Effect of ascorbic acid, ethanol and acetone on adhesion between the treated fiber posts and composite resin cores
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
PURPOSE. The aim of the present study was to assess the effect of ascorbic acid, ethanol and acetone on microtensile bond strength between fiber posts pre-treated with hydrogen peroxide and composite resin cores. MATERIALS AND METHODS. Twenty four fiber posts were pre-treated with 24% hydrogen peroxide and divided into 4 groups as follows: G1: no treatment, as control group; G2: treatment with 10% ascorbic acid solution for 5 minutes; G3: treatment with 70% ethanol solution for 5 minutes; and G4: treatment with70% acetone solution for 5 minutes. Each fiber post was surrounded by a cylinder-shaped polyglass matrix which was subsequently filled with composite resin. Two sections from each sample were selected for microtensile test at a crosshead with speed of 0.5 mm/min. Statistical analyses were performed using one-way ANOVA and a post hoc Tukey HSD test. Fractured surfaces were observed under a stereomicroscope at ×20 magnification. The fractured surfaces of the specimens were observed and evaluated under a SEM. RESULTS. Means of microtensile bond strength values (MPa) and standard deviations in the groups were as follows: G1: 9.70±0.81; G2: 12.62±1.80; G3: 16.60±1.93; and G4: 21.24±1.95. G4 and G1 had the highest and the lowest bond strength values, respectively. A greater bond strength value was seen in G3 compared to G2. There were significant differences between all the groups (P<.001). All the failures were of the adhesive mode. CONCLUSION. Application of antioxidant agents may increase microtensile bond strength between fiber posts treated with hydrogen peroxide and composite cores. Acetone increased bond strength more than ascorbic acid and ethanol.
Abstract
PURPOSE. The aim of the present study was to assess the effect of ascorbic acid, ethanol and acetone on microtensile bond strength between fiber posts pre-treated with hydrogen peroxide and composite resin cores. MATERIALS AND METHODS. Twenty four fiber posts were pre-treated with 24% hydrogen peroxide and divided into 4 groups as follows: G1: no treatment, as control group; G2: treatment with 10% ascorbic acid solution for 5 minutes; G3: treatment with 70% ethanol solution for 5 minutes; and G4: treatment with70% acetone solution for 5 minutes. Each fiber post was surrounded by a cylinder-shaped polyglass matrix which was subsequently filled with composite resin. Two sections from each sample were selected for microtensile test at a crosshead with speed of 0.5 mm/min. Statistical analyses were performed using one-way ANOVA and a post hoc Tukey HSD test. Fractured surfaces were observed under a stereomicroscope at ×20 magnification. The fractured surfaces of the specimens were observed and evaluated under a SEM. RESULTS. Means of microtensile bond strength values (MPa) and standard deviations in the groups were as follows: G1: 9.70±0.81; G2: 12.62±1.80; G3: 16.60±1.93; and G4: 21.24±1.95. G4 and G1 had the highest and the lowest bond strength values, respectively. A greater bond strength value was seen in G3 compared to G2. There were significant differences between all the groups (P<.001). All the failures were of the adhesive mode. CONCLUSION. Application of antioxidant agents may increase microtensile bond strength between fiber posts treated with hydrogen peroxide and composite cores. Acetone increased bond strength more than ascorbic acid and ethanol.
