The effects of cement thickness and cement shade on the final color of lithium disilicate crowns
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Purpose. The aim of this study is to evaluate the effect of resin cement color, cement thickness, and thermocycling on the final color of monolithic lithium disilicate crowns. Materials and methods. A total of ninety prepared central incisors of typodont teeth were restored with lithium disilicate crowns which have different cement thicknesses (40 µm, 80 µm, and 120 µm) and cement shades (clear, yellow, and white). Color parameters of restorations were measured with a spectrophotometer in three different steps 1) before cementing 2) after cementing and 3) after thermocycling with 10000 cycles. Color differences (∆E00) were calculated with the CIEDE2000 formula and evaluated according to perceptibility (0.8) and acceptability (1.8) thresholds. The ∆E00 data were analyzed by using two-way ANOVA before and after thermocycling (α = .05). Results. There was no interaction between the cement shade and the cement thickness factors. After cementation, the mean ∆E00 was under the perceptibility threshold in the group of 40 µm cement thickness and clear cement while it was between the perceptibility and acceptability thresholds (0.8 < ∆E00 < 1.8) for all other groups. After thermocycling, the ∆E00 values were between the perceptibility and acceptability thresholds for all experimental groups. Although there were no significant differences among the groups, thermocycling increased the color difference values. Conclusion. The cementation of restorations with clear, yellow, and white resin cements resulted in color differences with uncemented restorations except for the group cemented with clear cement in 40 µm cement thickness. All study groups revealed perceptible color change after thermocycling. [J Adv Prosthodont 2023;15:93-100]
Abstract
Purpose. The aim of this study is to evaluate the effect of resin cement color, cement thickness, and thermocycling on the final color of monolithic lithium disilicate crowns. Materials and methods. A total of ninety prepared central incisors of typodont teeth were restored with lithium disilicate crowns which have different cement thicknesses (40 µm, 80 µm, and 120 µm) and cement shades (clear, yellow, and white). Color parameters of restorations were measured with a spectrophotometer in three different steps 1) before cementing 2) after cementing and 3) after thermocycling with 10000 cycles. Color differences (∆E00) were calculated with the CIEDE2000 formula and evaluated according to perceptibility (0.8) and acceptability (1.8) thresholds. The ∆E00 data were analyzed by using two-way ANOVA before and after thermocycling (α = .05). Results. There was no interaction between the cement shade and the cement thickness factors. After cementation, the mean ∆E00 was under the perceptibility threshold in the group of 40 µm cement thickness and clear cement while it was between the perceptibility and acceptability thresholds (0.8 < ∆E00 < 1.8) for all other groups. After thermocycling, the ∆E00 values were between the perceptibility and acceptability thresholds for all experimental groups. Although there were no significant differences among the groups, thermocycling increased the color difference values. Conclusion. The cementation of restorations with clear, yellow, and white resin cements resulted in color differences with uncemented restorations except for the group cemented with clear cement in 40 µm cement thickness. All study groups revealed perceptible color change after thermocycling. [J Adv Prosthodont 2023;15:93-100]
참고문헌 (33)
- Willard A, "The science and application of IPS e.Max dental ceramic", Kaohsiung J Med Sci, 34, pp.238~242 (2018)
- Phark JH, "Microstructural considerations for novel lithium disilicate glass ceramics : A review", J Esthet Restor Dent, 34, pp.92~103 (2022)
- Zarone F, "Current status on lithium disilicate and zirconia : a narrative review", BMC Oral Health, 19, pp.134~ (2019)
- Ziyad TA, "Optical properties of CAD-CAM monolithic systems compared : three multi-layered zirconia and one lithium disilicate system", Heliyon, 7, pp.e08151~ (2021)
- CIE Technical Report: Colorimetry, "Commission Internationale de lEclairage", CIE Central Bureau, ~, pp.CIE Pub No. 15. 3 (2004)
