959~ (1998)
- F. Mansfeld, , Electrochim. Acta, 43, pp.435~ (1998)
- F. Mansfeld, , Electrochim. Acta, 46, pp.3651~ (2001)
- F. Mansfeld, , Corros. Sci., 43, pp.341~ (2001)
- M. Leban, , Corros. Sci., 56, pp.921~ (2000)
- E. H. Lee, , Mater. Sci., Eng., A, 449, pp.330~ (2007)
- W. T. Tsai, , Corros. Sci., 38, pp.33~ (1996)
- M. C. Tsai, , Corros. Sci., 34, pp.741~ (1993)
- S. S. Hsu, , J. Nucl. Mater., 184, pp.97~ (1991)