SCC Mechanism of Ni Base alloys in Lead Contaminated Water
6
조회
0
다운로드
5
인용
0
참고문헌
키워드
초록
Transgranular stress corrosion cracking of nickel base alloys was reported by Copson and Dean in 1965. Study to establish this cracking mechanism needs to be carried out. Laboratory stress corrosion tests were performed for mill annealed(MA) or thermally treated(TT) steam generator tubing materials in a high temperature water containing lead. An electrochemical interaction of lead with the alloying elements of SG tubings was also investigated. Alloy 690 TT showed a transgranular stress corrosion cracking in a 40% NaOH solution with 5000 ppm of lead, while intergranular stress corrosion racking was observed in a 10% NaOH solution with 100 ppm lead. Lead seems to enhance the disruption of passive film and anodic dissolution of alloy 600 and alloy 690. Crack tip blunting at grain boundary carbides plays a role for the transgranular stress corrosion cracking.
Abstract
Transgranular stress corrosion cracking of nickel base alloys was reported by Copson and Dean in 1965. Study to establish this cracking mechanism needs to be carried out. Laboratory stress corrosion tests were performed for mill annealed(MA) or thermally treated(TT) steam generator tubing materials in a high temperature water containing lead. An electrochemical interaction of lead with the alloying elements of SG tubings was also investigated. Alloy 690 TT showed a transgranular stress corrosion cracking in a 40% NaOH solution with 5000 ppm of lead, while intergranular stress corrosion racking was observed in a 10% NaOH solution with 100 ppm lead. Lead seems to enhance the disruption of passive film and anodic dissolution of alloy 600 and alloy 690. Crack tip blunting at grain boundary carbides plays a role for the transgranular stress corrosion cracking.
참고문헌 (22)
- S. S. Hwang, , J. of Nuclear Materials, 246, pp.77~ (1977)
- J. M. Sarver, , the Conference 8th Int'l Symposium on Environmental Degradation of Materials in Nuclear Power Systems- Water Reactors, pp.208~ (1997)
- S. S. Hwang, , the Conference Contributions of materials investigation to the resolution of problems encountered in pressurized water reactors, pp.403~415 (1998)
- S. S. Hwang, , Journal of Nuclear Materials, 275, pp.28~ (1999)
- T. Sakai, , the Conference 5th Int'l Symposium on Environmental Degradation of Materials in Nuclear Power System-Water Reactors, pp.764~ (1991)
- H. R. Copson, , Corrosion, 21, pp.1~ (1965)
- S. S. Hwang, "Failure analysis report of the steam generator tubings pulled out from Kori unit 2" (1990), Korea Atomic Energy Research Institute
- R. J. Jacko, "“Corrosion evaluation of thermally treated Alloy 600 tubing in primary and faulted secondary water environments”", pp.3~ (1990)
- R. J. Jacko, , the Conference on thermally treated alloy 690 tubes for nuclear steam generators, pp.15~ (1986)
- Seong Sik Hwang, "submitted to the Corrosion Science", ~ (2007)
- M. Helie, , the Conference 7th Int'l Symposium Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, pp.247~ (1995)
- "Private communication with M. Helie in 2005 (CEA, France).", ~
- Roger W. Staehle, , the Conference 11th Int'l Symposium Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, pp.381~ (2003)
- S. M. Bruemmer, , Corrosion, 44, pp.782~ (1988)
- J. R. Rice, , Phil. Mag, 29, pp.73~ (1974)
- W. A. Byers, , the Conference 8th Int'l Symposium on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, pp.224~ (1997)
- T. Sakai, , Corrosion, pp.83~ (1992)
- T. Sakai, , Corrosion, 54, pp.515~ (1998)
- Koo Kab Jung, , the Conference 7th Int'l Symposium on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, pp.233~ (1995)
- D. Costa, , the Conference 7th Int'l Symposium on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors, pp.199~ (1995)
- S. S. Hwang, , Corrosion, 58, pp.392~ (2002)
- R. Kilian, , IAEA specialists meeting on steam generator problems and replacement, International Atomic Agency, pp.137~ (1993)