Change of phase transformation and bond strength of Y-TZP with various hydrofluoric acid etching
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Objectives: The purpose of this study was to quantify phase transformation after hydrofluoric acid (HF) etching at various concentrations on the surface of yttria-stabilized tetragonal zirconia polycrystal (Y-TZP), and to evaluate changes in bonding strength before and after thermal cycling. Materials and Methods: A group whose Y-TZP surface was treated with tribochemical silica abrasion (TS) was used as the control. Y-TZP specimens from each experimental group were etched with 5%, 10%, 20%, and 40% HF solutions at room temperature for 10 minutes. First, to quantify the phase transformation, Y-TZP specimens (n = 5) treated with TS, 5%, 10%, 20% and 40% HF solutions were subjected to X-ray diffraction. Second, to evaluate the change in bond strength before and after thermal cycling, zirconia primer and MDP-containing resin cement were sequentially applied to the Y-TZP specimen. After 5,000 thermal cycles for half of the Y-TZP specimens, shear bond strength was measured for all experimental groups (n = 10). Results: The monoclinic phase content in the 40% HF-treated group was higher than that of the 5%, 10%, and 20% HF-treated groups, but lower than that of TS-treated group (p < 0.05). The 40% HF-treated group showed significantly higher bonding strength than the TS, 5%, and 10% HF-treated groups, even after thermal cycling (p < 0.05). Conclusions: Through this experiment, the group treated with SiO2 containing air-borne abrasion on the Y-TZP surface showed higher phase transformation and higher reduction in bonding strength after thermal cycling compared to the group treated with high concentration HF.
Abstract
Objectives: The purpose of this study was to quantify phase transformation after hydrofluoric acid (HF) etching at various concentrations on the surface of yttria-stabilized tetragonal zirconia polycrystal (Y-TZP), and to evaluate changes in bonding strength before and after thermal cycling. Materials and Methods: A group whose Y-TZP surface was treated with tribochemical silica abrasion (TS) was used as the control. Y-TZP specimens from each experimental group were etched with 5%, 10%, 20%, and 40% HF solutions at room temperature for 10 minutes. First, to quantify the phase transformation, Y-TZP specimens (n = 5) treated with TS, 5%, 10%, 20% and 40% HF solutions were subjected to X-ray diffraction. Second, to evaluate the change in bond strength before and after thermal cycling, zirconia primer and MDP-containing resin cement were sequentially applied to the Y-TZP specimen. After 5,000 thermal cycles for half of the Y-TZP specimens, shear bond strength was measured for all experimental groups (n = 10). Results: The monoclinic phase content in the 40% HF-treated group was higher than that of the 5%, 10%, and 20% HF-treated groups, but lower than that of TS-treated group (p < 0.05). The 40% HF-treated group showed significantly higher bonding strength than the TS, 5%, and 10% HF-treated groups, even after thermal cycling (p < 0.05). Conclusions: Through this experiment, the group treated with SiO2 containing air-borne abrasion on the Y-TZP surface showed higher phase transformation and higher reduction in bonding strength after thermal cycling compared to the group treated with high concentration HF.
