Calcium-doped zinc oxide nanocrystals as an innovative intracanal medicament: a pilot study
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Objectives: This study investigated the cytotoxicity, radiopacity, pH, and dentinal tubule penetration of a paste of 1.0% calcium-doped zinc oxide nanocrystals (ZnO:1.0Ca) combined with propylene glycol (PRG) or polyethylene glycol and propylene glycol (PEG-PRG). Materials and methods: The pastes were prepared by mixing calcium hydroxide [Ca(OH)2] or ZnO:1.0Ca with PRG or a PEG-PRG mixture. The pH was evaluated after 24 and 96 hours of storage in deionized water. Digital radiographs were acquired for radiopacity analysis and bubble counting of each material. The materials were labeled with 0.1% fluorescein and applied to root canals, and images of their dentinal tubule penetration were obtained using confocal laser scanning microscopy. RAW264.7 macrophages were placed in different dilutions of culture media previously exposed to the materials for 24 and 96 hours and tested for cell viability using the MTT assay. Analysis of variance and the Tukey test (α = 0.05) were performed. Results: ZnO:1.0Ca materials showed lower viability at 1:1 and 1:2 dilutions than Ca(OH)2 materials (p < 0.0001). Ca(OH)2 had higher pH values than ZnO:1.0Ca at 24 and 96 hours, regardless of the vehicle (p < 0.05). ZnO:1.0Ca pastes showed higher radiopacity than Ca(OH)2 pastes (p < 0.01). No between-material differences were found in bubble counting (p = 0.0902). The ZnO:1.0Ca pastes had a greater penetration depth than Ca(OH)2 in the apical third (p < 0.0001). Conclusions: ZnO:1.0Ca medicaments presented higher penetrability, cell viability, and radiopacity than Ca(OH)2. Higher values of cell viability and pH were present in Ca(OH)2 than in ZnO:1.0Ca.
Abstract
Objectives: This study investigated the cytotoxicity, radiopacity, pH, and dentinal tubule penetration of a paste of 1.0% calcium-doped zinc oxide nanocrystals (ZnO:1.0Ca) combined with propylene glycol (PRG) or polyethylene glycol and propylene glycol (PEG-PRG). Materials and methods: The pastes were prepared by mixing calcium hydroxide [Ca(OH)2] or ZnO:1.0Ca with PRG or a PEG-PRG mixture. The pH was evaluated after 24 and 96 hours of storage in deionized water. Digital radiographs were acquired for radiopacity analysis and bubble counting of each material. The materials were labeled with 0.1% fluorescein and applied to root canals, and images of their dentinal tubule penetration were obtained using confocal laser scanning microscopy. RAW264.7 macrophages were placed in different dilutions of culture media previously exposed to the materials for 24 and 96 hours and tested for cell viability using the MTT assay. Analysis of variance and the Tukey test (α = 0.05) were performed. Results: ZnO:1.0Ca materials showed lower viability at 1:1 and 1:2 dilutions than Ca(OH)2 materials (p < 0.0001). Ca(OH)2 had higher pH values than ZnO:1.0Ca at 24 and 96 hours, regardless of the vehicle (p < 0.05). ZnO:1.0Ca pastes showed higher radiopacity than Ca(OH)2 pastes (p < 0.01). No between-material differences were found in bubble counting (p = 0.0902). The ZnO:1.0Ca pastes had a greater penetration depth than Ca(OH)2 in the apical third (p < 0.0001). Conclusions: ZnO:1.0Ca medicaments presented higher penetrability, cell viability, and radiopacity than Ca(OH)2. Higher values of cell viability and pH were present in Ca(OH)2 than in ZnO:1.0Ca.
