Effect of universal adhesive pretreatments on the bond strength durability of conventional and adhesive resin cements to zirconia ceramic
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
PURPOSE. This study aimed to evaluate the effect of pretreatment of three different universal adhesives (Single Bond Universal [SBU], All-Bond Universal [ABU], and Prime&Bond universal [PBU]) on the bonding durability of an adhesive (Panavia F 2.0, PF) and a conventional (Duo-Link, DL) resin cements to air-abraded zirconia. MATERIALS AND METHODS. Rectangular-shaped zirconia specimens were prepared. The chemical composition and surface energy parameters of the materials were studied by Fourier transform infrared spectroscopy and contact angle measurement, respectively. To evaluate resin bonding to the zirconia, all the bonding specimens were immersed in water for 24 h and the specimens to be aged were additionally thermocycled 10000 times before the shear bond strength (SBS) test. RESULTS. The materials showed different surface energy parameters, including the degree of hydrophilicity/hydrophobicity. While the DL/CON (no pretreatment) showed the lowest SBS and a significant decrease in the value after thermocycling (P < .001), the PF/CON obtained a higher SBS value than the DL/CON (P < .001) and no decrease even after thermocycling (P = .839). When the universal adhesives were used with DL, their SBS values were higher than the CON (P < .05), but the trend was adhesive-specific. In conjunction with PF, the PF/SBU produced the highest SBS followed by the PF/ABU (P = .002), showing no significant decrease after thermocycling (P > .05). The initial SBS of the PF/PBU was similar to the PF/CON (P = .999), but the value decreased after thermocycling (P < .001). CONCLUSION. The universal adhesive pretreatment did not necessarily show a synergistic effect on the bonding performance of an adhesive resin cement, whereas the pretreatment was beneficial to bond strength and durability of a conventional resin cement.
Abstract
PURPOSE. This study aimed to evaluate the effect of pretreatment of three different universal adhesives (Single Bond Universal [SBU], All-Bond Universal [ABU], and Prime&Bond universal [PBU]) on the bonding durability of an adhesive (Panavia F 2.0, PF) and a conventional (Duo-Link, DL) resin cements to air-abraded zirconia. MATERIALS AND METHODS. Rectangular-shaped zirconia specimens were prepared. The chemical composition and surface energy parameters of the materials were studied by Fourier transform infrared spectroscopy and contact angle measurement, respectively. To evaluate resin bonding to the zirconia, all the bonding specimens were immersed in water for 24 h and the specimens to be aged were additionally thermocycled 10000 times before the shear bond strength (SBS) test. RESULTS. The materials showed different surface energy parameters, including the degree of hydrophilicity/hydrophobicity. While the DL/CON (no pretreatment) showed the lowest SBS and a significant decrease in the value after thermocycling (P < .001), the PF/CON obtained a higher SBS value than the DL/CON (P < .001) and no decrease even after thermocycling (P = .839). When the universal adhesives were used with DL, their SBS values were higher than the CON (P < .05), but the trend was adhesive-specific. In conjunction with PF, the PF/SBU produced the highest SBS followed by the PF/ABU (P = .002), showing no significant decrease after thermocycling (P > .05). The initial SBS of the PF/PBU was similar to the PF/CON (P = .999), but the value decreased after thermocycling (P < .001). CONCLUSION. The universal adhesive pretreatment did not necessarily show a synergistic effect on the bonding performance of an adhesive resin cement, whereas the pretreatment was beneficial to bond strength and durability of a conventional resin cement.
