The aim of this study was to measure the shear bond strength (SBS) of different adhesive systems to calcium silicatebased materials (Biodentine and RetroMTA). Eighty cylindrical acrylic blocks, with a hole (5.0 mm diameter, 2.0 mm height) in each, were prepared. The holes were filled with Biodentine (BD) and RetroMTA (RMTA), and the specimens were divided into 2 groups. Each group was classified into 4 subgroups: ClearfilTM SE (CSE) ; AQ bond (AQ) ; All bond universal Self-etch (ABU-SE) ; and All bond universal Total-etch (ABU-TE). After the application of different adhesive systems, composite resin (Z350) was applied over BD and RMTA. The SBS was measured using a universal testing machine, and the data were compared using the Kruskal-Wallis test and the Mann-Whitney test. The highest and lowest values of SBS were observed for BD-ABU-SE and RMTA-AQ, respectively. No significant differences were found in the SBS between ABU-TE and ABU-SE and between ABU-TE and CSE to BD and RMTA. According to the data, BD showed a higher SBS than did RMTA when BD and RMTA are compared in the same adhesive agents. Further, among all groups, composite resin with ABU-SE showed better bond strength to BD and RMTA.
Abstract
The aim of this study was to measure the shear bond strength (SBS) of different adhesive systems to calcium silicatebased materials (Biodentine and RetroMTA). Eighty cylindrical acrylic blocks, with a hole (5.0 mm diameter, 2.0 mm height) in each, were prepared. The holes were filled with Biodentine (BD) and RetroMTA (RMTA), and the specimens were divided into 2 groups. Each group was classified into 4 subgroups: ClearfilTM SE (CSE) ; AQ bond (AQ) ; All bond universal Self-etch (ABU-SE) ; and All bond universal Total-etch (ABU-TE). After the application of different adhesive systems, composite resin (Z350) was applied over BD and RMTA. The SBS was measured using a universal testing machine, and the data were compared using the Kruskal-Wallis test and the Mann-Whitney test. The highest and lowest values of SBS were observed for BD-ABU-SE and RMTA-AQ, respectively. No significant differences were found in the SBS between ABU-TE and ABU-SE and between ABU-TE and CSE to BD and RMTA. According to the data, BD showed a higher SBS than did RMTA when BD and RMTA are compared in the same adhesive agents. Further, among all groups, composite resin with ABU-SE showed better bond strength to BD and RMTA.
참고문헌 (29)
- Gulati S, "Comparison of shear bond strength of resin-modified glass ionomer to conditioned and unconditioned mineral trioxide aggregate surface: An in vitro study", J Conserv Dent, 17, pp.440~443 (2014)
- Cantekin K, "Bond strength of different restorative materials to light-curable mineral trioxide aggregate", J Clin Pediatr Dent, 39, pp.143~148 (2015)
- Torabinejad M, "Clinical applications of mineral trioxide aggregate", J Endod, 25, pp.197~205 (1999)
- Antunes Bortoluzzi E, "The use of a setting accelerator and its effect on pH and calcium ion release of mineral trioxide aggregate and white Portland cement", J Endod, 32, pp.1194~1197 (2006)
- Boutsioukis C, "Ex vivo study of the efficiency of two techniques for the removal of mineral trioxide aggregate used as a root canal filling material", J Endod, 34, pp.1239~1242 (2008)
- About I, "Biodentine: from biochemical and bioactive properties to clinical applications", G Ital Endod, 30, pp.81~88 (2016)
- Nowicka A, "Response of human dental pulp capped with biodentine and mineral trioxide aggregate", J Endod, 39, pp.743~747 (2013)
- Cantekin K, "Evaluation of shear bond strength of two resin-based composites and glass ionomer cement to pure tricalcium silicate-based cement (Biodentine®)", J Appl Oral Sci, 22, pp.302~306 (2014)
- Kang CM, "A randomized controlled trial of various MTA materials for partial pulpotomy in permanent teeth", J Dent, 60, pp.8~13 (2017)
- Van Meerbeek B, "Buonocore memorial lecture. Adhesion to enamel and dentin:current status and future challenges", Oper Dent, 28, pp.215~235 (2003)
- 김용일, "다양한 세대별 치과용 상아질 접착제의 미세누출과 미세인장접착강도 평가", 대한치과재료학회지, 39(2), pp.119~128 (2012), 대한치과재료학회
- Subramaniam P, "Mineral trioxide aggregate as pulp capping agent for primary teeth pulpotomy : 2 year follow up study", J Clin Pediatr Dent, 33, pp.311~314 (2009)
- Altunsoy M, "Shear bond strength of a self-adhering flowable composite and a flowable base composite to mineral trioxide aggregate, calcium-enriched mixture cement, and Biodentine", J Endod, 41, pp.1691~1695 (2015)
- Atabek D, "Bond strength of adhesive systems to mineral trioxide aggregate with different time intervals", J Endod, 38, pp.1288~1292 (2012)
- Tunç ES, "The evaluation of bond strength of a composite and a compomer to white mineral trioxide aggregate with two different bonding systems", J Endod, 34, pp.603~605 (2008)
- Davidson CL, "The competition between the composite-dentin bond strength and the polymerization contraction stress", J Dent Res, 63, pp.1396~1399 (1984)
- Deepa VL, "Shear bond strength evaluation of resin composite bonded to three different liners : TheraCal LC, Biodentine, and resin-modified glass ionomer cement using universal adhesive: An in vitro study", J Conserv Dent, 19, pp.166~170 (2016)
- Ha WN, "D90: the strongest contributor to setting time in mineral trioxide aggregate and Portland cement", J Endod, 41, pp.1146~1150 (2015)
- Karadas M, "Evaluation of the bond strength of different adhesive agents to a resinmodified calcium silicate material (TheraCal LC)", Scanning, 38, pp.403~411 (2016)
- Shin JH, "Effect of mineral trioxide aggregate surface treatments on morphology and bond strength to composite resin", J Endod, 40, pp.1210~1216 (2014)
- Yoshida Y, "Comparative study on adhesive performance of functional monomers", J Dent Res, 83, pp.454~458 (2004)
- Gandolfi MG, "Development of the foremost light-curable calcium-silicate MTA cement as root-end in oral surgery. Chemical–physical properties, bioactivity and biological behavior", Dent Mater, 27, pp.134~157 (2011)
- Jang JH, "Comparative study of the dentin bond strength of a new universal adhesive", Dent Mater J, 35, pp.606~612 (2016)
- Bayrak S, "Shear bond strengths of different adhesive systems to white mineral trioxide aggregate", Dent Mater J, 28, pp.62~67 (2009)
- Kayahan MB, "Effect of acid-etching procedure on selected physical properties of mineral trioxide aggregate", Int Endod J, 42, pp.1004~1014 (2009)
- Hashem DF, "The physical characteristics of resin composite–calcium silicate interface as part of a layered", laminate adhesive restoration, 2014, pp.30, 343~349
- Hanabusa M, "Bonding effectiveness of a new ‘multi-mode’ adhesive to enamel and dentine", J Dent, 40, pp.475~484 (2012)
- Marchesi G, "Adhesive performance of a multi-mode adhesive system: 1-year in vitro study", J Dent, 42, pp.603~612 (2014)
- Ajami AA, "Comparison of shear bond strength of resin-modified glass ionomer and composite resin to three pulp capping agents", J Dent Res Dent Clin Dent Prospects, 7, pp.164~168 (2013)