Microwave dielectric properties of Ba2(Mg1-2xY2xW1-x Tix)O6 ceramics
2
조회
0
다운로드
6
인용
0
참고문헌
키워드
초록
Phase formation, microstructure and microwave dielectric properties of Y2O3 and TiO2 doped BMW, i.e., Ba2(Mg1-2xY2xW1-xTix)O6, ceramics were investigated. Up to the composition of x = 0.5, the BMW ceramics having an ordered cubic structurewere only observed and no secondary phase such as BaWO4 was detected. As the value of x increased, the lattice parameterincreased linearly, implying that a substitutional solid solution occurred. A dense microstructure was observed. The grainshapes was certainly a polyhedron, indicating that the solid phase sintering occurred. As the x value increased, the dielectricconstant (εr) exhibited a tendency to increase slightly. The quality factor (Q × f0) sintered at 1700 oC increased up to x = 0.02and then saturated. All of the compositions sintered at 1700 oC exhibited negative values of the temperature coefficient ofresonant frequency (τf). The absolute value of τf decreased as the x value increased. Dielectric constant (εr), quality factor(Q × f0) and temperature coefficient of resonant frequency (τf) of the composition of x = 0.05, i.e., Ba2(Mg0.40Y0.10W0.45Ti0.10)O3,sintered at 1700 oC, were 19.6, 162,794 GHz, and -11.5 ppm/oC, respectively.
Abstract
Phase formation, microstructure and microwave dielectric properties of Y2O3 and TiO2 doped BMW, i.e., Ba2(Mg1-2xY2xW1-xTix)O6, ceramics were investigated. Up to the composition of x = 0.5, the BMW ceramics having an ordered cubic structurewere only observed and no secondary phase such as BaWO4 was detected. As the value of x increased, the lattice parameterincreased linearly, implying that a substitutional solid solution occurred. A dense microstructure was observed. The grainshapes was certainly a polyhedron, indicating that the solid phase sintering occurred. As the x value increased, the dielectricconstant (εr) exhibited a tendency to increase slightly. The quality factor (Q × f0) sintered at 1700 oC increased up to x = 0.02and then saturated. All of the compositions sintered at 1700 oC exhibited negative values of the temperature coefficient ofresonant frequency (τf). The absolute value of τf decreased as the x value increased. Dielectric constant (εr), quality factor(Q × f0) and temperature coefficient of resonant frequency (τf) of the composition of x = 0.05, i.e., Ba2(Mg0.40Y0.10W0.45Ti0.10)O3,sintered at 1700 oC, were 19.6, 162,794 GHz, and -11.5 ppm/oC, respectively.
참고문헌 (14)
- S. Bindra Narang, "Low loss dielectric ceramics for microwave applications: a review", Journal of Ceramic Processing Research, 11(3), pp.316~321 (2010), 세라믹공정연구센터
- H. Ohsato, , J. Ceram. Soc. Jpn, 113, pp.703~711 (2005)
- Naratip Vittayakorn, "Synthesis and a crystal structural study of microwave dielectric Zirconium Titanate (ZrTiO4) powders via a mixed oxide synthesis route", Journal of Ceramic Processing Research, 7(4), pp.288~291 (2006), 세라믹공정연구센터
- Y. Zhou, , J. Am. Ceram. Soc, 94, pp.2933~2938 (2011)
- S. Nomura, , Jpn. Appl. Phys, 21, pp.L624~L626 (1982)
- S. Kawashima, , J. Am. Ceram. Soc, 66, pp.421~423 (1983)
- H. Takahashi, , Jpn. J. Appl. Phys, 36, pp.5597~5599 (1997)
- J.Y. Wu, , Ceram. Int, 39, pp.3641~3649 (2013)
- J.J. Bian, , Ceram. Int, 42, pp.3290~3295 (2016)
- Y.-J. Lin, , Ceram. Int, 41, pp.8931~8935 (2015)
- J.Y. Wu, , J. Am. Ceram. Soc, pp.880~884 (2014)
- L.L.Y. Chang, , J. Am. Ceram. Soc, 49, pp.385~390 (1966)
- R.D. Shannon, , J. Appl. Phys, 73, pp.348~366 (1993)
- V.J. Fratello, , J. Mater. Res, 9, pp.2554~2560 (1994)