Effect of Nd:YAG laser irradiation on adherence of retrograde filling materials: evaluation by microcomputed tomography
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Background/Purpose: The purpose of this study was to evaluate the effect of Nd:YAG irradiation on adherence of retrograde filling materials (mineral trioxide aggregate [MTA] and Super-EBA) by micro-computed tomography (CT) measurement and to observe the dentinal surface after irradiation by scanning electron microscopy (SEM). Materials and methods: Forty retrofilling models using extracted human teeth were divided into four groups according to the material and method used: ProRoot MTA (MTA group), Super-EBA (EBA group), MTA with Nd:YAG laser irradiation (LMTA group), and Super-EBA with Nd:YAG laser irradiation (LEBA group). All specimens were stored in 100% humidity for 24 hours until micro-CT was performed. The gap volume of the tooth/material interface was measured using the CTAn program. In six samples, the laser-irradiated dentin surface was observed using SEM. Results: The mean percent difference in gap volume was not statistically significant between the Nd:YAG laser-irradiated groups and non-irradiated in both materials(P > 0.05). The gap volume in the MTA group was significantly lower than that in the EBA group (P < 0.05). Examination of the non-irradiated specimens by SEM showed patent dentinal tubules. In contrast, alterations in the texture of the dentin surface and obliteration of the dentinal tubules were evident in the Nd:YAG laser-irradiated specimens. Conclusion: In this study, changes in the dentinal surface after Nd:YAG irradiation did not affect adherence between the apical filling material and the dentin wall.
Abstract
Background/Purpose: The purpose of this study was to evaluate the effect of Nd:YAG irradiation on adherence of retrograde filling materials (mineral trioxide aggregate [MTA] and Super-EBA) by micro-computed tomography (CT) measurement and to observe the dentinal surface after irradiation by scanning electron microscopy (SEM). Materials and methods: Forty retrofilling models using extracted human teeth were divided into four groups according to the material and method used: ProRoot MTA (MTA group), Super-EBA (EBA group), MTA with Nd:YAG laser irradiation (LMTA group), and Super-EBA with Nd:YAG laser irradiation (LEBA group). All specimens were stored in 100% humidity for 24 hours until micro-CT was performed. The gap volume of the tooth/material interface was measured using the CTAn program. In six samples, the laser-irradiated dentin surface was observed using SEM. Results: The mean percent difference in gap volume was not statistically significant between the Nd:YAG laser-irradiated groups and non-irradiated in both materials(P > 0.05). The gap volume in the MTA group was significantly lower than that in the EBA group (P < 0.05). Examination of the non-irradiated specimens by SEM showed patent dentinal tubules. In contrast, alterations in the texture of the dentin surface and obliteration of the dentinal tubules were evident in the Nd:YAG laser-irradiated specimens. Conclusion: In this study, changes in the dentinal surface after Nd:YAG irradiation did not affect adherence between the apical filling material and the dentin wall.
