Enhancement of photoluminescence properties of SrAl2Si2O8:Eu2+ by a large amount of SiO2 addition
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
SiO2 added phosphors, SrAl2Si2O8:Eu2++ xSiO2 (x = 0, 1, 2 and 3 mol) were synthesized by a novel liquid phase precursor (LPP) method. The photoluminescence properties of phosphor added by 2 mol of SiO2 showed 71% increase in the emission intensity compared with the SrAl2Si2O8:Eu2+ phosphor. A broad emission and excitation wavelength was observed approximately from 400 nm to 600 nm centered at 430 nm and from 300 nm to 400 nm centered at 350 nm, respectively. Photoluminescence intensity of the phosphors increased continuously by SiO2 addition up to x = 2 mol and then it decreased at 3 mol of SiO2. The observed photoluminescence properties of the phosphors were discussed by their crystalline structure and morphology
Abstract
SiO2 added phosphors, SrAl2Si2O8:Eu2++ xSiO2 (x = 0, 1, 2 and 3 mol) were synthesized by a novel liquid phase precursor (LPP) method. The photoluminescence properties of phosphor added by 2 mol of SiO2 showed 71% increase in the emission intensity compared with the SrAl2Si2O8:Eu2+ phosphor. A broad emission and excitation wavelength was observed approximately from 400 nm to 600 nm centered at 430 nm and from 300 nm to 400 nm centered at 350 nm, respectively. Photoluminescence intensity of the phosphors increased continuously by SiO2 addition up to x = 2 mol and then it decreased at 3 mol of SiO2. The observed photoluminescence properties of the phosphors were discussed by their crystalline structure and morphology
참고문헌 (12)
- N. Hololnyak Jr, , Appl. Phys. Lett, 1, pp.82~ (1962)
- K. Sakuma, , J. Lumin, 126, pp.843~852 (2007)
- X.F. Hu, , Powder Technol, 188, pp.242~247 (2009)
- Y. Chen, , J. Lumin, 131, pp.1589~1593 (2011)
- Z.F. Pan, , Chem. Phys. Lett, 428, pp.78~ (2006)
- H.D. Ju, , Mater. Lett, 63, pp.1275~ (2009)
- H. Liua, , J. Lumin, 131, pp.2422~2426 (2011)
- J. Zhang, , J. Lumin, 131, pp.2463~2467 (2011)
- 윤대호, "Photoluminescence Characteristics of the Nano-Sized Red Phosphor (Yx,Gdy)O3:Eu3+1-x-y by Using Liquid Phase Precursor Methods", Journal of the Korean Physical Society, 53(5), pp.2382~2385 (2008), 한국물리학회
- F. Clabau, , J. Solid State Chem, 181(6), pp.1456~1461 (2008)
- L. Zhang, , Electrochem. Soc, 157(3), pp.J50~J53 (2010)
- T. Uchino, , Phys. Rev. B, 68, pp.041201(R)~ (2003)