바우싱거 효과가 자긴가공된 압력용기의 피로균열전파수명에 미치는 영향
Bauschinger Effects on the Fatigue Crack Propagation Life of an Autofrettaged Thick-walled Pressure Vessel
0
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Thick-walled pressure vessel has been autofrettaged in order to improve the fatigue life of the pressure vessel. The compressive tangential residual stress near the bore of the pressure vessel due the autofrettage process is benefical to the fatigue crack initiation and propagation of the pressure vessel. However, a reverse yielding due to the Bauschinger effect during the unloading process in autofrettage causes the reduction of the compressive residual stress near the bore. In order to evaluate the fatigue crack propagation life of the autofrettaged thick-walled pressure vessel, the Bauschinger effects were considered. Stress intensity factors of the crack at the inside surface of the pressure vessel due to operating pressure loading of 707 MPa and autofrettage loading with different levels of overstrain were calculated by using finite element methods, and used for evaluating fatigue crack propagation lives. Fatigue lives of the pressure vessel with the Bauschinger effects resulted in 45% to 67% reductions in fatigue life compared to those of the pressure vessel with ideal residual stress distributions depending on the autofrettage level.
Abstract
Thick-walled pressure vessel has been autofrettaged in order to improve the fatigue life of the pressure vessel. The compressive tangential residual stress near the bore of the pressure vessel due the autofrettage process is benefical to the fatigue crack initiation and propagation of the pressure vessel. However, a reverse yielding due to the Bauschinger effect during the unloading process in autofrettage causes the reduction of the compressive residual stress near the bore. In order to evaluate the fatigue crack propagation life of the autofrettaged thick-walled pressure vessel, the Bauschinger effects were considered. Stress intensity factors of the crack at the inside surface of the pressure vessel due to operating pressure loading of 707 MPa and autofrettage loading with different levels of overstrain were calculated by using finite element methods, and used for evaluating fatigue crack propagation lives. Fatigue lives of the pressure vessel with the Bauschinger effects resulted in 45% to 67% reductions in fatigue life compared to those of the pressure vessel with ideal residual stress distributions depending on the autofrettage level.
참고문헌 (10)
- Harvey, J. F., "Theory and Design of Pressure Vessels" (1991), Van Nostrand Reinhold
- Underwood, J. H., "Fatigue Life Analyses and Tests for Thick-Wall Cylinders Including Effects of Overstrain and Axial Grooves", J. Pressure Vessel Technology, 117, pp.222~226 (1995)
- Hill, R., "Mathematical Theory of Plasticity" (1950), Oxford University Press
- Milligan, R. V., "The Bauschinger Effect in a High-Strength Steel", J. Basic Engineering, American Society of Mechanical Engineers, pp.480~488 (1966)
- Parker, A. P., "Fatigue and Fracture Mechanics: 29th Volume, ASTM STP 1332", pp.565~583 (1996), American Society for Testing and Materials
- Chen, P. C. T., "The Bauschinger and Hardening Effect on Residual Stresses in an Autofrettaged Thick-walled Cylinder", J. Pressure Vessel Technology, 108, pp.108~112 (1986)
- Koh, S. K., "Fatigue Crack Growth Life of Thick-walled Cylinder with an External Radial Crack", Int. J. Fatigue, 21(2), pp.135~146 (1999)
- Kendall, D. P., "The Influence of the Bauschinger Effect on Re-yielding of Autofrettaged Thick-walled Cylinders", ASME PVP, 125, pp.17~21 (1987)
- 고승기, "바우싱거 효과가 자긴가공된 압력용기의 잔류응력 분포에 미치는 영향", 한국기계기술학회지, 23(4), pp.544~550 (2021), 한국기계기술학회[DOI]
- Kendall, D. P., "Simple Fracture Mechanics-Based Method for Fatigue Life Prediction in Thick-Walled Cylinders", J. Pressure Vessel Technology, 108, pp.490~494 (1986)