참고문헌 (28)
- Harty FJ, "The success rate of apicectomy. A retrospective study of 1,016 cases", Br Dent J, 129(9), pp.407~413 (1970)
- Gutmann JL, "Surgical endodontics" (1991), Blackwell Scientific Publications
- Dorn SO, "Retrograde filling materials: a retrospective success-failure study of amalgam, EBA, and IRM", J Endod, 16(8), pp.391~393 (1990)
- Frank AL, "Longterm evaluation of surgically placed amalgam fillings", J Endod, 18(8), pp.391~398 (1992)
- Lee SJ, "Sealing ability of a mineral trioxide aggregate for repair of lateral root perforations", J Endod, 19(11), pp.541~544 (1993)
- Torabinejad M, "Sealing ability of a mineral trioxide aggregate when used as a root end filling material", J Endod, 19(12), pp.591~595 (1993)
- Maillet WA, "Connective tissue response to root surfaces resected with Nd:YAG laser or burs", Oral Surg Oral Med Oral Pathol Oral Radiol Endod, 82(6), pp.681~690 (1996)
- Pozza DH, "CO(2), Er: YAG and Nd:YAG lasers in endodontic surgery", J Appl Oral Sci, 17(6), pp.596~599 (2009)
- Oliver CM, "Entrapped air and its effects on dye penetration of voids", Endod Dent Traumatol, 7(3), pp.135~138 (1991)
- Hammad M, "Evaluation of root canal obturation: a three-dimensional in vitro study", J Endod, 35(4), pp.541~544 (2009)
- Zeiger DN, "Evaluation of dental composite shrinkage and leakage in extracted teeth using X-ray microcomputed tomography", Dent Mater, 25(10), pp.1213~1220 (2009)
- Gondim E, Jr., "An investigation of microleakage from root-end fillings in ultrasonic retrograde cavities with or without finishing: a quantitative analysis", Oral Surg Oral Med Oral Pathol Oral Radiol Endod, 99(6), pp.755~760 (2005)
- Xavier CB, "Root-end filling materials: apical microleakage and marginal adaptation", J Endod, 31(7), pp.539~542 (2005)
- Pichardo MR, "Apical leakage of root-end placed SuperEBA, MTA, and Geristore restorations in human teeth previously stored in 10% formalin", J Endod, 32(10), pp.956~959 (2006)
- Wu MK, "Endodontic leakage studies reconsidered. Part I. Methodology, application and relevance", Int Endod J, 26(1), pp.37~43 (1993)
- Yildirim T, "Effect of smear layer and root-end cavity thickness on apical sealing ability of MTA as a root-end filling material: a bacterial leakage study", Oral Surg Oral Med Oral Pathol Oral Radiol Endod, 109(1), pp.e67~e72 (2010)
- Torabinejad M, "Bacterial leakage of mineral trioxide aggregate as a root-end filling material", J Endod, 21(3), pp.109~112 (1995)
- Scheerer SQ, "A comparative evaluation of three root-end filling materials: an in vitro leakage study using Prevotella nigrescens", J Endod, 27(1), pp.40~42 (2001)
- Mangin C, "The comparative sealing ability of hydroxyapatite cement, mineral trioxide aggregate, and super ethoxybenzoic acid as root-end filling materials", J Endod, 29(4), pp.261~264 (2003)
- Maltezos C, "Comparison of the sealing of Resilon, Pro Root MTA, and Super-EBA as root-end filling materials:a bacterial leakage study", J Endod, 32(4), pp.324~327 (2006)
- Jung M, "The imaging of root canal obturation using micro-CT", Int Endod J, 38(9), pp.617~626 (2005)
- Barletta FB, "In vitro comparative analysis of 2 mechanical techniques for removing gutta-percha during retreatment", J Can Dent Assoc, 73(1), pp.65~ (2007)
- Song M, "Outcomes of endodontic micro-resurgery: a prospective clinical study", J Endod, 37(3), pp.316~320 (2011)
- Bergmans L, "Bactericidal effect of Nd:YAG laser irradiation on some endodontic pathogens ex vivo", Int Endod J, 39(7), pp.547~557 (2006)
- Oliveira RG, "Scanning electron microscopy (SEM) and optical microscopy: effects of Er:YAG and Nd:YAG lasers on apical seals after apicoectomy and retrofill", Photomed Laser Surg, 22(6), pp.533~536 (2004)
- Lee BS, "Ultrastructural changes of human dentin after irradiation by Nd:YAG laser", Lasers Surg Med, 30(3), pp.246~252 (2002)
- Gurbuz T, "Evaluation of root canal dentin after Nd:YAG laser irradiation and treatment with five different irrigation solutions: a preliminary study", J Endod, 34(3), pp.318~321 (2008)
- Gilheany PA, "Apical dentin permeability and microleakage associated with root end resection and retrograde filling", J Endod, 20(1), pp.22~26 (1994)