Effect of Rice Straw Steaming Time and Mixing Ratio between Acacia mangium Willd Wood and Steamed Rice Straw on the Properties of the Mixed Particleboard
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
This study examined the effects of rice straw steaming time and mixing ratio between rice straw and wood particle on the properties of mixed particle board from Acacia mangium Willd wood and rice straw. Rice straw and Acacia mangium Willd wood were collected in Hanoi, Vietnam. The particle board was three-layer particle board with the structural ratio of 1：3：1. The thickness, density and board size of the particle board were 18 mm, 0.7 g/cm3, and 800x800x18 (mm, including trimming), respectively. A resin mixture between commercial Urea-formaldehyde (U-F) adhesive and methylene diphenyl isocyanate (MDI) adhesive was used with a dosage of 12% for the core layer and 14% for the surface layer. In this experimental design, the steaming time for rice straw was 15, 30, 45, 60, and 75 minutes at 100oC. The rice straw-wood mixing ratio was 10, 20, 30, 40, and 50%. The results showed that both mixing ratio and steaming time affect the properties of the particleboard, but the mixing ratio has a stronger impact. A higher mixing ratio and a longer steaming time resulted in a better quality of particleboard. The optimal steaming time for rice straw was 46.12 minutes with the straw-wood mixing ratio of 29.85% with the following characteristics of the particle board: the modulus of rupture (MOR) of 14.64 MPa, internal bond strength (IB) of 0.382 MPa, thickness swelling (TS) of 8.83%, and board density of 0.7-0.73 g/cm3.
Abstract
This study examined the effects of rice straw steaming time and mixing ratio between rice straw and wood particle on the properties of mixed particle board from Acacia mangium Willd wood and rice straw. Rice straw and Acacia mangium Willd wood were collected in Hanoi, Vietnam. The particle board was three-layer particle board with the structural ratio of 1：3：1. The thickness, density and board size of the particle board were 18 mm, 0.7 g/cm3, and 800x800x18 (mm, including trimming), respectively. A resin mixture between commercial Urea-formaldehyde (U-F) adhesive and methylene diphenyl isocyanate (MDI) adhesive was used with a dosage of 12% for the core layer and 14% for the surface layer. In this experimental design, the steaming time for rice straw was 15, 30, 45, 60, and 75 minutes at 100oC. The rice straw-wood mixing ratio was 10, 20, 30, 40, and 50%. The results showed that both mixing ratio and steaming time affect the properties of the particleboard, but the mixing ratio has a stronger impact. A higher mixing ratio and a longer steaming time resulted in a better quality of particleboard. The optimal steaming time for rice straw was 46.12 minutes with the straw-wood mixing ratio of 29.85% with the following characteristics of the particle board: the modulus of rupture (MOR) of 14.64 MPa, internal bond strength (IB) of 0.382 MPa, thickness swelling (TS) of 8.83%, and board density of 0.7-0.73 g/cm3.
참고문헌 (28)
- Bi NV, "Experimental design", pp.2005
- Binod P, "Bioethanol production from rice straw : an overview", Bioresource Technology, 101, pp.4767~4774 (2010)
- Cai Z, "Opportunities for using bio-based fibers for value added composites", In the proceedings of the 8th Pacific Rim bio-based composite symposium (2006)
- Chu TV, "Research on manufacturing fire retardant particleboard", 박사, pp.2001
- Duc NV, "Solutions to preserve particleboard", 박사, pp.2005
- Duong HT, "Research on solutions to improve the quality of particleboard", 박사, pp.2004
- Vietnam General Statistics Office, "Statistical handbook of Vietnam 2013" (2014)
- Haimes YY, "On a bicriterion formulation of the problems of integrated system identification and system optimization", IEEE Trans Syst Man Cybern, SMC-1, pp.296~297 (1971)
- Han G, "Effect of steam explosion treatment on characteristics of wheat straw", Industrial Crops and Products, 31, pp.28~33 (2010)
- Hien NT, "Effects of rice straw softening treatment conditions to the quality of particleboard from rice straw", 석사, pp.2011
- Hung LT, "Study on some rice straw pretreatment methods to improve its bondability by using chemicals", 석사, pp.2010
- Lambini CK, "A Comparative analysis of the effects of institutional property rights on forest livelihoods and forest conditions : evidence from Ghana and Vietnam", Forest Policy and Economics, 38, pp.178~190 (2014)
- Li X, "Effect of oxalic acid and steam pretreatment on the primary properties of UF-bonded rice straw particleboards", Industrial Crops and Products, 33, pp.665~669 (2011)
- Mantanis G, "Strawboards bonded with urea formaldehyde resins", the Proceedings of the 35th International Particleboard, 2001, ~[DOI]
- Effect of straw substitution level on properties of wood-straw hybrid particleboard, "Mei C", Nanjing Forestry University, ~ (2001)
- Mo X, "Compression and tensile strength of low density straw protein particleboard", Industrial Crops and Products, 14, pp.1~9 (2001)
- Ngoc LV, "Optimum pressing conditions for manufacturing particleboard from rice straw using as building materials", 석사, pp.2010
- Nguyen NT, "Land reform and farm production in the northern uplands of Vietnam", Asian Economic Journal, 26, pp.43~61 (2012)
- Nguyen TT, "Land privatization and afforestation incentive of rural farms in the northern uplands of Vietnam", Forest Policy and Economics, 12, pp.518~526 (2010)
- Nguyen TT, "The impact of land reform on farm households in the northern uplands of Vietnam" (2008), Margraf Publishers
- Nguyen TT, "Linking regional land use and payments for forest hydrological services : A case study of Hoa Binh Reservoir in Vietnam", Land Use Policy, 33, pp.130~140 (2013)
- Nguyen TT, "An economic analysis of reforestation with a native tree species : the case of Vietnamese farmers", Biodiversity and Conservation, 23(4), pp.811~830 (2014)
- Rowell RM, "The state of art and future development of biobased composite science and technology towards the 21st Century", the proceedings of the 4th Pacific Rim bio-based composite symposium (1998)
- Saadatnia M, "Comparing sound absorption characteristic of acoustic boards made of Aspen particles and different percentage of Wheat and Barely straws", 17th World Conference on Nondestructive Testing (2008)
- Research on the manufacturing technology of particleboard from Ceiba pentandra wood, "Thiet NV", ~ (1996)
- Wang W, "Adhesive application method in MDI-U-F particleboard manufacture", Front For China, 2, pp.225~229 (2006)
- Yang HS, "Rice straw–wood particle composite for sound absorbing wooden construction materials", Bioresource Technology, 86, pp.117~121 (2003)
- Youngquist YA, "Agricultural fibers in composition panels", the Proceedings of the 35th International Particleboard, 1993, ~[DOI]