Correlation between the size of released titanium particles and changes in the surface of dental implants during insertion into bone blocks: an in vitro study
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Purpose: This study investigated the size and amount of titanium particles immediately released following dental implant insertion into bovine bone blocks and aimed to correlate them with the surface roughness of the implants. Methods: Twelve bone blocks were prepared from bovine mandibles. Six tapered (group A) and 6 cylindrical (group B) dental implants were inserted into the bone blocks under water irrigation, following the standard drilling protocol. After insertion, the implants were immediately removed from the bone. Scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and atomic force microscopy were performed to investigate the released titanium particles and implant surface roughness, respectively. The amount of titanium ions in the irrigation water was measured using inductively coupled plasma mass spectrometry. Dynamic light scattering (DLS) was used to determine the size range of the released titanium particles. Results: The percentages of titanium content on the surface of implants decreased in both groups after implantation into bone blocks. SEM-EDX analysis confirmed the presence of titanium particles embedded in the implanted bone bed. Group B implants showed significantly higher concentrations of titanium ions in the collected water than group A implants (0.868 and 0.565 μg/L, respectively). Group A implants demonstrated high pre-implantation surface roughness, which led to a much greater decrease in post-implantation surface roughness than was observed for group B implants. DLS analysis showed that the titanium particles released from group A implants were within the nano-size range, whereas those released from group B implants were within the micro-size range. Conclusions: Dental implant placement leads to a decrease in implant surface roughness and the immediate release of titanium particles into the peri-implant bone. Variations in the size range and amount of released particles were correlated with implant surface roughness. This finding has clinical implications and warrants additional in vivo studies.
Abstract
Purpose: This study investigated the size and amount of titanium particles immediately released following dental implant insertion into bovine bone blocks and aimed to correlate them with the surface roughness of the implants. Methods: Twelve bone blocks were prepared from bovine mandibles. Six tapered (group A) and 6 cylindrical (group B) dental implants were inserted into the bone blocks under water irrigation, following the standard drilling protocol. After insertion, the implants were immediately removed from the bone. Scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and atomic force microscopy were performed to investigate the released titanium particles and implant surface roughness, respectively. The amount of titanium ions in the irrigation water was measured using inductively coupled plasma mass spectrometry. Dynamic light scattering (DLS) was used to determine the size range of the released titanium particles. Results: The percentages of titanium content on the surface of implants decreased in both groups after implantation into bone blocks. SEM-EDX analysis confirmed the presence of titanium particles embedded in the implanted bone bed. Group B implants showed significantly higher concentrations of titanium ions in the collected water than group A implants (0.868 and 0.565 μg/L, respectively). Group A implants demonstrated high pre-implantation surface roughness, which led to a much greater decrease in post-implantation surface roughness than was observed for group B implants. DLS analysis showed that the titanium particles released from group A implants were within the nano-size range, whereas those released from group B implants were within the micro-size range. Conclusions: Dental implant placement leads to a decrease in implant surface roughness and the immediate release of titanium particles into the peri-implant bone. Variations in the size range and amount of released particles were correlated with implant surface roughness. This finding has clinical implications and warrants additional in vivo studies.
참고문헌 (24)
- Silva RC, "Titanium dental implants : an overview of applied nanobiotechnology to improve biocompatibility and prevent infections", Materials(Basel), 15, pp.3150~ (2022)
- Kim KT, "General review of titanium toxicity", Int J Implant Dent, 5, pp.10~ (2019)
- Matos GR, "Surface roughness of dental implant and osseointegration", J Maxillofac Oral Surg, 20, pp.1~4 (2021)
- Kant B, "A randomized controlled trial comparing the radiographic evaluation of crestal bone resorption in single implant versus two implant-retained overdentures", J Family Med Prim Care, 8, pp.1594~1598 (2019)
- Meyer U, "Fast element mapping of titanium wear around implants of different surface structures", Clin Oral Implants Res, 17, pp.206~211 (2006)
- Olmedo D, "An experimental study of the dissemination of titanium and zirconium in the body", J Mater Sci Mater Med, 13, pp.793~796 (2002)
- Frisken KW, "A study of titanium release into body organs following the insertion of single threaded screw implants into the mandibles of sheep", Aust Dent J, 47, pp.214~217 (2002)
- Weingart D, "Titanium deposition in regional lymph nodes after insertion of titanium screw implants in maxillofacial region", Int J Oral Maxillofac Surg, 23, pp.450~452 (1994)
- Delgado-Ruiz R, "Potential causes of titanium particle and ion release in implant dentistry : a systematic review", Int J Mol Sci, 19, pp.3585~ (2018)
- Amengual-Peñafiel L, "Osteoimmunology drives dental implant osseointegration : a new paradigm for implant dentistry", Jpn Dent Sci Rev, 57, pp.12~19 (2021)
- Lechner J, "Titanium implants and silent inflammation in jawbone-a critical interplay of dissolved titanium particles and cytokines TNF-α and RANTES", CCL5 on overall health?, 2018, pp.9, 331~343
- Heibel H, "Cortical thickness of the mandible with special reference to miniplate osteosynthesis. Morphometric analysis of autopsy material", Mund Kiefer Gesichtschir, 5, pp.180~185 (2001)
- Katranji A, "Cortical bone thickness in dentate and edentulous human cadavers", J Periodontol, 78, pp.874~878 (2007)
- Elias CN, "Biomedical applications of titanium and its alloys", J Miner Met Mater Soc, 60, pp.46~49 (2008)
- Asa’ad F, "The role of titanium particles and ions in the pathogenesis of peri-implantitis", J Bone Metab, 29, pp.145~154 (2022)
- He X, "Analysis of titanium and other metals in human jawbones with dental implants-a case series study", Dent Mater, 32, pp.1042~1051 (2016)
- Dong WP, "An integrated approach to the characterization of surface wear I : qualitative characterization", Wear, 181-183, pp.700~716 (1995)
- Le Guéhennec L, "Surface treatments of titanium dental implants for rapid osseointegration", Dent Mater, 23, pp.844~854 (2007)
- De Maeztu MA, "Ion implantation : surface treatment for improving the bone integration of titanium and Ti6Al4V dental implants", Clin Oral Implants Res, 14, pp.57~62 (2003)
- Zareidoost A, "The relationship of surface roughness and cell response of chemical surface modification of titanium", J Mater Sci Mater Med, 23, pp.1479~1488 (2012)
- Wang ML, "Direct and indirect induction of apoptosis in human mesenchymal stem cells in response to titanium particles", J Orthop Res, 21, pp.697~707 (2003)
- Coen N, "Particulate debris from a titanium metal prosthesis induces genomic instability in primary human fibroblast cells", Br J Cancer, 88, pp.548~552 (2003)
- Borgognoni CF, "Reaction of human macrophages on protein corona covered TiO2 nanoparticles", Nanomedicine, 11, pp.275~282 (2015)
- Sundfeldt M, "Aseptic loosening, not only a question of wear : a review of different theories", Acta Orthop, 77, pp.177~197 (2006)