Flow characteristics and alkalinity of novel bioceramic root canal sealers
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Objective: This study aimed to examine the physical properties (pH and flow) of 2 novel bioceramic sealers. Materials: and Methods The tested sealers were a calcium hydroxide sealer (Sealapex) and 2 bioceramic sealers (BioRoot RCS and TotalFill BC Sealer). Flow measurements were conducted according to ISO 6876/2012, with a press method of 0.05 mL of sealer. The pH of fresh samples was tested immediately after manipulation, while set samples were stored for 3 times the recommended setting time. The predetermined time intervals ranged from 3 minutes to 24 hours for fresh samples and from 10 minutes to 7 days and 4 weeks for the set samples. Analysis of variance was performed, with p = 0.05 considered indicating significance. Results: The mean flow values were 26.99 mm for BioRoot, 28.19 for Sealapex, and 30.8 mm for TotalFill BC Sealer, satisfying the ISO standard. In the set samples, BioRoot RCS had higher pH values at 24 hours to 1 week after immersion in distilled water. At 2 weeks, both bioceramic sealers had similar pH values, greater than that of Sealapex. In the fresh samples, the bioceramic sealers had significantly higher initial pH values than Sealapex (p < 0.05). At 24 hours post-immersion, all sealers showed an alkaline pH, with the highest pH observed for TotalFill. Conclusions: The TotalFill BC Sealer demonstrated the highest flow. The bioceramic sealers initially presented higher alkaline activity than the polymeric calcium hydroxide sealer. However, at 3 and 4 weeks post-immersion, all sealers had similar pH values.
Abstract
Objective: This study aimed to examine the physical properties (pH and flow) of 2 novel bioceramic sealers. Materials: and Methods The tested sealers were a calcium hydroxide sealer (Sealapex) and 2 bioceramic sealers (BioRoot RCS and TotalFill BC Sealer). Flow measurements were conducted according to ISO 6876/2012, with a press method of 0.05 mL of sealer. The pH of fresh samples was tested immediately after manipulation, while set samples were stored for 3 times the recommended setting time. The predetermined time intervals ranged from 3 minutes to 24 hours for fresh samples and from 10 minutes to 7 days and 4 weeks for the set samples. Analysis of variance was performed, with p = 0.05 considered indicating significance. Results: The mean flow values were 26.99 mm for BioRoot, 28.19 for Sealapex, and 30.8 mm for TotalFill BC Sealer, satisfying the ISO standard. In the set samples, BioRoot RCS had higher pH values at 24 hours to 1 week after immersion in distilled water. At 2 weeks, both bioceramic sealers had similar pH values, greater than that of Sealapex. In the fresh samples, the bioceramic sealers had significantly higher initial pH values than Sealapex (p < 0.05). At 24 hours post-immersion, all sealers showed an alkaline pH, with the highest pH observed for TotalFill. Conclusions: The TotalFill BC Sealer demonstrated the highest flow. The bioceramic sealers initially presented higher alkaline activity than the polymeric calcium hydroxide sealer. However, at 3 and 4 weeks post-immersion, all sealers had similar pH values.
참고문헌 (38)
- Schilder H, "Filling root canals in three dimensions. 1967", J Endod, 32, pp.281~290 (2006)
- Gopikrishna V, "Grossman's endodontic practice" (2018), Wolters Kluwer India
- Orstavik D, "Essential endodontology" (2020), Wiley Blackwell
- Donnermeyer D, "Endodontic sealers based on calcium silicates : a systematic review", Odontology, 107, pp.421~436 (2019)
- Al-Haddad A, "Bioceramic-based root canal sealers : a review", Int J Biomater, 2016, pp.9753210~ (2016)
- Siboni F, "Properties of BioRoot RCS, a tricalcium silicate endodontic sealer modified with povidone and polycarboxylate", Int Endod J, 50(Suppl 2), pp.e120~e136 (2017)
- da Silva LA, "Calcium hydroxide root canal sealers: evaluation of pH, calcium ion concentration and conductivity", Int Endod J, 30, pp.205~209 (1997)
