슬러리 펌프용 고크롬 주철의 교반 가속 부식법
Stir-Accelerated Corrosion Test of High Chromium Cast Iron for Application in Slurry Pumps
0
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
Stir-accelerated corrosion test of a high chromium cast iron was attempted in 0.1 mol dm-3 H2SO4 + 0.05 mol dm-3 HCl + 10 wt% SiC solution for 48 h at room temperature or at 45 oC. The high chromium cast iron was composed of 2.8 wt% C and 27 wt% Cr and balanced with Fe. The high chromium cast iron was positioned into a 500 mL beaker with stirring of the solution at 1050 rpm using a magnetic hot plate. The corrosion rate was increased by agitating the solution. In addition, the corroded depth of the high chromium cast iron surface was increased by agitating the solution. The surface morphology of the high chromium cast iron after the stir-accelerated corrosion test revealed that a dendritic austenite phase partially remained in the corroded region after agitating the solution, indicating that solution movement during agitating could accelerate the corrosion rate of the high chromium cast iron.
Abstract
Stir-accelerated corrosion test of a high chromium cast iron was attempted in 0.1 mol dm-3 H2SO4 + 0.05 mol dm-3 HCl + 10 wt% SiC solution for 48 h at room temperature or at 45 oC. The high chromium cast iron was composed of 2.8 wt% C and 27 wt% Cr and balanced with Fe. The high chromium cast iron was positioned into a 500 mL beaker with stirring of the solution at 1050 rpm using a magnetic hot plate. The corrosion rate was increased by agitating the solution. In addition, the corroded depth of the high chromium cast iron surface was increased by agitating the solution. The surface morphology of the high chromium cast iron after the stir-accelerated corrosion test revealed that a dendritic austenite phase partially remained in the corroded region after agitating the solution, indicating that solution movement during agitating could accelerate the corrosion rate of the high chromium cast iron.
참고문헌 (9)
- YuguiZheng, "Damage Mechanisms and Metallic Materials Development in Multiphase Flow", CORROSION SCIENCE AND TECHNOLOGY, 31(1), pp.41~47 (2002), 한국부식방식학회
- 김창규, "열처리된 고크롬 백주철", 저크롬강 이중주조재료의 내마모성과 파괴인성, 2004, pp.42(11), 877~886[DOI]
- 이로운, "초내식성 주철의 경도 및 부식 특성에 미치는 열처리의 영향", 대한금속·재료학회지, 52(7), pp.511~518 (2014), 대한금속·재료학회
- I. Chakrabarty, "Structural study of Cr-Mn-Cu white cast irons", Journal of Materials Science Letters, 6, pp.1399~ (1987)[DOI]
- 이준섭, "산성 용액에서 고크롬 주철의 전면 부식 거동", CORROSION SCIENCE AND TECHNOLOGY, 20(6), pp.367~372 (2021), 한국부식방식학회[DOI]
- 정영재, "Cr 첨가가 고망간강의 중성 수용액 환경 내 유동가속부식 거동에 미치는 영향", CORROSION SCIENCE AND TECHNOLOGY, 20(6), pp.373~383 (2021), 한국부식방식학회[DOI]
- 황현규, "순환동전위 분극실험을 이용한 스테인리스강의 그린데스용액에서 전기화학적 특성에 미치는 온도의 영향", CORROSION SCIENCE AND TECHNOLOGY, 20(5), pp.266~280 (2021), 한국부식방식학회[DOI]
- 김경모, "원전 2차계통수 모사 환경에서 용접배관 감육 특성에 미치는 재료 및 유속의 영향", CORROSION SCIENCE AND TECHNOLOGY, 15(5), pp.245~252 (2016), 한국부식방식학회[DOI]