지르코니아 전장 세라믹의 파절강도에 관한 비교 연구
Comparative Study in Fracture Strength of Zirconia Veneering Ceramics
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
This study was performed to evaluate the fracture strength of the dental zirconia veneering ceramics for zirconia ceramic core. Six commercial zirconia veneering ceramics were used in this study, namely E-Max(Ivoclar vivadent, Inc, Liechtenstein), Creation ZI(KLEMA Dental produckte GmbH, Austria), Cercon ceram kiss(Degudent,GmbH, Hanau-Wolfgang, Germany), Triceram(Dentaurum, Ispringen, Germany), Zirkonzahn(Zirkonzahn GmbH, Italy),Zirmax(Alpadent, korea). All samples were prepared according to the relevant instructions of manufacture. Disc specimens were prepared to the final dimensions of 17 mm in diameter and 1.5 mm in thickness. The biaxial flexure strength test was conducted using a ball-on-three-ball method. All specimens were tested in a moisture-free environment. Average flexural strengths were analyzed with Weibull analysis and one-way analysis of variance(ANOVA). Significant differences were founded between the mean flexural strength values of five commercials zirconia veneering ceramics and the other. The flexural strengths and Weibull modulus were similar to those of five groups E-Max(EM), Creation ZI(CR),Cercon ceram kiss(CE), Triceram(TR), Zirkonzahn(ZI) with the exception of Zirmax(ZM). The biaxial flexural strength from Cercon ceram kiss(CE) was higher than those of other groups. Fracture analysis showed similar results for these five groups.
Abstract
This study was performed to evaluate the fracture strength of the dental zirconia veneering ceramics for zirconia ceramic core. Six commercial zirconia veneering ceramics were used in this study, namely E-Max(Ivoclar vivadent, Inc, Liechtenstein), Creation ZI(KLEMA Dental produckte GmbH, Austria), Cercon ceram kiss(Degudent,GmbH, Hanau-Wolfgang, Germany), Triceram(Dentaurum, Ispringen, Germany), Zirkonzahn(Zirkonzahn GmbH, Italy),Zirmax(Alpadent, korea). All samples were prepared according to the relevant instructions of manufacture. Disc specimens were prepared to the final dimensions of 17 mm in diameter and 1.5 mm in thickness. The biaxial flexure strength test was conducted using a ball-on-three-ball method. All specimens were tested in a moisture-free environment. Average flexural strengths were analyzed with Weibull analysis and one-way analysis of variance(ANOVA). Significant differences were founded between the mean flexural strength values of five commercials zirconia veneering ceramics and the other. The flexural strengths and Weibull modulus were similar to those of five groups E-Max(EM), Creation ZI(CR),Cercon ceram kiss(CE), Triceram(TR), Zirkonzahn(ZI) with the exception of Zirmax(ZM). The biaxial flexural strength from Cercon ceram kiss(CE) was higher than those of other groups. Fracture analysis showed similar results for these five groups.
참고문헌 (21)
- Rosenblum M, "A review of all-ceramic restoration", J Am Dent Assoc, 128(3), pp.297~307 (1997)
- 박재홍, "수종 지르코니아 세라믹의 굴곡강도에 관한 연구", 대한치과보철학회지, 42(2), pp.142~153 (2004), 대한치과보철학회
- Albakry M, "Fracture toughness and hardness evaluation of three pressable all-ceramic dental materials", J Dent, 3(3), pp.181~188 (2003)
- Ritter JE, "Engineering design and fatigue failure of brittle materials in Fracture mechanics of ceramics. Vol 4, Crack growth and Microstructure", pp.667~686 (1978), Plenum
- Marcelo M, "Influence of pH on slow crack growth of dental porcelains", Dent Mater, 24(6), pp.814~823 (2008)
- White SN, "Chanical fatigue of a feldspathic dental porcelain", Dent Mater, 9(4), pp.260~264 (1993)
- AndrR, "Fatigue of zirconia under cyclic loading in water and its implications for the design of dental bridges", Dent Mater, 23(1), pp.106~114 (2007)
- Petra C, "Shear bond strengths between different zirconia cores and veneering ceramics and their susceptibility to thermocycling", Dent Mater, 24(11), pp.1556~1567 (2008)
- De Jager N, "The influence of design parameters on the FEA-determined stress distribution in CAD", CAM produced all-ceramic dental crowns, 2006, pp.21(3), 242~251
- Sundh A, "A comparison of fracture strength of yttrium-oxide-partially-stabilized zirconia ceramic crowns with varying core thickness, shapes and veneer ceramics", J Oral Rehabil, 31(7), pp.682~682 (2004)
- Sherrill CA, "Transverse strength of aluminous and feldspathic porcelain", J Dent Res, 53(3), pp.683~690 (1974)
- Ban S, "Inflence of test method on failure stress of brittle dental materials", J Dent Res, 69(12), pp.1791~1799 (1990)
- Ban S, "Effect of loading conditions on bi-axial flexure strength of dental cements", Dent Mater, 8(2), pp.100~104 (1992)
- Russell AG, "Flexural strength of feldspathic porcelain treated with ion exchange, overglaze, and polishing", J Prosthet Dent, 71(5), pp.468~472 (1994)
- Fairhurst CW, "The effect of glaze on porcelain strength", Dent Mater, 8(3), pp.203~207 (1992)
- Fairhurst CW, "A study of flaw size in porcelain(abstract)", J Dent Res, 73, pp.370~ (1994)
- Smyth KK, "Dyanmic fatigue of a machinable glass-ceramic", J Amer Ceram Soc, 66(7), pp.500~505 (1983)
- Fairhurst CW, "Dynamic fatigue of feldspathic porcelain", Dent Mater, 9(4), pp.269~273 (1993)
- Myers ML, "Fatigue failure parameters of IPS-Empress porcelain", Int J Prosth, 7(6), pp.549~553 (1994)
- Wachtman JB, "Bi-axial flexure tests of ceramic substrates", J Mater, 7, pp.188~194 (1972)
- McCabe JF, "The treatment of results for tensile bond strength testing", J Dent Res, 14(4), pp.165~168 (1986)