- Urban K, "Solubility and pH value of 3 different root canal sealers : a long-term investigation", J Endod, 44, pp.1736~1740 (2018)
- Colombo M, "Biological and physico-chemical properties of new root canal sealers", J Clin Exp Dent, 10, pp.e120~e126 (2018)
- Poggio C, "Solubility and pH of bioceramic root canal sealers : a comparative study", J Clin Exp Dent, 9, pp.e1189~e1194 (2017)
- International Standards Organization, "Dentistry - root canal sealing materials (ISO 6876:2012)", ISO, ~ (2012)
- Zhou HM, "Physical properties of 5 root canal sealers", J Endod, 39, pp.1281~1286 (2013)
- 송유석, "In vitro evaluation of a newly produced resin-based endodontic sealer", Restorative Dentistry and Endodontics, 41(3), pp.189~195 (2016), 대한치과보존학회
- Lim ES, "Physical properties and biocompatibility of an injectable calcium-silicate-based root canal sealer : in vitro and in vivo study", BMC Oral Health, 15, pp.129~ (2015)
- Candeiro GT, "Evaluation of radiopacity, pH, release of calcium ions, and flow of a bioceramic root canal sealer", J Endod, 38, pp.842~845 (2012)
- Brackett MG, "Cytotoxicity of endodontic materials over 6-weeks ex vivo", Int Endod J, 41, pp.1072~1078 (2008)
- Scarparo RK, "Analysis of tissue reactions to methacrylate resin-based, epoxy resin-based, and zinc oxide-eugenol endodontic sealers", J Endod, 35, pp.229~232 (2009)
- Lee JK, "Physicochemical properties of epoxy resin-based and bioceramic-based root canal sealers", Bioinorg Chem Appl, 2017, pp.2582849~ (2017)
- Vertuan GC, "Evaluation of physicochemical properties of a new root canal sealer", J Endod, 44, pp.501~505 (2018)
- Khalil I, "Properties of tricalcium silicate sealers", J Endod, 42, pp.1529~1535 (2016)
- Tanomaru-Filho M, "Physicochemical properties and volumetric change of silicone", bioactive glass and calcium silicate-based endodontic sealers, 2017, pp.43, 2097~2101
- Chang SW, "Comparison of the rheological properties of four root canal sealers", Int J Oral Sci, 7, pp.56~61 (2015)
- Almeida JF, "Filling of artificial lateral canals and microleakage and flow of five endodontic sealers", Int Endod J, 40, pp.692~699 (2007)
- Silva EJ, "Evaluation of cytotoxicity and physicochemical properties of calcium silicate-based endodontic sealer MTA Fillapex", J Endod, 39, pp.274~277 (2013)
- Vitti RP, "Physical properties of MTA Fillapex sealer", J Endod, 39, pp.915~918 (2013)
- American National Standards Institute, "ANSI", ADA specification No. 57 for endodontic filling materials, 2000
- Marín-Bauza GA, "Physicochemical properties of endodontic sealers of different bases", J Appl Oral Sci, 20, pp.455~461 (2012)
- Reddi BA, "Why is saline so acidic(and does it really matter?)", Int J Med Sci, 10, pp.747~750 (2013)
- Zamparini F, "Properties of calcium silicate-monobasic calcium phosphate materials for endodontics containing tantalum pentoxide and zirconium oxide", Clin Oral Investig, 23, pp.445~457 (2019)
- Duarte MA, "Evaluation of pH and calcium ion release of three root canal sealers", J Endod, 26, pp.389~390 (2000)
- Eldeniz AU, "Evaluation of pH and calcium ion release of Acroseal sealer in comparison with Apexit and Sealapex sealers", Oral Surg Oral Med Oral Pathol Oral Radiol Endod, 103, pp.e86~e91 (2007)
- Siqueira JF Jr, "Evaluation of sealing ability, pH and flow rate of three calcium hydroxide-based sealers", Endod Dent Traumatol, 11, pp.225~228 (1995)
- Faria-Júnior NB, "Antibiofilm activity, pH and solubility of endodontic sealers", Int Endod J, 46, pp.755~762 (2013)
- Santos AD, "Physico-chemical properties of MTA and a novel experimental cement", Int Endod J, 38, pp.443~447 (2005)
- McHugh CP, "pH required to kill Enterococcus faecalis in vitro", J Endod, 30, pp.218~219 (2004)
- Okabe T, "Effects of pH on mineralization ability of human dental pulp cells", J Endod, 32, pp.198~201 (2006)
- Stuart CH, "Enterococcus faecalis : its role in root canal treatment failure and current concepts in retreatment", J Endod, 32, pp.93~98 (2006)
- Stock CJ, "Calcium hydroxide : root resorption and perio-endo lesions", Br Dent J, 158, pp.325~334 (1985)