참고문헌 (33)
- Al-Omiri MK, "Fracture resistance of teeth restored with post-retained restorations: an overview", J Endod, 36, pp.1439~1449 (2010)
- Bateman G, "Fibre-based post systems: a review", Br Dent J, 195, pp.43~48 (2003)
- Schmage P, "Effect of surface conditioning on the retentive bond strengths of fiberreinforced composite posts", J Prosthet Dent, 102, pp.368~377 (2009)
- Grandini S, "Fatigue resistance and structural characteristics of fiber posts: three-point bending test and SEM evaluation", Dent Mater, 21, pp.75~82 (2005)
- Monticelli F, "Post-surface conditioning improves interfacial adhesion in post", core restorations, 2006, pp.22, 602~609
- Soares CJ, "Influence of airborne-particle abrasion on mechanical properties and bond strength of carbon", epoxy and glass, J Prosthet Dent, pp.2008, 99[DOI]
- Monticelli F, "Surface treatments for improving bond strength to prefabricated fiber posts: a literature review", Oper Dent, 33, pp.346~355 (2008)
- D'Arcangelo C, "Influence of surface treatments on the flexural properties of fiber posts", J Endod, 33, pp.864~867 (2007)
- Xible AA, "Effect of silica coating and silanization on flexural and composite- resin bond strengths of zirconia posts: An in vitro study", J Prosthet Dent, 95, pp.224~229 (2006)
- Grandini S, "Fatigue resistance and structural integrity of different types of fiber posts", Dent Mater J, 27, pp.687~694 (2008)
- Balbosh A, "Effect of surface treatment on retention of glass-fiber endodontic posts", J Prosthet Dent, 95, pp.218~223 (2006)
- Cheleux N, "Sandblasting effect on flexural properties of fiber posts", Euro Cell Mater, 10, pp.3~ (2005)
- Bitter K, "In vitro evaluation of push-out bond strengths of various luting agents to tooth-colored posts", J Prosthet Dent, 95, pp.302~310 (2006)
- Sahafi A, "Resistance to cyclic loading of teeth restored with posts", Clin Oral Investig, 9, pp.84~90 (2005)
- Valandro LF, "Microtensile bond strength between Quartz fiber post and resin cement: Effect of post surface treatment", J Endodont Mater, 4, pp.271~274 (2003)
- Ro¨dig T, "Effects of different luting agents on bond strengths of fiber-reinforced composite posts to root canal dentin", J Adhes Dent, 12, pp.197~205 (2010)
- Sahafi A, "Retention of adhesively bonded posts: effect of pretreatment of the root canal", J Adhes Dent, 11, pp.319~323 (2009)
- Bitter K, "Effects of pretreatment and thermocycling on bond strength of resin core materials to various fiber-reinforced composite posts", J Adhes Dent, 10, pp.481~489 (2008)
- Papacchini F, "The application of hydrogen peroxide in composite repair", J Biomed Mater Res B Appl Biomater, 82, pp.298~304 (2007)
- Comlekoglu ME, "Reversal of reduced bond strength after bleaching", Gen Dent, 58, pp.258~263 (2010)
- Kaya AD, "Reversal of dentin bonding to bleached teeth", Oper Dent, 28, pp.825~829 (2003)
- Nihi FM, "In vitro assessment of solvent evaporation from commercial adhesive systems compared to experimental systems", Braz Dent J, 20, pp.396~402 (2009)
- Allen JF, "Superoxide reduction as a mechanism of ascorbate- stimulated oxygen uptake by isolated chloroplasts", Biochem Biophys Res Commun, 52, pp.856~862 (1973)
- Al-Ayash AI, "The mechanism of reduction of single-site redox proteins by ascorbic acid", Biochem J, 177, pp.641~648 (1979)
- Bielski BH, "Some properties of the ascorbate free radical", Ann N Y Acad Sci, 258, pp.231~237 (1975)
- Cadenaro M, "Effects of residual ethanol on the rate and degree of conversion of five experimental resins", Dent Mater, 25, pp.621~628 (2009)
- Garcia FC, "Influences of surface and solvent on retention of HEMA", mixture components after evaporation, 2010, pp.38, 44~49
- Goracci C, "The adhesion between prefabricated FRC posts and composite resin cores: microtensile bond strength with and without post-silanization", Dent Mater, 21, pp.437~444 (2005)
- Young IS, "Antioxidants in health and disease", J Clin Pathol, 54, pp.176~186 (2001)
- Tu¨rku¨n M, "Effect of 10% sodium ascorbate on the shear bond strength of composite resin to bleached bovine enamel", J Oral Rehabil, 31, pp.1184~1191 (2004)
- Kimyai S, "Comparison of the effect of hydrogel and a solution of sodium ascorbate on dentin-composite bond strength after bleaching", J Contemp Dent Pract, 9, pp.105~112 (2008)
- Tu¨rku¨n M, "Can the hydrogel form of sodium ascorbate be used to reverse compromised bond strength after bleaching?", J Adhes Dent, 11, pp.35~40 (2009)
- Hashimoto M, "Bonding of self-etching adhesives on dehydrated dentin", J Adhes Dent, 13, pp.49~54 (2011)