Effect of fabrication processes on mechanical properties of glass fiber reinforced polymer composites for 49 meter (160 foot) recreational yachts
2
조회
0
다운로드
5
인용
0
참고문헌
초록
Polymer composite materialsoffer high strength and stiffness to weight ratio, corrosion resistance, and total life cost reductions that appeal to the marine industry. The advantages of composite construction have led to their incorporation in U.S. yacht hull structures over 46 meters (150 feet) in length. In order to construct even larger hull structures, higher quality composites with a lower cost production techniques need to be developed. In this study, the effect of composite hull fabrication processes on mechanical properties of glass fiber reinforced plastic(GFRP) composites is presented. Fabrication techniques used in this study are hand lay-up (HL), vacuum infusion (VI), and hybrid (HL+VI) processes. Mechanical property testing includes: tensile, compressive, and ignition loss sample analysis. Results demonstrate that the vacuum pressure implemented during composite fabrication has an effect on mechanical properties. The VI processed GFRP yields improved mechanical properties in tension/compression strengths and tensile modulus. The hybrid GFRP composites, however, failed in a sequential manor, due to dissimilar failure modes in the HL and VI processed sides. Fractography analysis was conducted to validate the mechanical property testing results.
Abstract
Polymer composite materialsoffer high strength and stiffness to weight ratio, corrosion resistance, and total life cost reductions that appeal to the marine industry. The advantages of composite construction have led to their incorporation in U.S. yacht hull structures over 46 meters (150 feet) in length. In order to construct even larger hull structures, higher quality composites with a lower cost production techniques need to be developed. In this study, the effect of composite hull fabrication processes on mechanical properties of glass fiber reinforced plastic(GFRP) composites is presented. Fabrication techniques used in this study are hand lay-up (HL), vacuum infusion (VI), and hybrid (HL+VI) processes. Mechanical property testing includes: tensile, compressive, and ignition loss sample analysis. Results demonstrate that the vacuum pressure implemented during composite fabrication has an effect on mechanical properties. The VI processed GFRP yields improved mechanical properties in tension/compression strengths and tensile modulus. The hybrid GFRP composites, however, failed in a sequential manor, due to dissimilar failure modes in the HL and VI processed sides. Fractography analysis was conducted to validate the mechanical property testing results.
참고문헌 (21)
- ABS, "Guide for building and classing motor pleasure yachts, Chapter 8 "design pressures", Chaper 9 "hull scantling, high speed craft", American Bureau of Shipping, ~ (2000)
- Adams, D, "Influence of specimen gage length and loading method on the axial compressive strength of a unidirectional composite material", Experimental Mechanics, 31(1), pp.14~21 (1990)
- ASTM D2584, "Standard test method for Ignition loss of cured reinforced resins", ASTM International, ~
- ASTM D3039, "Standard test method for tensile properties of polymer matrix composite materials", ASTM International, ~
- ASTM D695, "Standard test method for compressive properties of rigid plastics", ASTM International, ~
- Baley, C, "Mechanical properties of composites based on low styrene emission polyester resins for marine applications", Applied Composite Materials, 13, pp.1~22 (2006)
- Belingardi, G, "repeated impact response of hand lay-up and vacuum infusion thick glass reinforced laminates", International Journal of Impact Engineering, 35, pp.609~619 (2008)
- Belingardi, G, "Repeated impact response of hand lay-up and vacuum infusion thick glass reinforced laminates", International Journal of Impact Engineering, 35, pp.609~619 (2008)
- Borsellino, C, "Effect of bonder at skin", core interface on the mechanical performances of sandwich structures used in marine industry, 2007, pp.14, 307~323
- Capello, F, "Lay-up optimization for the hull of a racing sailing yacht", Advances in Engineering Software, 32, pp.133~139 (2001)
- Costa, M. L, "The influence of porosity on the interlaminar shear strength of carbon", epoxy and carbon, Composites Science and Technology, pp.2001, 61(14)[DOI]
- Fu, S.-Y, "Tensile properties of short-glass-fiber- and short-carbonfiber-reinforced polypropylene composites", composites Part A: Applied Science and Manufacturing, 31(10), pp.1117~1125 (2000)
- Horsmon, A., "Lightweight composites for heavy-duty solutions", Marine Technology, 38(2), pp.112~115 (2001)
- Mallick, P.K, "Fiber reinforce composites: materials, manufacturing, and design" (2007), CRC Press, Taylor and Francis Group
- Modi, D, "Active control of the vacuum infusion process", composites Part A: Applied Science and Manufacturing, 38(5), pp.1271~1287 (2007)
- Mouring, S., "Buckling and postbuckling of composite ship panels stiffened with preform frames", Ocean Engineering, 26, pp.793~803 (1999)
- Mouritz, A, "Review of advanced composite structures for naval ships and submarines", Composite Structures,, 53(1), pp.21~24 (2001)
- Rodriguez, E, "Characterization of composites based on natural and glass fibers obtained by vacuum infusion", Journal of Composite Materials, 39(3), pp.265~282 (2005)
- Schultheisz, C.R, "Compressive failure of composites, Part 1: testing and micro-mechanical theories", Progress in Aerospace Sciences, 32(1), pp.1~42 (1996)
- Squires, C, "Understanding the factors affecting compressive testing of unidirectional carbon fiber composites", Composites Part B: Engineering, 38(4), pp.481~487 (2007)
- Thomason, J.L., "The Interface region in glass fiber reinforced epoxy resin composites", Sample preparation, void content and interfacial strength, 26, pp.467~47 (1995)