Preparation and characterization of rutile TiO₂films
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Rutile titanium dioxide (TiO2) films were prepared by calcination for 4 h at temperatures in the range 550-700oC. Their structure and crystalline nature were investigated by X-ray diffraction (XRD), selected area electron diffraction (SAED) and Raman spectroscopy. After film preparation at 700oC, rutile TiO2 with a tetragonal structure was detected. Raman spectra displayed centered bands at 235, 440 and 603 cm−1, corresponding to the rutile structure of TiO2. The intensity of rutile TiO2increased with an increase in the calcination temperatures. The Raman spectra agree very well with SAED patterns. In addition, the characterization of rutile films with (scanning electron microscopy) SEM and atomic force microscopy (AFM)showed a surface roughness and dense particles with an angular shape.
Abstract
Rutile titanium dioxide (TiO2) films were prepared by calcination for 4 h at temperatures in the range 550-700oC. Their structure and crystalline nature were investigated by X-ray diffraction (XRD), selected area electron diffraction (SAED) and Raman spectroscopy. After film preparation at 700oC, rutile TiO2 with a tetragonal structure was detected. Raman spectra displayed centered bands at 235, 440 and 603 cm−1, corresponding to the rutile structure of TiO2. The intensity of rutile TiO2increased with an increase in the calcination temperatures. The Raman spectra agree very well with SAED patterns. In addition, the characterization of rutile films with (scanning electron microscopy) SEM and atomic force microscopy (AFM)showed a surface roughness and dense particles with an angular shape.
참고문헌 (10)
- C. H. Ao, , Chem. Eng. Sci, 60, pp.103~109 (2005)
- L. Zhang, , Sep. Purif Tehnol, 31, pp.105~110 (2003)
- E. Gyorgy, , Appl. Surf. Sci, 247, pp.429~433 (2005)
- K. M. Lee, , Sol. Energ. Mat. Sol. C, 92, pp.1628~1633 (2008)
- R. Mechiakh, , C. R. Physique, 7, pp.464~470 (2006)
- B. C. Kang, , Surf. Coat. Technol, 131, pp.88~92 (2000)
- T. Miyata, , Thin Solid Films, 496, pp.136~140 (2006)
- K. Eufinger, , Appl. Surf. Sci, 254, pp.148~152 (2007)
- Powder Diffract, "File, JCPDS Internat", JCPDS Internat. Centre for Diffract. Data, PA 19073-3273, U.S.A, ~ (2001)
- S. J. Rigby, , Appl. Surf. Sci, 252, pp.7948~7952 (2006)