참고문헌 (48)
- Bourguignon C, "International Association of Dental Traumatology guidelines for the management of traumatic dental injuries: 1. Fractures and luxations", Dent Traumatol, 36, pp.314~330 (2020)
- Lauridsen E, "Combination injuries 1. The risk of pulp necrosis in permanent teeth with concussion injuries and concomitant crown fractures", Dent Traumatol, 28, pp.364~370 (2012)
- Krastl G, "Endodontic management of traumatized permanent teeth: a comprehensive review", Int Endod J, 54, pp.1221~1245 (2021)
- Athanassiadis B, "Aspects of solvent chemistry for calcium hydroxide medicaments", Materials (Basel), 10, pp.1219~ (2017)
- Deniz Sungur D, "Effect of a low surface tension vehicle on the dentinal tubule penetration of calcium hydroxide and triple antibiotic paste", J Endod, 43, pp.452~455 (2017)
- Faria G, "Influence of the vehicle and antibiotic formulation on cytotoxicity of triple antibiotic paste", J Endod, 44, pp.1812~1816 (2018)
- de Jesus Soares A, "Apexification with a new intra-canal medicament: a multidisciplinary case report", Iran Endod J, 7, pp.165~170 (2012)
- Herrera DR, "Repair of apical root resorption associated with periodontitis using a new intracanal medicament protocol", J Oral Sci, 56, pp.311~314 (2014)
- Lima TF, "Influence of chlorhexidine and zinc oxide in calcium hydroxide pastes on pH changes in external root surface", Braz Oral Res, 33, pp.e005~ (2019)
- Guerreiro-Tanomaru JM, "Use of nanoparticulate zinc oxide as intracanal medication in endodontics: pH and antimicrobial activity", Acta Odontol Latinoam, 26, pp.144~148 (2013)
- Silva AC, "Cytotoxicity", pp.149~161 (2018), IntechOpen
- Souza Gabriela Leite de, "Effects of zinc oxide and calcium–doped zinc oxide nanocrystals on cytotoxicity and reactive oxygen species production in different cell culture models", Restorative Dentistry and Endodontics, 45(4), pp.1~16 (2020), 대한치과보존학회[DOI]
- Oliveira LV, "Biological parameters, discolouration and radiopacity of calcium silicate-based materials in a simulated model of partial pulpotomy", Int Endod J, 54, pp.2133~2144 (2021)
- Pintor AV, "MTT versus other cell viability assays to evaluate the biocompatibility of root canal filling materials: a systematic review", Int Endod J, 53, pp.1348~1373 (2020)
- Lin LM, "Repair and regeneration in endodontics", Int Endod J, 44, pp.889~906 (2011)
- Guerreiro-Tanomaru JM, "Release and diffusion of hydroxyl ion from calcium hydroxide-based medicaments", Dent Traumatol, 28, pp.320~323 (2012)
- Samiei M, "antibacterial effect of two nano zinc oxide gel preparations compared to calcium hydroxide and chlorhexidine mixture", Iran Endod J, 13, pp.305~311 (2018)
- de Almeida Barbosa M, "Effect of vehicle and agitation methods on the penetration of calcium hydroxide paste in the dentinal tubules", J Endod, 46, pp.980~986 (2020)
- Oliveira LV, "A laboratory evaluation of cell viability, radiopacity and tooth discoloration induced by regenerative endodontic materials", Int Endod J, 53, pp.1140~1152 (2020)
- Souza GL, "Cytotoxicity and effects of a new calcium hydroxide nanoparticle material on production of reactive oxygen species by LPS-stimulated dental pulp cells", Iran Endod J, 15, pp.227~235 (2020)
- Jeevanandam J, "Cytotoxicity analysis of morphologically different solgel-synthesized MgO nanoparticles and their in vitro insulin resistance reversal ability in adipose cells", Appl Biochem Biotechnol, 190, pp.1385~1410 (2020)
- Pan C, "Improved blood compatibility and endothelialization of titanium oxide nanotube arrays on titanium surface by zinc doping", ACS Biomater Sci Eng, 6, pp.2072~2083 (2020)
- Vasile BŞ, "Eu3+-doped ZnO nanostructures: advanced characterizations, photoluminescence and cytotoxic effect", Rom J Morphol Embryol, 58, pp.941~952 (2017)
- Mishra PK, "Zinc oxide nanoparticles: a promising nanomaterial for biomedical applications", Drug Discov Today, 22, pp.1825~1834 (2017)
