BaWO4:Dy3+,Eu3+ 백색광 형광체의 발광 특성과 에너지 전달 효율
Luminescent Properties and Energy Transfer Efficiency of BaWO4:Dy3+, Eu3+ White Light-Emitting Phosphors
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Dy3+- and Eu3+-codoped BaWO4 phosphors for white light-emitting diode were synthesized with different activator ions via a solid-state reaction process. The structural, morphological, and optical properties of the BaWO4:Dy3+,Eu3+ phosphors were investigated as a function of Eu3+ concentration at a fixed concentration of Dy3+ ions. XRD patterns exhibited that all the synthesized phosphors had a tetragonal system, irrespective of the concentrations of Dy3+ and Eu3+ ions. The excitation spectra of the synthesized phosphors were composed of three intense bands centered at 251, 355, and 393 nm and several weak peaks. For the BaWO4:Dy3+,Eu3+ phosphors synthesized with 1 mol% of Eu3+, the emission spectra under ultraviolet excitation at 393 nm showed two strong blue and yellow bands at 485 and 577 nm corresponding to the 4F9/26H15/2 and 4F9/26H13/2 transitions of Dy3+ ions, respectively and several weak bands in the range of 600–700 nm resulting from the 4f transitions of Eu3+ ions. As the concentration of Eu3+ ions increased, intensities of the blue and yellow emission bands gradually decreased while those of the red emissions increased rapidly and the energy transfer efficiency from Dy3+ to Eu3+ ions was 95.3% at 20 mol% of Eu3+. The optimum white light emission with x=0.363, y=0.357 CIE 1931 chromaticity coordinates was obtained for the sample doped with 5 mol% Dy3+ and 1 mol% of Eu3+.
Abstract
Dy3+- and Eu3+-codoped BaWO4 phosphors for white light-emitting diode were synthesized with different activator ions via a solid-state reaction process. The structural, morphological, and optical properties of the BaWO4:Dy3+,Eu3+ phosphors were investigated as a function of Eu3+ concentration at a fixed concentration of Dy3+ ions. XRD patterns exhibited that all the synthesized phosphors had a tetragonal system, irrespective of the concentrations of Dy3+ and Eu3+ ions. The excitation spectra of the synthesized phosphors were composed of three intense bands centered at 251, 355, and 393 nm and several weak peaks. For the BaWO4:Dy3+,Eu3+ phosphors synthesized with 1 mol% of Eu3+, the emission spectra under ultraviolet excitation at 393 nm showed two strong blue and yellow bands at 485 and 577 nm corresponding to the 4F9/26H15/2 and 4F9/26H13/2 transitions of Dy3+ ions, respectively and several weak bands in the range of 600–700 nm resulting from the 4f transitions of Eu3+ ions. As the concentration of Eu3+ ions increased, intensities of the blue and yellow emission bands gradually decreased while those of the red emissions increased rapidly and the energy transfer efficiency from Dy3+ to Eu3+ ions was 95.3% at 20 mol% of Eu3+. The optimum white light emission with x=0.363, y=0.357 CIE 1931 chromaticity coordinates was obtained for the sample doped with 5 mol% Dy3+ and 1 mol% of Eu3+.
참고문헌 (19)
- P. Fu, "Perovskite Nanocrystals:Synthesis, Properties and Applications", Sci. Bull., 62, pp.369~380 (2017)
- 류한열, "Analysis on the Luminous Efficiency of Phosphor-Conversion White Light-Emitting Diode", Current Optics and Photonics, 17(1), pp.22~26 (2013), 한국광학회
- Y. C. Li, "Synthesis and Luminescent Properties of Ln3+(Eu3+, Sm3+, Dy3+)-doped Lanthanum Aluminum Germanate LaAlGe2O7 Phosphors", J. Alloy. Compd, 439, pp.367~375 (2007)
- T. W. Kuo, "High Color Rendering White Light-Emitting-Diode Illuminator Using the Red-Emitting Eu2+-Activated CaZnOS Phosphors Excited by Blue LED", Opt. Express, 18(8), pp.8187~8192 (2010)
- A. A. Setlur, "Phosphors for LED-based Solid-State Lighting", Electrochem. Soc. Interface, (Winter), pp.32~36 (2009)
- H. Wu, "Research of Color Rendering of White LED Based on Red and Green Phosphors", Acta. Optica. Sinica, 28(9), pp.1777~1781 (2008)
- C. C. Lin, "KBaPO4:Ln (Ln=Eu, Tb, Sm) Phosphors for UV Excitable White Light-Emitting Diodes", J. Lumin, 129, pp.1682~1684 (2009)
- R. Grasser, "Defect Luminescence in Tungstate", J. Lumin, 40, pp.41 (1988), 343~344
- M. Nazarov, "Rare Earth Double Activated Phosphors for Different Applications", J. Rare Earth, 28, pp.1~11 (2010)
- Z. Yang, "Synthesis and Luminescence Properties of a Novel Red Sr3Bi(PO4)3 : Sm3+ Phosphor", J. Rare Earth, 30(12), pp.1199~1202 (2012)
- S. Shi, "Effects of Charge Compensation on the Luminescence Behavior of Eu3+ Activated CaWO4Phosphor", Opt. Mater, 30, pp.1616~1620 (2008)
- N. Niu, "Solvothermal Synthesis of SrMoO4:Ln (Ln=Eu3+, Tb3+, Dy3+)Nanoparticles and Its Photoluminescence Properties at Room Temperature", Mater. Res. Bull, 46, pp.333~339 (2011)
- 조형철, "CaNb2O6:RE3+ (RE = Dy, Eu, Dy", Eu) 형광체의 발광 특성, 2017, pp.27(6), 339~344[DOI]
- A. Pandey, "Pr3+-Yb3+ Codoped Y2O3 Phosphor for Display Devices", Mater. Res. Bull, 57(9), pp.156~161 (2014)
- Y. Zhang, "A New Single-phase White-Light-Emitting CaWO4:Dy3+Phosphor: Synthesis, Luminescence and Energy Transfer", RSC Adv, 5, pp.62527~62533 (2015)
- A. K. Bedyal, "A Near-UV-Converted LiMgBO3 : Dy3+Nanoparticle : Surface and Spectral Investigations", Appl. Surf. Sci, 329, pp.40~46 (2015)
- Y. Zhai, "A Novel White-Emitting Phosphor ZnWO4 : Dy3+", J. Rare Earth, 33(4), pp.350~354 (2015)
- M. Shi, "Dy3+:Ca2SnO4, a New Yellow Phosphor with Afterglow Behavior", J. Alloy. Compd, 639, pp.168~172 (2015)
- B. Devakumar, "A Single-Phased W a r m - W h i t e - E m i t t i n g K3Y(PO4)2:Dy3+,Sm3+ Phosphor with Tuneable Photoluminescence for Near-UV-Excited White LEDs", Dyes Pigm, 157, pp.72~79 (2018)