Corrosion Behavior and Inhibition Studies of AZ31B Magnesium Alloy With and Without Cl- in the Alkaline Electrolytes in Addition with Various Inhibitor Additives
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The pitting corrosion and inhibition studies of AZ31B magnesium alloy were investigated in the alkaline solution (pH12) with chloride and inhibitors. The corrosion behavior of passive film with/without Cl- in the alkaline electrolyte were conducted by polarization curve and immersion tests in the presence of various additives (inhibitors) to clarify the inhibition efficiency of pitting corrosion at higher potential region. Critical concentration of pitting corrosion for Mg alloy was evaluated with 0.005 M NaCl in 0.01 M NaOH on the anodic polarization behavior. Critical pitting of AZ31B Mg alloy in 0.01 M NaOH is a function of chlorides; Epit = - 1.36 – 0.2 log [Cl–]. When the Sodium Benzoate (SB) was only used as an inhibitor, a few metastable pits developed on the Mg surface by an immersion test despite no pitting corrosion on the polarization curve meaning that adsorption of SB on the surface is insufficient protection from pitting corrosion in the presence of chloride. The role of SB and Sodium Dodecylbenzenesulfonate (SDBS) inhibitors for the Mg alloy surface in the presence of chloride was suppressed from pitting corrosion to co-adsorb on the Mg alloy surface with strong formation of passive film preventing pitting corrosion.
Abstract
The pitting corrosion and inhibition studies of AZ31B magnesium alloy were investigated in the alkaline solution (pH12) with chloride and inhibitors. The corrosion behavior of passive film with/without Cl- in the alkaline electrolyte were conducted by polarization curve and immersion tests in the presence of various additives (inhibitors) to clarify the inhibition efficiency of pitting corrosion at higher potential region. Critical concentration of pitting corrosion for Mg alloy was evaluated with 0.005 M NaCl in 0.01 M NaOH on the anodic polarization behavior. Critical pitting of AZ31B Mg alloy in 0.01 M NaOH is a function of chlorides; Epit = - 1.36 – 0.2 log [Cl–]. When the Sodium Benzoate (SB) was only used as an inhibitor, a few metastable pits developed on the Mg surface by an immersion test despite no pitting corrosion on the polarization curve meaning that adsorption of SB on the surface is insufficient protection from pitting corrosion in the presence of chloride. The role of SB and Sodium Dodecylbenzenesulfonate (SDBS) inhibitors for the Mg alloy surface in the presence of chloride was suppressed from pitting corrosion to co-adsorb on the Mg alloy surface with strong formation of passive film preventing pitting corrosion.
참고문헌 (33)
- 최경수, "경량 마그네슘 합금(AZ31B)의 도금층 형성 연구", 한국표면공학회지, 44(6), pp.239~245 (2011), 한국표면공학회
- E. F. Emley, "Principle of Magnesium Technology", pp.30~31 (1966), Pergamon Press
- G. L. Makar, , Int. Mater. Rev., 38, pp.138~ (1993)
- J. E. Gray, , J. Alloys Compd, 336, pp.88~ (2002)
- W. S. Loose, "Corrosion and Protection of Magnesium", pp.173~ (1946), ASM Int., Materials Park
- O. Lander, , Corrosion, 45, pp.741~ (1989)
- L. Wang, , Zairyo-to-Kankyo, 58, pp.105~ (2009)
- D. Thirumalaikumarasamy, , J. Magnes. Alloy, 2, pp.36~ (2014)
- I. B. Singh, , J. Magnes. Alloy, 3, pp.1~ (2015)
- L. Gao, , J. Alloys Compd, 468, pp.285~ (2009)
- S. Li, , Corros. Sci, 112, pp.596~ (2016)
- Q. Qu, , Corros. Sci, 53, pp.1186~ (2011)
- M. Pourbaix, "Atlas of Electrochemical Equilibria in Aqueous Solutions", pp.140~143 (1974), NACE
- A. Pardo, , Corros. Sci, 50, pp.823~ (2008)
- J. Liao, , Corros. Sci, 61, pp.208~ (2012)
- A. Pardo, , Corros. Sci, 50, pp.823~ (2008)
- F. Cao, , Corros. Sci, 111, pp.835~ (2016)
- A. Sadeghi, , Corros. Sci, 141, pp.117~ (2018)
- A. Fattah-alhosseini, , J. Magnes. Aolly, 2, pp.75~ (2014)
- L. Li, "Magnesium Alloys - Corrosion and Surface Treatments", pp.344~ (2011), Intech
- H. Gao, , Corros. Sci, 52, pp.1603~ (2010)
- Z. Feng, , J. Electrochem. Soc., 165, pp.C94~ (2018)
- S. Thirugnanaselvi, , T. Nonferr. Mettal. Soc, 24, pp.1969~ (2014)
- Yu. I. Kuznetsov, , Int. J. Corros. Scale Inhib, 5, pp.31~ (2016)
- F. Zucchi, , Mater. Corros, 60, pp.199~ (2009)
- MARS G. Fontana, "Corrosion Engineering", pp.14~174 (1986), McGraw-Hill
- H. Yashiro, , Corros. Sci, 31, pp.485~ (1990)
- S. Ningshen, , Br. Corros. J, 36, pp.36~ (2013)
- J. Park, , J. Electrochem. Soc., 149, pp.B34~ (2002)
- F. E. T. Heakal, , Corros. Sci, 53, pp.1174~ (2011)
- W. H. Ailor, "Handbook on corrosion testing and evaluation", pp.174~ (1971), John Wiley and Sons
- M. C. Zhao, , Corros. Sci, 50, pp.3168~ (2008)
- M. Kaseem, , Surf. Coat. Technol, 283, pp.268~ (2015)