- Grabrucker AM, "Development of novel Zn2+ loaded nanoparticles designed for cell-type targeted drug release in CNS neurons: in vitro evidences", PLoS One, 6, pp.e17851~ (2011)
- Yamamoto O, "Influence of particle size on the antibacterial activity of zinc oxide", Int J Inorg Mater, 3, pp.643~646 (2001)
- Jones N, "Antibacterial activity of ZnO nanoparticle suspensions on a broad spectrum of microorganisms", FEMS Microbiol Lett, 279, pp.71~76 (2008)
- Kishen A, "An investigation on the antibacterial and antibiofilm efficacy of cationic nanoparticulates for root canal disinfection", J Endod, 34, pp.1515~1520 (2008)
- International Organization for Standardization, "ISO 6876: dental root canal sealing materials", International Organization for Standardization, 3~4 (2012)
- Villa N, "A new calcium silicatebased root canal dressing: physical and chemical properties, cytotoxicity and dentinal tubule penetration", Braz Dent J, 31, pp.598~604 (2020)
- Shetty S, "An in-vitro evaluation of the pH change through root dentin using different calcium hydroxide preparations as an intracanal medicament", J Clin Diagn Res, 8, pp.ZC13~ZC16 (2014)
- Zancan RF, "Antimicrobial activity and physicochemical properties of calcium hydroxide pastes used as intracanal medication", J Endod, 42, pp.1822~1828 (2016)
- Louwakul P, "Efficacy of calcium oxide and calcium hydroxide nanoparticles on the elimination of Enterococcus faecalis in human root dentin", Clin Oral Investig, 21, pp.865~871 (2017)
- Fava LR, "Calcium hydroxide pastes: classification and clinical indications", Int Endod J, 32, pp.257~282 (1999)
- Mohammadi Z, "Properties and applications of calcium hydroxide in endodontics and dental traumatology", Int Endod J, 44, pp.697~730 (2011)
- Zand V, "Comparison of the penetration depth of conventional and nano-particle calcium hydroxide into dentinal tubules", Iran Endod J, 12, pp.366~370 (2017)
- Komabayashi T, "Particle size and shape of calcium hydroxide", J Endod, 35, pp.284~287 (2009)
- Paredes RM, "Chemical calcium indicators", Methods, 46, pp.143~151 (2008)
- Xuereb M, "Development of novel tricalcium silicate-based endodontic cements with sintered radiopacifier phase", Clin Oral Investig, 20, pp.967~982 (2016)
- Ordinola-Zapata R, "The effect of radiopacifiers agents on pH, calcium release, radiopacity, and antimicrobial properties of different calcium hydroxide dressings", Microsc Res Tech, 78, pp.620~625 (2015)
- Pelepenko LE, "Dental discoloration caused by Grey-MTAFlow cement: analysis of its physicochemical, biological and antimicrobial properties", J Appl Oral Sci, 28, pp.e20200269~ (2020)
- Galvão T, "Efficacy of three methods for inserting calcium hydroxide-based paste in root canals", J Clin Exp Dent, 9, pp.e762~e766 (2017)
- Zare Sahar, "Micro-computed tomographic evaluation of single-cone obturation with three sealers", Restorative Dentistry and Endodontics, 46(2), pp.1~12 (2021), 대한치과보존학회[DOI]
- Bhandi S, "Complete obturation-cold lateral condensation vs. thermoplastic techniques: a systematic review of micro-CT studies", Materials (Basel), 14, pp.4013~ (2021)
- Donnermeyer D, "Removal of calcium hydroxide from artificial grooves in straight root canals: sonic activation using EDDY versus passive ultrasonic irrigation and XP endo Finisher", J Endod, 45, pp.322~326 (2019)
- De Faria-Júnior NB, "Residues of calcium hydroxide-based intracanal medication associated with different vehicles: a scanning electron microscopy evaluation", Microsc Res Tech, 75, pp.898~902 (2012)
- Balvedi RP, "A comparison of two techniques for the removal of calcium hydroxide from root canals", Int Endod J, 43, pp.763~768 (2010)
- da Silva JM, "Microscopic cleanliness evaluation of the apical root canal after using calcium hydroxide mixed with chlorhexidine, propylene glycol, or antibiotic paste", Oral Surg Oral Med Oral Pathol Oral Radiol Endod, 111, pp.260~264 (2011)