백색광 소자 응용을 위한 Gd2WO6:RE3+ (RE = Dy, Sm, Dy/Sm) 형광체의 구조 및 발광 특성
Structural and Luminescent Properties of Gd2WO6:RE3+ (RE = Dy, Sm, Dy/Sm) Phosphors for White Light Emitting Devices
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
A series of Dy3+, Sm3+, and Dy3+/Sm3+ doped Gd2WO6 phosphors were synthesized by the conventional solid-state reaction. The X-ray diffraction patterns revealed that all of the diffraction peaks could be attributed to the monoclinic Gd2WO6 crystal structure, irrespective of the type and the concentration of activator ions. The photoluminescence (PL) excitation spectra of Dy3+-doped Gd2WO6 phosphors contained an intense charge transfer band centered at 302 nm in the range of 240–340 nm and two weak peaks at 351 and 386 nm. Under an excitation wavelength of 302 nm, the PL emission spectra consisted of two strong blue and yellow bands centered at 482 nm and 577 nm. The PL emission spectra of the Sm3+-doped Gd2WO6 phosphors had a series of three peaks centered at 568 nm, 613 nm, and 649 nm, corresponding to the 6G5/2→6H5/2, 6G5/2→6H9/2, and 6G5/2→6H11/2 transitions of Sm3+, respectively. The PL emission spectra of the Dy3+- and Sm3+-codoped Gd2WO6 phosphors showed the blue and yellow emission lines originating from the 4F9/2→6H15/2 and 4F9/2→6H13/2 transitions of Dy3+ and reddish-orange and red emission bands due to the 4G5/2→6H7/2 and 4G5/2→6H9/2 transitions of Sm3+. As the concentration of Sm3+ increased from 1 to 15 mol%, the intensities of two PL spectra emitted by the Dy3+ ions gradually decreased, while those of the three emission bands due to the Sm3+ ions slowly increased, thus producing the color change from white to orange. The CIE color coordinates of Gd2WO6:5 mol% Dy3+, 1 mol% Sm3+ phosphors were (0.406, 0.407), which was located in the warm white light region.
Abstract
A series of Dy3+, Sm3+, and Dy3+/Sm3+ doped Gd2WO6 phosphors were synthesized by the conventional solid-state reaction. The X-ray diffraction patterns revealed that all of the diffraction peaks could be attributed to the monoclinic Gd2WO6 crystal structure, irrespective of the type and the concentration of activator ions. The photoluminescence (PL) excitation spectra of Dy3+-doped Gd2WO6 phosphors contained an intense charge transfer band centered at 302 nm in the range of 240–340 nm and two weak peaks at 351 and 386 nm. Under an excitation wavelength of 302 nm, the PL emission spectra consisted of two strong blue and yellow bands centered at 482 nm and 577 nm. The PL emission spectra of the Sm3+-doped Gd2WO6 phosphors had a series of three peaks centered at 568 nm, 613 nm, and 649 nm, corresponding to the 6G5/2→6H5/2, 6G5/2→6H9/2, and 6G5/2→6H11/2 transitions of Sm3+, respectively. The PL emission spectra of the Dy3+- and Sm3+-codoped Gd2WO6 phosphors showed the blue and yellow emission lines originating from the 4F9/2→6H15/2 and 4F9/2→6H13/2 transitions of Dy3+ and reddish-orange and red emission bands due to the 4G5/2→6H7/2 and 4G5/2→6H9/2 transitions of Sm3+. As the concentration of Sm3+ increased from 1 to 15 mol%, the intensities of two PL spectra emitted by the Dy3+ ions gradually decreased, while those of the three emission bands due to the Sm3+ ions slowly increased, thus producing the color change from white to orange. The CIE color coordinates of Gd2WO6:5 mol% Dy3+, 1 mol% Sm3+ phosphors were (0.406, 0.407), which was located in the warm white light region.
참고문헌 (16)
- X. Wu, "Structure, Luminescence Properties and Energy Transfer of Dy3+ and Eu3+ Codoped KBa(VO4) Phosphor", J. Solid State Chem., 265, pp.109~116 (2018)
- F. Xiao, "Color Tunable Emission and Energy Transfer of Ce3+", Dy3+ Codoped Ba3La2(BO3)4 Phosphor for UV White LEDs, 2018, pp.202, 352~358
- X. Wu, "Structure, Luminescence, Properties and Energy Transfer of Dy3+ and Eu3+ codoped Ca4LaO(BO3)3 Phosphor", J. Alloys Compd., 822, pp.153562~ (2020)
- G. Jyothi, "White Emitting Dy3+ Activated Perovskite Titanates and Energy Transfer by Eu3+Codoping", Ceram. Int, 43, pp.12044~12056 (2007)
- X. Y. Sun, "Investigation on Luminescence Properties of Dy3+-, Eu3+-doped, and Eu3+", Dy3+-codoped SrGd2O4 Phosphors, 2018, pp.204, 89~94
- Z. Li, "Luminescence and Energy Transfer of a Novel Tunable-emitting Phosphor Sr0.8Ca0.2Al2Si2O8:Eu", Tb for White LEDs, 2019, pp.191, 60~67
- X. Sun, "Tb3+→Sm3+ Energy Transfer Induced Tunable Luminescence in Ba3MgSi2O8 : Tb3+", Sm3+ Phosphors, 2020, pp.219, 116925~
- B. Devakumar, "A Single-phased Warm-White-Emitting K3Y(PO4)2:Dy3+, Sm3+ Phosphor with Tuneable Photoluminescence for Near-UV-excited White LEDs", Dyes Pigm., 157, pp.72~79 (2018)
- Timur Sh. Atabaev, "Synthesis and Optical Properties of Dy3+-doped Y2O3 Nanoparticles", Journal of the Korean Physical Society, 60(2), pp.244~248 (2012), 한국물리학회
- S. Liu, "Photoluminescence Properties of Novel White Phosphor Dy3+-doped LaBSiO5Glass", Mater. Sci. Semicond. Process, 38, pp.266~248 (2015)
- 최경재, "자회선 여기용 청색 및 황색 형광체의 발광특성", 한국세라믹학회지, 43(5), pp.7~7 (2006), 한국세라믹학회
- Y. Jin, "Luminescence Properties of a Novel Orange Emission Long Persistent Phosphor CaO : Sm3+", Opt. Commun, 311, pp.266~269 (2013)
- Z. W. Zhang, "Synthesis and Luminescence Properties of Novel LiSr4(BO3)3 : Dy3+ Phosphors", Ceram. Int, 39, pp.1723~1728 (2013)
- P. Babu, "White Light Generation in Dy3+-doped Oxyfluoride Glass and Transparent Glass-Ceramics Containing CaF2Nanocrystals", Opt. Express, 19, pp.1836~1841 (2011)
- T. P. Tang, "The Photoluminescence of SrAl2O4 : Sm3+ Phosphor", Ceram. Int, 32, pp.665~671 (2006)
- H. Zhang, "Uniform Hollow TiO2 : Sm3+ Spheres : Solvothermal Synthesis and Luminescence Properties", Powder Technol, 239, pp.403~408 (2013)