A Liner Breakage in Total Hip Arthroplasty after Using 1st Generation Highly Cross Linked Polyethylene Mated against 36-mm Metal Head: A Case Report
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
It has been known the highly cross linked polyethylene (HXLPE) has an advantage of improved wear rate. However, the alteration in mechanical properties such as decreased tensile yield and fatigue strength make concerns about fragility of HXLPE. We experienced a case of HXLPE breakage. But, this case of liner breakage happened although patient belonged to normal BMI and proper acetabular cup position so called “safe zone” on radiographs. So, we report this case with reference review.
Abstract
It has been known the highly cross linked polyethylene (HXLPE) has an advantage of improved wear rate. However, the alteration in mechanical properties such as decreased tensile yield and fatigue strength make concerns about fragility of HXLPE. We experienced a case of HXLPE breakage. But, this case of liner breakage happened although patient belonged to normal BMI and proper acetabular cup position so called “safe zone” on radiographs. So, we report this case with reference review.
참고문헌 (10)
- Soong M, "Dislocation after total hip arthroplasty", J Am Acad Orthop Surg, 12, pp.314~321 (2004)
- Johnson AJ, "Short-term wear evaluation of thin acetabular liners on 36-mm femoral heads", Clin Orthop Relat Res, 472, pp.624~629 (2014)
- Lee JH, "Midterm results of primary total hip arthroplasty using highly cross-linked polyethylene : minimum 7-year follow-up study", J Arthroplasty, 26, pp.1014~1019 (2011)
- Harris WH, "A review of current crosslinked polyethylenes used in total joint arthroplasty", Clin Orthop Relat Res, (430), pp.46~52 (2005)
- Pruitt LA, "Deformation, yielding, fracture and fatigue behavior of conventional and highly cross-linked ultra high molecular weight polyethylene", Biomaterials, 26, pp.905~915 (2005)
- Tower SS, "Rim cracking of the cross-linked longevity polyethylene acetabular liner after total hip arthroplasty", J Bone Joint Surg Am, 89, pp.2212~2217 (2007)
- Waewsawangwong W, "Unexpected failure of highly cross-linked polyethylene acetabular liner", J Arthroplasty, 27, pp.323.e1~323.e4 (2012)
- Moore KD, "Early failure of a cross-linked polyethylene acetabular liner. A case report", J Bone Joint Surg Am, 90, pp.2499~2504 (2008)
- Berry DJ, "Catastrophic failure of the polyethylene liner of uncemented acetabular components", J Bone Joint Surg Br, 76, pp.575~578 (1994)
- Puértolas JA, "Influence of the remelting process on the fatigue behavior of electron beam irradiated UHMWPE", J Biomed Mater Res B Appl Biomater, 76, pp.346~353 (2006)