참고문헌 (33)
- Blatz MB, "Resin-ceramic bonding: a review of the literature", J Prosthet Dent, 89, pp.268~274 (2003)
- Derand T, "Bond strength of composite luting cement to zirconia ceramic surfaces", Dent Mater, 21, pp.1158~1162 (2005)
- Thompson JY, "Adhesion", cementation to zirconia and other non-silicate ceramics: where are we now?, 2011, pp.27, 71~82
- Burke FJ, "Are adhesive technologies needed to support ceramics? An assessment of the current evidence", J Adhes Dent, 4, pp.7~22 (2002)
- Nagaoka N, "Chemical interaction mechanism of 10-MDP with zirconia", Sci Rep, 7, pp.45563~ (2017)
- Okada M, "Optimal sandblasting conditions for conventional-type yttria-stabilized tetragonal zirconia polycrystals", Dent Mater, 35, pp.169~175 (2019)
- Inokoshi M, "Meta-analysis of bonding effectiveness to zirconia ceramics", J Dent Res, 93, pp.329~334 (2014)
- Özcan M, "Adhesion to zirconia used for dental restorations: a systematic review and meta-analysis", J Adhes Dent, 17, pp.7~26 (2015)
- Aboushelib MN, "Selective infiltration-etching technique for a strong and durable bond of resin cements to zirconia-based materials", J Prosthet Dent, 98, pp.379~388 (2007)
- Sriamporn T, "Dental zirconia can be etched by hydrofluoric acid", Dent Mater J, 33, pp.79~85 (2014)
- Chaiyabutr Y, "The effect of hydrofluoric acid surface treatment and bond strength of a zirconia veneering ceramic", J Prosthet Dent, 100, pp.194~202 (2008)
- Kim HE, "Changes in bond strength and topography for Y-TZP etched with hydrofluoric acid depending on concentration and temperature conditions", Medicina (Kaunas), 56, pp.568~ (2020)
- Liu D, "Effects of some chemical surface modifications on resin zirconia adhesion", J Mech Behav Biomed Mater, 46, pp.23~30 (2015)
- Jevnikar P, "The effect of nano-structured alumina coating on resin-bond strength to zirconia ceramics", Dent Mater, 26, pp.688~696 (2010)
- Papia E, "Bonding between oxide ceramics and adhesive cement systems: a systematic review", J Biomed Mater Res B Appl Biomater, 102, pp.395~413 (2014)
- Wegner SM, "Long-term resin bond strength to zirconia ceramic", J Adhes Dent, 2, pp.139~147 (2000)
- Wolfart M, "Durability of the resin bond strength to zirconia ceramic after using different surface conditioning methods", Dent Mater, 23, pp.45~50 (2007)
- Myung-Jin Lim, "The effect of continuous application of MDP-containing primer and luting resin cement on bond strength to tribochemical silica-coated Y-TZP", Restorative Dentistry and Endodontics, 43(2), pp.1~10 (2018), 대한치과보존학회
- Özcan M, "Effect of surface conditioning methods on the bond strength of luting cement to ceramics", Dent Mater, 19, pp.725~731 (2003)
- 이정진, "Evaluation of shear bond strength between dual cure resin cement and zirconia ceramic after thermocycling treatment", The Journal of Advanced of Prosthodontics, 7(1), pp.1~7 (2015), 대한치과보철학회[DOI]
- Garvie RC, "Phase analysis in zirconia systems", J Am Ceram Soc, 55, pp.303~305 (1972)
- Toraya H, "Calibration curve for quantitative analysis of the monoclinic-tetragonal ZrO2 system by X-ray diffraction", J Am Ceram Soc, 67, pp.C119~C121 (1984)
- Aboushelib MN, "Bonding to zirconia using a new surface treatment", J Prosthodont, 19, pp.340~346 (2010)
- Kosmac T, "The effect of surface grinding and sandblasting on flexural strength and reliability of Y-TZP zirconia ceramic", Dent Mater, 15, pp.426~433 (1999)
- Sato H, "Mechanical properties of dental zirconia ceramics changed with sandblasting and heat treatment", Dent Mater J, 27, pp.408~414 (2008)
- Guazzato M, "Influence of surface and heat treatments on the flexural strength of Y-TZP dental ceramic", J Dent, 33, pp.9~18 (2005)
- Smielak B, "Effect of hydrofluoric acid concentration and etching duration on select surface roughness parameters for zirconia", J Prosthet Dent, 113, pp.596~602 (2015)
- Kang YJ, "Effect of low-concentration hydrofluoric acid etching on shear bond strength and biaxial flexural strength after thermocycling", Materials (Basel), 13, pp.1409~ (2020)
- Meryem Gülce Subaşı, "Mechanical properties of zirconia after different surface treatments and repeated firings", The Journal of Advanced of Prosthodontics, 6(6), pp.462~467 (2014), 대한치과보철학회[DOI]
- Lee JH, "Effect of the surface treatment method using airborne-particle abrasion and hydrofluoric acid on the shear bond strength of resin cement to zirconia", Dent J (Basel), 5, pp.23~ (2017)
- Mi-Kyung Yu, "Effect of hydrofluoric acid-based etchant at an elevated temperature on the bond strength and surface topography of Y-TZP ceramics", Restorative Dentistry and Endodontics, 45(1), pp.1~8 (2020), 대한치과보존학회[DOI]
- Attia A, "Bond strength of three luting agents to zirconia ceramic - influence of surface treatment and thermocycling", J Appl Oral Sci, 19, pp.388~395 (2011)
- Ding Q, "Effects of different surface treatments on the cyclic fatigue strength of one-piece CAD", CAM zirconia implants, 2018, pp.84, 249~257