참고문헌 (28)
- Samran A, "Bond strength durability of self-adhesive resin cements to zirconia ceramic : An in vitro study", J Prosthet Dent, 121, pp.477~484 (2019)
- Kim MJ, "Shear bond strengths of various luting cements to zirconia ceramic : surface chemical aspects", J Dent, 39, pp.795~803 (2011)
- Kim JH, "Effects of multipurpose, universal adhesives on resin bonding to zirconia ceramic", Oper Dent, 40, pp.55~62 (2015)
- Go EJ, "Evaluation of the microshear bond strength of MDP-containing and Non-MDP-containing self-adhesive resin cement on zirconia restoration", Oper Dent, 44, pp.379~385 (2019)
- Kern M, "Bonding to zirconia ceramic : adhesion methods and their durability", Dent Mater, 14, pp.64~71 (1998)
- Passos SP, "Adhesive quality of self-adhesive and conventional adhesive resin cement to Y-TZP ceramic before and after aging conditions", Oper Dent, 35, pp.689~696 (2010)
- Nicoloso GF, "Is there a best protocol to optimize bond strength of a universal adhesive to artificially induced caries-affected primary or permanent dentin?", J Adhes Dent, 18, pp.441~446 (2016)
- Antonucci JM, "Novel dental resins from trialkoxysilanes and dental monomers by in situ formation of oligomeric silyl ethers and silsesquioxanes", Polym Prepr, 43, pp.633~634 (2002)
- Marghalani HY, "Sorption and solubility characteristics of self-adhesive resin cements", Dent Mater, 28, pp.e187~e198 (2012)
- Dimitriadi M, "Self-etch silane primer : reactivity and bonding with a lithium disilicate ceramic", Materials, 13, pp.641~ (2020)
- Asmussen E, "Resin composites : strength of the bond to dentin versus surface energy parameters", Dent Mater, 21, pp.1039~1043 (2005)
- Kwon SM, "Challenging the resin-zirconia interface by thermal cycling or mechanical load cycling or their combinations", Appl Sci, 10, pp.7352~ (2020)
- Kern M, "Surface conditioning influences zirconia ceramic bonding", J Dent Res, 88, pp.817~822 (2009)
- Van Oss CJ, "The hydrophilicity and hydrophobicity of clay minerals", Clays Clay Miner, 43, pp.474~477 (1995)
- Yang B, "Influence of air-abrasion on zirconia ceramic bonding using an adhesive composite resin", Dent Mater, 26, pp.44~50 (2010)
- "ISO 29022. Dentistry-Adhesion-Notche-dedge shear bond strength test", International Standards Organization (ISO), ~ (2013)
- Kwon SM, "Durability of resin bond strength to dental noble metal-ceramic alloys conditioned with novel mercapto silane-based primer systems", J Adhes Sci Technol, 30, pp.506~519 (2016)
- Siboni S, "Acid-base theory of adhesion : A critical review", Rev Adhes Adhes, 3, pp.253~310 (2015)
- Lee LH, "Adhesion and surface-hydrogen-bond components for polymers and biomaterials", J Adhes, 67, pp.1~18 (1998)
- Kim YK, "Influence of surface energy parameters of dental self-adhesive resin cements on bond strength to dentin", J Adhes Sci Technol, 27, pp.1778~1789 (2013)
- Beatty MW, "Effect of crosslinking agent content, monomer functionality, and repeat unit chemistry on properties of unfilled resins", J Biomed Mater Res, 27, pp.403~413 (1993)
- Gale MS, "Thermal cycling procedures for laboratory testing of dental restorations", J Dent, 27, pp.89~99 (1999)
- Zhang F, "Lifetime estimation of zirconia ceramics by linear ageing kinetics", Acta Mater, 92, pp.290~298 (2015)
- Lüthy H, "Effect of thermocycling on bond strength of luting cements to zirconia ceramic", Dent Mater, 22, pp.195~200 (2006)
- Ito S, "Effects of resin hydrophilicity on water sorption and changes in modulus of elasticity", Biomaterials, 26, pp.6449~6459 (2005)
- Kerby RE, "Synthesis and evaluation of modified urethane dimethacrylate resins with reduced water sorption and solubility", Dent Mater, 25, pp.302~313 (2009)
- Wolfart M, "Durability of the resin bond strength to zirconia ceramic after using different surface conditioning methods", Dent Mater, 23, pp.45~50 (2007)
- Salem RST, "In vitro evaluation of shear bond strength of three primer", resin cement systems to monolithic zirconia, 2019, pp.32, 519~525