Polymerization behavior and thermal characteristics of two new composites at five temperatures: refrigeration to preheating
0
조회
0
다운로드
1
인용
0
참고문헌
초록
PURPOSE. Heat of composite polymerization (HP) indicates setting efficacy and temperature increase of composite in clinical procedures. The purpose of this in vitro experimental study was to evaluate the effects of 5 temperatures on HP of two new composites. MATERIALS AND METHODS. From each material (Core Max II [CM] and King Dental [KD]), 5 groups of 5 specimens each were prepared and their total HPs (J/gr) were measured and recorded, at one of the constant temperatures 0℃, 15℃, 23℃, 37℃ and 60℃ (2 × 5 × 5 specimens) using a differential scanning calorimetry (DSC) analyzer. The data were analyzed using a two-way ANOVA, a Tukey’s test, an independent-samples ttest, and a linear regression analysis (α=0.05). RESULTS. No polymerization reactions occurred at 0℃ then this temperature was excluded from statistical analyses. The mean HP of the remaining 20 KD specimens was 20.5 ± 14.9 J/gr, while it was 40.7 ± 12.9 J/gr for CM. The independent-samples t-test showed that there were significant differences between the HP of the two materials at the temperatures 15℃ (P=.0001), 23℃ (P=.0163), 37℃ (P=.0039), and 60℃ (P=.0106). Linear regression analysis showed statistically significant correlations between environment temperatures and HP of CM (R2=0.777). CONCLUSION. Using CM is advantageous over conventional composite because of its better polymerization capacity. However due to its high HP, further studies should assess its temperature increase in vivo. Preheating KD is recommended. Refrigerating composites can negatively affect their polymerization potential.
Abstract
PURPOSE. Heat of composite polymerization (HP) indicates setting efficacy and temperature increase of composite in clinical procedures. The purpose of this in vitro experimental study was to evaluate the effects of 5 temperatures on HP of two new composites. MATERIALS AND METHODS. From each material (Core Max II [CM] and King Dental [KD]), 5 groups of 5 specimens each were prepared and their total HPs (J/gr) were measured and recorded, at one of the constant temperatures 0℃, 15℃, 23℃, 37℃ and 60℃ (2 × 5 × 5 specimens) using a differential scanning calorimetry (DSC) analyzer. The data were analyzed using a two-way ANOVA, a Tukey’s test, an independent-samples ttest, and a linear regression analysis (α=0.05). RESULTS. No polymerization reactions occurred at 0℃ then this temperature was excluded from statistical analyses. The mean HP of the remaining 20 KD specimens was 20.5 ± 14.9 J/gr, while it was 40.7 ± 12.9 J/gr for CM. The independent-samples t-test showed that there were significant differences between the HP of the two materials at the temperatures 15℃ (P=.0001), 23℃ (P=.0163), 37℃ (P=.0039), and 60℃ (P=.0106). Linear regression analysis showed statistically significant correlations between environment temperatures and HP of CM (R2=0.777). CONCLUSION. Using CM is advantageous over conventional composite because of its better polymerization capacity. However due to its high HP, further studies should assess its temperature increase in vivo. Preheating KD is recommended. Refrigerating composites can negatively affect their polymerization potential.
참고문헌 (26)
- Shillingburg HT, "Fundamentals of fixed prosthodontics" (1997), Quintessence Publishing
- Kovarik RE, "Fatigue life of three core materials under simulated chewing conditions", J Prosthet Dent, 68, pp.584~590 (1992)
- Antonucci JM, "Extent of polymerization of dental resins by differential scanning calorimetry", J Dent Res, 62, pp.121~125 (1983)
- Prasanna N, "Degree of conversion and residual stress of preheated and roomtemperature composites", Indian J Dent Res, 18, pp.173~176 (2007)
- Cotti E, "Comparison of the Degree of Conversion of Resin Based Endodontic Sealers Using the DSC Technique", Eur J Dent, 5, pp.131~138 (2011)
- Daronch M, "Monomer conversion of pre-heated composite", J Dent Res, 84, pp.663~667 (2005)
- Awliya WY, "The influence of temperature on the efficacy of polymerization of composite resin", J Contemp Dent Pract, 8, pp.9~16 (2007)
- Faria-E-Silva AL, "Time-dependent effect of refrigeration on viscosity and conversion kinetics of dental madhesive resins", Eur J Dent, 4, pp.150~155 (2010)
- Daronch M, "Clinically relevant issues related to preheating composites", J Esthet Restor Dent, 18, pp.340~350 (2006)
- Lohbauer U, "The effect of resin composite pre-heating on monomer conversion and polymerization shrinkage", Dent Mater, 25, pp.514~519 (2009)
- Choudhary N, "Effect of preheating composite resin on gap formation at three different temperatures", J Conserv Dent, 14, pp.191~195 (2011)
- Driscoll CF, "Comparison of exothermic release during polymerization of four materials used to fabricate interim restorations", J Prosthet Dent, 65, pp.504~506 (1991)
- Hussey DL, "Thermographic assessment of heat generated on the root surface during post space preparation", Int Endod J, 30, pp.187~190 (1997)
- Lipski M, "Root surface temperature rises during root canal obturation, in vitro, by the continuous wave of condensation technique using System B HeatSource", Oral Surg Oral Med Oral Pathol Oral Radiol Endod, 99, pp.505~510 (2005)
- Behnia A, "In vitro infrared thermographic assessment of root surface temperatures generated by the thermafil plus system", J Endod, 27, pp.203~205 (2001)
- Atai M, "Synthesis, characterization, shrinkage and curing kinetics of a new low-shrinkage urethane dimethacrylate monomer for dental applications", Dent Mater, 23, pp.1030~1041 (2007)
- Lee H, "Heat of polymerization of nine mono-, di-, and trimethacrylate esters tested neat and with low levels of peroxide by dynamic differential scanning calorimetry", Dent Mater, 2, pp.175~178 (1986)
- MartIn JL, "Kinetic analysis of an asymmetrical DSC peak in the curing of an unsaturated polyester resin catalysed with MEKP and cobalt octoate", Polymer, 40, pp.3451~3462 (1999)
- Tanimoto Y, "Analysis of photopolymerization behavior of UDMA", TEGDMA resin mixture and its composite by differential scanning calorimetry, 2005, pp.72, 310~315
- Atai M, "Temperature rise and degree of photopolymerization conversion of nanocomposites and conventional dental composites", Clin Oral Investig, 13, pp.309~316 (2009)
- Chung KH, "Correlation between degree of conversion, filler concentration and mechanical properties of posterior composite resins", J Oral Rehabil, 17, pp.487~494 (1990)
- Guiraldo RD, "Influence of light energy density on heat generation during photoactivation of dental composites with different dentin and composite thickness", J Appl Oral Sci, 17, pp.289~293 (2009)
- Bayne SC, "Biomaterials in: Sturdevant’s art and science of operative dentistry", pp.135~242 (2006), The CV Mosby Co
- Pojman JA, "Free-radical frontal polymerization: self-propagating thermal reaction waves", J Chem Soc Faraday Trans, 92, pp.2825~2837 (1996)
- Daronch M, "Effect of composite temperature on in vitro intrapulpal temperature rise", Dent Mater, 23, pp.1283~1288 (2007)
- Tantbirojn D, "Hardness and postgel shrinkage of preheated composites", Quintessence Int, 42, pp.51~59 (2011)