Electrical properties of semiconducting YBa2Cu3O7-x thin film with variation of oxygen partial pressure
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
YBa2Cu3O7-x (YBCO) is the material of choice for second-generation superconducting wires and is the only current option for critical current density (Jc)> 1 MA/cm2 at 77 K [1]. YBCO belongs to a class of copper oxides well known for their superconducting properties. Its conduction properties can be changed from metallic (0.5 < x < 1) to insulating (0x0.5) by suitably decreasing the oxygen content [2]. The structural, electrical and optical properties of YBa2Cu3O7-x can be varied by adjusting the oxygen content x [3, 4]. As x is decreased to 0.5, the crystal undergoes a phase transition to a tetragonal structure and it exhibits semiconducting conductivity characteristics as it exists in a Fermi glass state. YBCO precursor solutions were prepared by the sol-gel method YBCO films were fabricated by the spin coating method, and structural and its electrical were studied at various oxygen partial pressures. The films Ar/O2 at 7 : 3 showed the more obvious YBa2Cu3O7-x phase and tetragonal phase. The thickness of all the films was approximately 0.23 ~ 0.31 µm and the average grain size of the YBCO film Ar/O2 at 7 : 3 was about 50 nm. Temperature resistance coefficient (TCR), responsivity, and detectivity of the YBCO film Ar/O2 at 7 : 3 were 3.2%/K at room temperature, 14.72 V/W, and 2.27 cmHz1/2/W, respectively.
Abstract
YBa2Cu3O7-x (YBCO) is the material of choice for second-generation superconducting wires and is the only current option for critical current density (Jc)> 1 MA/cm2 at 77 K [1]. YBCO belongs to a class of copper oxides well known for their superconducting properties. Its conduction properties can be changed from metallic (0.5 < x < 1) to insulating (0x0.5) by suitably decreasing the oxygen content [2]. The structural, electrical and optical properties of YBa2Cu3O7-x can be varied by adjusting the oxygen content x [3, 4]. As x is decreased to 0.5, the crystal undergoes a phase transition to a tetragonal structure and it exhibits semiconducting conductivity characteristics as it exists in a Fermi glass state. YBCO precursor solutions were prepared by the sol-gel method YBCO films were fabricated by the spin coating method, and structural and its electrical were studied at various oxygen partial pressures. The films Ar/O2 at 7 : 3 showed the more obvious YBa2Cu3O7-x phase and tetragonal phase. The thickness of all the films was approximately 0.23 ~ 0.31 µm and the average grain size of the YBCO film Ar/O2 at 7 : 3 was about 50 nm. Temperature resistance coefficient (TCR), responsivity, and detectivity of the YBCO film Ar/O2 at 7 : 3 were 3.2%/K at room temperature, 14.72 V/W, and 2.27 cmHz1/2/W, respectively.
참고문헌 (12)
- J. C. McIntyre, , J. appl. Phys, 71, pp.1868~ (1992)
- A. Jahanzeb, , Appl. Phys. Lett, 70, pp.3495~ (1997)
- A. Aligia, , Phys. Rev. B, 49, pp.524~ (1994)
- N. A. Khan, , Solid State Commun, 92, pp.607~ (1994)
- R.K. Bhan, "Uncooled Infrared Microbolometer Arrays and their Characterisation Techniques", Defence Science Journal, 59(6), pp.580~589 (2009)
- M. Lager, "Uncooled Carbon Microbolometer Imager", Ph.D., pp.2006
- J. Y. Yang, "A Research on How to Optimize the Level of the TCR and 1", f Noise Which Occur in the Polycrystalline Silicon Film Used as a Bolometer Resistor, Korea Advanced Institute of Science and Technology, 2006
- S. A. Dayeh, "Micromachined infrared bolometers on flexible polyimide substrates Original Research Article", Sensors and Actuators A: Physical, 118(1), pp.49~56 (2005)
- N. A. Khan, , Solid State Commun, 92, pp.607~ (1994)
- A. Dasgupta, "Highly conducttive ptype microcrystalline silicon carbide prepared by photochemical vapour deposition", J. Mater. Sci. Lett, 14, pp.1037~ (1995)
- M. Longhin, "Semiconducting YBCO thin films for uncooled terahertz imagers", Materials Science Forum, 587-588, pp.273~277 (2008)
- A. Mahmood, "Micromachined bolometers on polyimide", Sens. Actuators A, 132, pp.452~459 (2006)