Sensing performance of electrolyte-insulator-metal device based anodic aluminum oxide for pH detection
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
We fabricated the electrolyte-insulator-metal (EIM) sensor on the base of anodic aluminum oxide (AAO) template forcapacitive pH sensors. For the change of the thickness of AAO template, the second anodizing time was varied from 1 minto 10 min. With increasing the second anodizing time from 1 min to 10 min, the thickness of AAO template increased from90 nm to 1.3 µm. And the surface area compared to planar structure increased from 3 times to 25 times. The pH sensitivityof sensors with the second anodizing time of 10 min showed the highest value of 56.8 mV/pH in the concentration range frompH 3 to pH 11, a large hysteresis voltage of 7.6 mV in a cycle of pH 7 → 11 → 7 → 3 → 7. The EIM sensor with the secondanodizing time of 1 min exhibited the best long-term stability of 2.5 mV/h.
Abstract
We fabricated the electrolyte-insulator-metal (EIM) sensor on the base of anodic aluminum oxide (AAO) template forcapacitive pH sensors. For the change of the thickness of AAO template, the second anodizing time was varied from 1 minto 10 min. With increasing the second anodizing time from 1 min to 10 min, the thickness of AAO template increased from90 nm to 1.3 µm. And the surface area compared to planar structure increased from 3 times to 25 times. The pH sensitivityof sensors with the second anodizing time of 10 min showed the highest value of 56.8 mV/pH in the concentration range frompH 3 to pH 11, a large hysteresis voltage of 7.6 mV in a cycle of pH 7 → 11 → 7 → 3 → 7. The EIM sensor with the secondanodizing time of 1 min exhibited the best long-term stability of 2.5 mV/h.
참고문헌 (11)
- Y. M. Bae, , Biosens. Bioelectron, 21, pp.103~110 (2005)
- Z. Li, , Nano Letters, 4, pp.245~247 (2004)
- N. Nather, , Electrochimica Acta, 51, pp.924~929 (2005)
- K. Risveden, , Biosens. Bioelectron, 22, pp.3105~3112 (2007)
- M. J. Schoning, , Sensors and Actuators B, 35, pp.228~233 (1996)
- C. S. Lee, , Sensors, 9, pp.7111~7131 (2009)
- M. Schoning, , Sensors and Actuators B, 91, pp.92~97 (2003)
- B. Cullity, "Elements of X-ray Diffraction" (1978), Addison-Wesley
- D. L. Harame, , IEEE Trans. Electron Devices, 34, pp.1700~1707 (1987)
- T. M. Pan, , Sensors and Actuators B : Chemical, 127, pp.480~485 (2007)
- L. Bousse, , Sensors and Actuators B, 17, pp.157~164 (1994)