Elaboration and characterization of barium titanate powders obtained by the mechanical activation of barium nitrate and titanate oxide, and electrical properties of the ceramics sintered by SPS
2
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
The current work aims to reduce the energy required to obtain a high quality barium titanate nanocrystals via solid-statereaction. In order to achieve this challenge, Ba(NO3)2 and TiO2 were mechanically activated by high-energy ball milling, andthen heat treated at moderate temperature (600 oC). When stoichiometric mixture was used, the formation of BT and minorBaCO3 and TiO2 impurities was observed. The use of Ba(NO3)2 excess leads to the formation of BT and a minor BaCO3impurity. A simple acid wash treatment was used to remove the carbonate impurity and to provide a high purity BT. Thepowders were characterized by XRD, BET, Raman spectroscopy, and SEM-FEG. Spark Plasma Sintering (SPS) technique wasused to get the dense nanoceramics. These materials show, at room temperature and at 1 kHz, colossal permittivity (ε = 105)associated with low dielectric loss (tg δ = 0.07).
Abstract
The current work aims to reduce the energy required to obtain a high quality barium titanate nanocrystals via solid-statereaction. In order to achieve this challenge, Ba(NO3)2 and TiO2 were mechanically activated by high-energy ball milling, andthen heat treated at moderate temperature (600 oC). When stoichiometric mixture was used, the formation of BT and minorBaCO3 and TiO2 impurities was observed. The use of Ba(NO3)2 excess leads to the formation of BT and a minor BaCO3impurity. A simple acid wash treatment was used to remove the carbonate impurity and to provide a high purity BT. Thepowders were characterized by XRD, BET, Raman spectroscopy, and SEM-FEG. Spark Plasma Sintering (SPS) technique wasused to get the dense nanoceramics. These materials show, at room temperature and at 1 kHz, colossal permittivity (ε = 105)associated with low dielectric loss (tg δ = 0.07).
참고문헌 (33)
- W. Heywang, , J. Am. Ceram. Soc, 47, pp.484~490 (1964)
- J.M. Herbert, "Electroceramics: Materials, Properties, Applications" (2003), Chapman and Hall
- Y. Ohara, , J. Am. Ceram. Soc, 68, pp.C-108~C-109 (1985)
- M. T. Buscaglia, , J. Am. Ceram. Soc, 88, pp.2374~2379 (2005)
- H. Xu, , Mater. Lett, 58, pp.1582~1586 (2004)
- S. K. Lee, , Mater. Lett, 57, pp.2201~2207 (2003)
- W. Li, , J. Alloys Compd, 482, pp.137~140 (2009)
- R. Kavian, , J. Alloys Compd, 468, pp.528~532 (2009)
- L. Wu, , Ceram. Int, 35, pp.957~960 (2009)
- Z. Valdez-Nava, , J. Electroceram, 22, pp.238~244 (2009)
- R. Licheri, , J. Eur. Ceram. Soc, 27, pp.2245~2253 (2007)
- C. Gomez-Yañez, , Ceram. Int, 26, pp.271~277 (2000)
- L. B. Kong, , J. Alloys Compd, 337, pp.226~230 (2002)
- S. Ohara, , Mater. Lett, 62, pp.2957~2959 (2008)
- A. K. Nath, , Physica B : Condensed Matter, 405, pp.430~434 (2010)
- M. F. S. Alves, , cripta Mater, 66, pp.1053~1056 (2012)
- B. D. Stojanovic, , J. Eur. Ceram. Soc, 25, pp.1985~1989 (2005)
- H. A. M. van Hal, , J. Eur. Ceram. Soc, 21, pp.1689~1692 (2001)
- L. G. D. Silveira, , Mater. Res. Bull, 48, pp.1772~1777 (2013)
- T. Sundararajan, , Mater. Res. Bull, 47, pp.1448~1454 (2012)
- V. Berbenni, , Thermochim. Acta, 374, pp.151~158 (2001)
- S. -S. Ryu, , J. Electroceram, 18, pp.243~250 (2007)
- J. Xue, , J. Am. Ceram. Soc, 83, pp.232~234 (2000)
- 윤당혁, "Tetragonality of barium titanate powder for a ceramic capacitor application", Journal of Ceramic Processing Research, 7(4), pp.343~354 (2006), 세라믹공정연구센터
- S. Guillemet-Fritsch, , Adv. Mater, 20, pp.551~555 (2008)
- H. Han, , J. Appl. Phys, 113, pp.024102~ (2013)
- E. Brzozowski, , Thermochim. Acta, 398, pp.123~129 (2003)
- B. Chen, , Phase Transitions, 86, pp.380~390 (2012)
- A. Neubrand, , J. Am. Ceram. Soc, 83, pp.860~864 (2000)
- T. Hoshina, , J. Appl. Phys, 99, pp.054311~ (2006)
- R. Burlica, , IEEE Transactions on, 44, pp.482~489 (2008)
- T. Al-Naboulsi, , International Journal of Engineering Research & Science, 1 (2015)
- C. Voisin, , Int. J. Appl. Ceram. Technol, 10, pp.E122~E133 (2013)