Effect of zirconia surface treatment using nitric acid-hydrofluoric acid on the shear bond strengths of resin cements
2
조회
0
다운로드
5
인용
0
참고문헌
키워드
초록
PURPOSE. The aim of this study was to compare the surface roughness of zirconia when using Zircos E etching system (ZSAT), applying a nitric acid-hydrofluoric acid compound as a pretreatment agent, and also to compare the shear bonding strength according to different resin cements. MATERIALS AND METHODS. ZSAT, air abrasion, and tribochemical silicacoating were applied on prepared 120 zirconia specimens (10 mm in diameter, 7 mm in height) using CAD/CAM. Each 12 specimens with 4 different resin cements (Panavia F 2.0, Rely X Unicem, Superbond C&B, and Hot bond) were applied to test interfacial bond strength. The statistical analysis was performed using SAS 9.1 (SAS Institute Inc., Cary, NC, USA). The results are as follows: after application of the ZSAT on the zirconia specimens, surface roughness value after 2-hour etching was higher than those after 1-and 3-hour etching on SEM images. RESULTS. For Superbond C&B and Rely X Unicem, the specimens treated with ZSAT showed higher shear bond strength values than those treated with air abrasion and tribochemical silicacoating system. Regarding the failure mode of interface over cement and zirconia surface, Rely X Unicem and Hot bond showed cohesive failures and Panavia F 2.0 and Superbond C&B showed mixed failures. CONCLUSION. Zircos E etching system in zirconia restoration could increase its shear bond strength. However, its long term success rate and clinical application should be further evaluated.
Abstract
PURPOSE. The aim of this study was to compare the surface roughness of zirconia when using Zircos E etching system (ZSAT), applying a nitric acid-hydrofluoric acid compound as a pretreatment agent, and also to compare the shear bonding strength according to different resin cements. MATERIALS AND METHODS. ZSAT, air abrasion, and tribochemical silicacoating were applied on prepared 120 zirconia specimens (10 mm in diameter, 7 mm in height) using CAD/CAM. Each 12 specimens with 4 different resin cements (Panavia F 2.0, Rely X Unicem, Superbond C&B, and Hot bond) were applied to test interfacial bond strength. The statistical analysis was performed using SAS 9.1 (SAS Institute Inc., Cary, NC, USA). The results are as follows: after application of the ZSAT on the zirconia specimens, surface roughness value after 2-hour etching was higher than those after 1-and 3-hour etching on SEM images. RESULTS. For Superbond C&B and Rely X Unicem, the specimens treated with ZSAT showed higher shear bond strength values than those treated with air abrasion and tribochemical silicacoating system. Regarding the failure mode of interface over cement and zirconia surface, Rely X Unicem and Hot bond showed cohesive failures and Panavia F 2.0 and Superbond C&B showed mixed failures. CONCLUSION. Zircos E etching system in zirconia restoration could increase its shear bond strength. However, its long term success rate and clinical application should be further evaluated.
참고문헌 (23)
- Koutayas SO, "Zirconia in dentistry: part 2. Evidence-based clinical breakthrough", Eur J Esthet Dent, 4, pp.348~380 (2009)
- Reich S, "Clinical fit of fourunit zirconia posterior fixed dental prostheses", Eur J Oral Sci, 116, pp.579~584 (2008)
- Sailer I, "Five-year clinical results of zirconia frameworks for posterior fixed partial dentures", Int J Prosthodont, 20, pp.383~388 (2007)
- Kern M, "Bonding to zirconia ceramic: adhesion methods and their durability", Dent Mater, 14, pp.64~71 (1998)
- Qeblawi DM, "The effect of zirconia surface treatment on flexural strength and shear bond strength to a resin cement", J Prosthet Dent, 103, pp.210~220 (2010)
- Thompson JY, "Adhesion", cementation to zirconia and other non-silicate ceramics: where are we now?, 2011, pp.27, 71~82
- Blatz MB, "In vitro evaluation of shear bond strengths of resin to densely-sintered high-purity zirconium-oxide ceramic after long-term storage and thermal cycling", J Prosthet Dent, 91, pp.356~ (2004)
- Blatz MB, "Influence of surface treatment and simulated aging on bond strengths of luting agents to zirconia", Quintessence Int, 38, pp.745~753 (2007)
- Karimipour-Saryazdi M, "Influence of surface treatment of yttrium-stabilized tetragonal zirconium oxides and cement type on crown retention after artificial aging", J Prosthet Dent, 111, pp.395~403 (2014)
- Sriamporn T, "Dental zirconia can be etched by hydrofluoric acid", Dent Mater J, 33, pp.79~85 (2014)
- Vojdani M, "Comparison the Marginal and Internal Fit of Metal Copings Cast from Wax Patterns Fabricated by CAD", CAM and Conventional Wax up Techniques, 2013, pp.14, 118~129
- Martins LM, "Internal fit of two all-ceramic systems and metal-ceramic crowns", J Appl Oral Sci, 20, pp.235~240 (2012)
- Subaşı MG, "Influence of surface treatments and resin cement selection on bonding to zirconia", Lasers Med Sci, 29, pp.19~27 (2014)
- Tsukakoshi M, "Effects of dental adhesive cement and surface treatment on bond strength and leakage of zirconium oxide ceramics", Dent Mater J, 27, pp.159~171 (2008)
- Xible AA, "Effect of silica coating and silanization on flexural and composite-resin bond strengths of zirconia posts: An in vitro study", J Prosthet Dent, 95, pp.224~229 (2006)
- Yang B, "Influence of air-abrasion on zirconia ceramic bonding using an adhesive composite resin", Dent Mater, 26, pp.44~50 (2010)
- 이호정, "Effect of surface treatment methods on the shear bond strength of resincement to zirconia ceramic", 대한치과보철학회지, 45(6), pp.743~752 (2007), 대한치과보철학회
- Lüthy H, "Effect of thermocycling on bond strength of luting cements to zirconia ceramic", Dent Mater, 22, pp.195~200 (2006)
- Piwowarczyk A, "The shear bond strength between luting cements and zirconia ceramics after two pre-treatments", Oper Dent, 30, pp.382~388 (2005)
- Parsa RZ, "An in vitro comparison of tensile bond strengths of noble and base metal alloys to enamel", J Prosthet Dent, 90, pp.175~183 (2003)
- Ozcan M, "Effect of various surface conditioning methods on the adhesion of dual-cure resin cement with MDP functional monomer to zirconia after thermal aging", Dent Mater J, 27, pp.99~104 (2008)
- Reddy SM, "Evaluation of shear bond strength of zirconia bonded to dentin after various surface treatments of zirconia", J Indian Prosthodont Soc, 14, pp.38~41 (2014)
- 김지혜, "지르코니아 세라믹의 표면처리에 따른 치과용 접착제의 전단결합강도", 대한치과보철학회지, 51(2), pp.73~81 (2013), 대한치과보철학회[DOI]