- Alp G, "Effect of surface treatments and coffee thermocycling on the color and translucency of CAD-CAM monolithic glass-ceramic", J Prosthet Dent, 120, pp.263~268 (2018)
- "ISO", TR 28642. Dentistry-Guidance on colour measurement, 2016, pp.1~10
- Seyidaliyeva A, "Color stability of polymer-infiltrated-ceramics compared with lithium disilicate ceramics and composite", J Esthet Restor Dent, 32, pp.43~50 (2020)
- Theocharidou A, "Effect of in vitro aging and acidic storage on color, translucency, and contrast ratio of monolithic zirconia and lithium disilicate ceramics", J Prosthet Dent, 127, pp.479~488 (2022)
- Alencar-Silva FJ, "Effect of beverage solutions and toothbrushing on the surface roughness, microhardness, and color stainability of a vitreous CAD-CAM lithium disilicate ceramic", J Prosthet Dent, 121, pp.711.e1~6 (2019)
- Palla ES, "Color stability of lithium disilicate ceramics after aging and immersion in common beverages", J Prosthet Dent, 119, pp.632~642 (2018)
- Ashy LM, "The effect of thermocyclic aging on color stability of high translucency monolithic lithium disilicate and zirconia ceramics luted with different resin cements : an in vitro study", BMC Oral Health, 21, pp.587~ (2021)
- Yildirim B, "Effect of cement color and tooth-shaded background on the final color of lithium disilicate and zirconia-reinforced lithium silicate ceramics : An in vitro study", J Esthet Restor Dent, 33, pp.380~386 (2021)
- Paravina RD, "Color difference thresholds in dentistry", J Esthet Restor Dent, 27, pp.S1~9 (2015)
- Paravina RD, "Acceptability and perceptibility thresholds in dentistry : A comprehensive review of clinical and research applications", J Esthet Restor Dent, 31, pp.103~112 (2019)
- Chaiyabutr Y, "Effect of abutment tooth color, cement color, and ceramic thickness on the resulting optical color of a CAD", CAM glass-ceramic lithium disilicate-reinforced crown, 2011, pp.105, 83~90
- Volpato CA, "Optical influence of the type of illuminant, substrates and thickness of ceramic materials", Dent Mater, 25, pp.87~93 (2009)
- Vichi A, "Influence of ceramic and cement thickness on the masking of various types of opaque posts", J Prosthet Dent, 83, pp.412~417 (2000)
- Tafur-Zelada CM, "The influence of zirconia veneer thickness on the degree of conversion of resin-matrix cements : an integrative review", Clin Oral Investig, 25, pp.3395~3408 (2021)
- Bayindir F, "The effect of restoration thickness and resin cement shade on the color and translucency of a high-translucency monolithic zirconia", J Prosthet Dent, 123, pp.149~154 (2020)
- Liebermann A, "Impact of resin composite cement on color of computer-aided design", computer-aided manufacturing ceramics, 2021, pp.33, 786~794
- Dede DÖ, "Effect of brand and shade of resin cements on the final color of lithium disilicate ceramic", J Prosthet Dent, 117, pp.539~544 (2017)
- Comba A, "Effects of substrate and cement shade on the translucency and color of CAD", CAM lithium-disilicate and zirconia ceramic materials, 2022, pp.14, 1778~
- Rodrigues RB, "Influence of resin cements on color stability of different ceramic systems", Braz Dent J, 28, pp.191~195 (2017)
- Hernandes DK, "Influence of resin cement shade on the color and translucency of ceramic veneers", J Appl Oral Sci, 24, pp.391~396 (2016)
- Vafaee F, "Effect of resin cement color on the final color of lithium disilicate all-ceramic restorations", J Dent(Tehran), 15, pp.143~150 (2018)
- Chang J, "The optical effect of composite luting cement on all ceramic crowns", J Dent, 37, pp.937~943 (2009)
- Niu E, "Color match of machinable lithium disilicate ceramics : Effects of cement color and thickness", J Prosthet Dent, 111, pp.42~50 (2014)
- Gale MS, "Thermal cycling procedures for laboratory testing of dental restorations", J Dent, 27, pp.89~99 (1999)
- Yuan JC, "Effect of brushing and thermocycling on the shade and surface roughness of CAD-CAM ceramic restorations", J Prosthet Dent, 119, pp.1000~1006 (2018)
- Aldosari LI, "Surface roughness and color measurements of glazed or polished hybrid, feldspathic, and Zirconia CAD", CAM restorative materials after hot and cold coffee immersion, 2021, pp.21, 422~
- Haralur SB, "Effect of hydrothermal aging and beverages on color stability of lithium disilicate and zirconia based ceramics", Medicina(Kaunas), 55, pp.749~ (2019)
- Dos Santos DM, "Effect of different acidic solutions on the optical behavior of lithium disilicate ceramics", J Prosthet Dent, 118, pp.430~436 (2017)