Synthesis of Eu, Dy co-doped SrAl2O4 phosphors by using liquid phase precursor process
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
SrAl2O4: Eu2+, Dy3+s are well-known as persistent luminescence phosphors with high brightness and long afterglow. They havebeen widely commercialized for afterglow applications such as security signs, emergency route signage, identification markers,and also bio-image in vivo. The persistent researches of SrAl2O4:Eu2+, Dy3+ phosphor have been widely studied during the pastdecades. In this study, the properties of SrAl2O4: Eu2+, Dy3+ phosphor were studied with wide range firing temperature anddifferent annealing conditions. Synthesis of persistent phosphorescence in Eu2+ and Dy3+ ions co-doped SrAl2O4 phosphorsfired at 1100-1300 oC was conducted by using the cellulose assisted liquid phase precursor (LPP) process under reducingatmosphere. The SrAl2O4: Eu2+ showed a typically broad emission band at 512 nm under excitation of UV range and Dy3+considerably enhanced the persistent luminescence intensity. Europium ions substituted for the two different Sr sites in thephosphor’s the monoclinic of host lattice resulting in greenish emission. The obtained phosphors were measured and analyzedby X-ray diffraction (XRD), scanning electron microscope (FE-SEM) and photoluminescence spectra (PL).
Abstract
SrAl2O4: Eu2+, Dy3+s are well-known as persistent luminescence phosphors with high brightness and long afterglow. They havebeen widely commercialized for afterglow applications such as security signs, emergency route signage, identification markers,and also bio-image in vivo. The persistent researches of SrAl2O4:Eu2+, Dy3+ phosphor have been widely studied during the pastdecades. In this study, the properties of SrAl2O4: Eu2+, Dy3+ phosphor were studied with wide range firing temperature anddifferent annealing conditions. Synthesis of persistent phosphorescence in Eu2+ and Dy3+ ions co-doped SrAl2O4 phosphorsfired at 1100-1300 oC was conducted by using the cellulose assisted liquid phase precursor (LPP) process under reducingatmosphere. The SrAl2O4: Eu2+ showed a typically broad emission band at 512 nm under excitation of UV range and Dy3+considerably enhanced the persistent luminescence intensity. Europium ions substituted for the two different Sr sites in thephosphor’s the monoclinic of host lattice resulting in greenish emission. The obtained phosphors were measured and analyzedby X-ray diffraction (XRD), scanning electron microscope (FE-SEM) and photoluminescence spectra (PL).
참고문헌 (14)
- D. Ravichandran, , Displays, 19(4), pp.197~203 (1999)
- V. Abbruscato, , J. of the Electrochem. Soc, 118(6), pp.930~933 (1971)
- T. Matsuzawa, , J. of the Electrochem. Soc, 143(8), pp.2670~2673 (1996)
- J. Qiu, , Solid State Communications, 106(12), pp.795~798 (1998)
- H. Takasaki, , Journal of Ceramic Society Japan, 104(4), pp.322~326 (1996)
- Q. M. Song, , Chinese Journal of Luminescence, 12(2), pp.144~149 (1991)
- M. D. Tang, , Chinese Journal of Luminescence, 16, pp.51~56 (1995)
- F. C. Palilla, , Journal of the Electrochemical Society, 115(10), pp.1076~1081 (1968)
- G. Blasse, , Philips Research Reports, 23, pp.201~206 (1968)
- S. Poort, , Chemistry of Materials, 7, pp.1547~1551 (1995)
- G. Blasse, "Luminescent Materials" (1994), Springer Verlag
- H. Yamada, , J. of the Electrochem. Soc, 150, pp.E251~E254 (2003)
- J. Holsa, , Journal of Alloys Compounds, 323, pp.326~330 (2001)
- 김정식, "Synthesis of SrAl2O4 : Eu, Dy-based phosphors by coprecipitation and characterization of their photoluminescence", Journal of Ceramic Processing Research, 10(4), pp.443~447 (2009), 세라믹공정연구센터