치과용 Ni-Ti파일의 표면특성에 미치는 ta-C코팅효과
Effects of ta-C Coatings on Surface Characteristics of Dental Ni-Ti Files
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Dental Ni-Ti files must ensure stability and resistance to fatigue fracture. DLC and ta-C were coated to remove defects on the surface and ensure stability, and the surface characteristics were investigated. When coated with DLC, it was black, and in case of ta-C coating, it was blue-black. Scratches, which are defects caused by mechanical processing, were formed on the surface of the un-coated Ni-Ti file from the end of the file along the direction of processing, with the Pro-file appearing in the vertical direction and the K-file appearing in the file direction. Scratches were reduced on the coated surface, and the surface roughness was greatly reduced after coating compared to before coating. The un-coated Ni-Ti file had the lowest hardness, the DLC-coated file had the highest hardness, and ta-C showed relatively high hardness. The elastic modulus of the DLC coating film was high, and the ta-C elastic modulus was low. The adhesion of the DLC coating film tended to be higher than that of ta-C, and the wear loss amount of DLC coating of taC was lower. The corrosion potential of the ta-C coating increased significantly, and the corrosion current density decreased.
Abstract
Dental Ni-Ti files must ensure stability and resistance to fatigue fracture. DLC and ta-C were coated to remove defects on the surface and ensure stability, and the surface characteristics were investigated. When coated with DLC, it was black, and in case of ta-C coating, it was blue-black. Scratches, which are defects caused by mechanical processing, were formed on the surface of the un-coated Ni-Ti file from the end of the file along the direction of processing, with the Pro-file appearing in the vertical direction and the K-file appearing in the file direction. Scratches were reduced on the coated surface, and the surface roughness was greatly reduced after coating compared to before coating. The un-coated Ni-Ti file had the lowest hardness, the DLC-coated file had the highest hardness, and ta-C showed relatively high hardness. The elastic modulus of the DLC coating film was high, and the ta-C elastic modulus was low. The adhesion of the DLC coating film tended to be higher than that of ta-C, and the wear loss amount of DLC coating of taC was lower. The corrosion potential of the ta-C coating increased significantly, and the corrosion current density decreased.
참고문헌 (12)
- B. Clark Dalton, "Bacterial reduction with nickel-titanium rotary instrumentation", Journal of Endodontics, 24(11), pp.763~767 (1998), Elsevier BV[DOI]
- S ALAPATI, "Scanning Electron Microscope Observations of New and Used Nickel-Titanium Rotary Files", Journal of Endodontics, 29(10), pp.667~669 (2003), Ovid Technologies (Wolters Kluwer Health)[DOI]
- 최한철, "치과용 Ni-Ti합금의 표면특성에 미치는 Mo함량의 영향", CORROSION SCIENCE AND TECHNOLOGY, 22(1), pp.64~72 (2023), 한국부식방식학회[DOI]
- A. M. Elnaghy, "Mechanical properties of ProTaper Gold nickel‐titanium rotary instruments", International Endodontic Journal, 49(11), pp.1073~1078 (2015), Wiley[DOI]
- Gianluca Plotino, "Influence of Temperature on Cyclic Fatigue Resistance of ProTaper Gold and ProTaper Universal Rotary Files", Journal of Endodontics, 43(2), pp.200~202 (2017), Elsevier BV[DOI]
- Harmeet Walia, "An initial investigation of the bending and torsional properties of nitinol root canal files", Journal of Endodontics, 14(7), pp.346~351 (1988), Elsevier BV[DOI]
- Ahmad A. Madarati, "Management of Intracanal Separated Instruments", Journal of Endodontics, 39(5), pp.569~581 (2013), Elsevier BV[DOI]
- B SATTAPAN, "Defects in Rotary Nickel-Titanium Files After Clinical Use", Journal of Endodontics, 26(3), pp.161~165 (2000), Ovid Technologies (Wolters Kluwer Health)[DOI]
- Yong-Hoon Jeong, "Effects of TiN and WC coating on the fatigue characteristics of dental implant", Surface and Coatings Technology, 243, pp.71~81 (2014), Elsevier BV[DOI]
- 김영식, "Synergistic Effect of Nitrogen and Molybdenum on Localized Corrosion of Stainless Steels", CORROSION SCIENCE AND TECHNOLOGY, 9(1), pp.20~28 (2010), 한국부식방식학회
- 최예지, "Titanium 양극산화시 TiO2의 형상 및 특성에 미치는 전해질의 영향", CORROSION SCIENCE AND TECHNOLOGY, 22(3), pp.193~200 (2023), 한국부식방식학회[DOI]
- "알루미늄 합금의 수소취화 방지를 위한 경질양극산화 및 플라즈마이온질화의 영향", CORROSION SCIENCE AND TECHNOLOGY, 22(4), pp.221~231 (2023), 한국부식방식학회[DOI]