Effect of Hydrodynamic Condition on the Electrochemical Behavior of Various Metals in 3.5 wt% NaCl Solution
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The electrochemical behaviors of various metals with and without diamond-like-carbon (DLC) coating in 3.5 wt% NaCl solution were investigated. The effect of hydrodynamic conditions was focused by employing a rotating disc electrode (RDE). The experimental results showed that each bare metal had a more positive corrosion potential and a higher corrosion rate due to enhanced oxygen transport at the higher rotating speed of the RDE. DLC coating caused a substantial increase in the corrosion resistance of all metals studied. However, localized corrosion was still found in the DLC-coated metal at sites where deposition defects existed. Surface morphology examination was performed after the electrochemical test to confirm the roles of hydrodynamic conditions and DLC coating.
Abstract
The electrochemical behaviors of various metals with and without diamond-like-carbon (DLC) coating in 3.5 wt% NaCl solution were investigated. The effect of hydrodynamic conditions was focused by employing a rotating disc electrode (RDE). The experimental results showed that each bare metal had a more positive corrosion potential and a higher corrosion rate due to enhanced oxygen transport at the higher rotating speed of the RDE. DLC coating caused a substantial increase in the corrosion resistance of all metals studied. However, localized corrosion was still found in the DLC-coated metal at sites where deposition defects existed. Surface morphology examination was performed after the electrochemical test to confirm the roles of hydrodynamic conditions and DLC coating.
참고문헌 (16)
- A. L. Baia Neto, , Thin Solid Films, 293, pp.206~ (1997)
- J. F. Zhao, , Diam. Relat. Mater, 10, pp.1070~ (2001)
- A. K. Gangopadhyay, , Tribol. Int, 30, pp.9~ (1997)
- W. J. Wu, , Diam. Relat. Mater, 7, pp.1478~ (1998)
- J. Choi, , Diam. Relat. Mater, 16, pp.1361~ (2007)
- H. G. Kim, , Diam. Relat. Mater, 14, pp.35~ (2005)
- A. Dorner-Reisel, , Surf. Coat. Technol, 177-178, pp.830~ (2004)
- M. Azzi, , Surf. Coat. Technol, 204, pp.3986~ (2010)
- B. Tomcik, , Thin Solid Films, 360, pp.173~ (2000)
- A. Dorner, , Thin Solid Films, 355-356, pp.214~ (1999)
- J. Robertson, , Mat. Sci. Eng. R, 37, pp.129~ (2002)
- M. S. Jellesen, , Wear, 267, pp.1709~ (2009)
- S. S. Hadinata, , Thin Solid Films, 529, pp.412~ (2013)
- L. Cáceres, , Corros. Sci, 49, pp.3168~ (2007)
- A. Neville, , Wear, 250, pp.726~ (2001)
- M. D. Bermudez, , Wear, 258, pp.693~ (2005)