Mechanical properties and electrical resistivity of SiC-TiC composites with nitrate sintering additives
1
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
We fabricated SiC-TiC composites by hot-press sintering with aluminum and yttrium nitrate additive and evaluated crystal phase, relative density, microstructure, electrical resistivity and mechanical properties of the sintered body. And the effect of nitrate additive on the densification of SiC-TiC composites was compared with that of Al2O3 and Y2O3 additives. Because nitrate additives were uniformly dispersed in SiC and TiC mixture, it inhibited the growth of crystal grain between each other and formed fine and uniform microstructure, thereby improving mechanical properties and electrical resistivity. The electrical resistivity and flexural strength of the SiC-TiC composite with aluminum and yttrium nitrate additive were 2.3 Ω·cm and 652.3 MPa respectively.
Abstract
We fabricated SiC-TiC composites by hot-press sintering with aluminum and yttrium nitrate additive and evaluated crystal phase, relative density, microstructure, electrical resistivity and mechanical properties of the sintered body. And the effect of nitrate additive on the densification of SiC-TiC composites was compared with that of Al2O3 and Y2O3 additives. Because nitrate additives were uniformly dispersed in SiC and TiC mixture, it inhibited the growth of crystal grain between each other and formed fine and uniform microstructure, thereby improving mechanical properties and electrical resistivity. The electrical resistivity and flexural strength of the SiC-TiC composite with aluminum and yttrium nitrate additive were 2.3 Ω·cm and 652.3 MPa respectively.
참고문헌 (32)
- Y. G. Gogotsi, , Diam. Relat. Mater, 5(2), pp.151~162 (1996)
- Alfian Noviyanto, "Metal oxide additives for the sintering of silicon carbide: Reactivity and densification", Current Applied Physics, 13(1), pp.287~292 (2013), 한국물리학회
- O. Lopes, , J. Eur. Ceram. Soc, 27(11), pp.3351~3357 (2007)
- S. Prochazka, , J. Am. Ceram. Soc, 58(12), pp.72~ (1975)
- R. A. Alliegro, , J. Am. Ceram. Soc, 39(11), pp.386~389 (1956)
- D. Sciti, , J. Mater. Sci, 35(15), pp.3849~3855 (2000)
- K. Biswas, , J. Eur. Ceram. Soc, 23(7), pp.1099~1104 (2003)
- M. Balog, , J. Eur. Ceram. Soc, 25(4), pp.529~534 (2005)
- S. Kaur, , J. Eur. Ceram. Soc, 34(15), pp.3571~3578 (2014)
- H. Harima, , Microelectron. Eng, 83(1), pp.126~129 (2006)
- K. J. Kim, , Ceram. Int, 42(15), pp.17892~17896 (2016)
- J. R. Jenny, , J. Electron. Mater, 32(5), pp.432~436 (2003)
- F. Siegelin, , J. Mater. Res, 18(11), pp.2608~2617 (2003)
- K. J. Kim, , Ceram. Int, 43(15), pp.5343~5346 (2017)
- G. Augustine, , J. Cryst. Growth, 211(1-4), pp.339~342 (2000)
- T. Y. Cho, , J. Eur. Ceram. Soc, 36(11), pp.2659~2665 (2016)
- J. Cabrero, , J. Eur. Ceram. Soc, 31(3), pp.313~320 (2011)
- M. Khodaei, , Ceram. Int, 44(14), pp.16535~16542 (2018)
- O. Agac, , Ceram. Int, 43, pp.10434~10441 (2017)
- H. Endo, , J. Mater. Sci, 26, pp.3769~3774 (1991)
- D. Ahmoye, , Ceram. Int, 44(12), pp.14401~14407 (2018)
- D. Shaoming, , J. Mater. Sci. Lett, 15, pp.394~396 (1996)
- H. G. An, , J. Eur. Ceram. Soc, 21(1), pp.93~98 (2001)
- G. C. Wei, , J. Am. Ceram. Soc, 67(8), pp.571~574 (1984)
- M. Khodaei, , Int. J. Refract. Met. Hard Mater, 76, pp.141~148 (2018)
- J. Y. Kim, , J. Am. Ceram. Soc, 79(10), pp.2744~2746 (1996)
- T. Miyoshi, , J. Jpn. SpC. Mech. Eng. A, 51(471), pp.2489~2497 (1985)
- Z. Zhang, , Int. J. Refract. Met. Hard Mater, 41, pp.270~275 (2013)
- Y. Azizian-Kalandaragh, , Ceram. Int, 44(16), pp.19932~19938 (2018)
- M. Taya, , J. Am. Ceram. Soc, 73(5), pp.1382~1391 (1990)
- S. M. So, , Ceram. Int, 46(7), pp.9575~9581 (2020)
- M. S. Asl, , Ceram. Int, 45(16), pp.19808~19821 (2019)