Crack-healing behavior and bending strength of Al2O3/SiC composite ceramics according to the amount of added Y2O3
1
조회
0
다운로드
8
인용
0
참고문헌
키워드
초록
Three Al2O3/SiC composite ceramics were prepared, which included 1, 3 or 5 wt.% Y2O3, and their high-temperature bending strengths and in-situ crack-healing behaviors examined. A surface elliptical-crack of about 100 ߦ in diameter was introduced in the specimens using a Vickers hardness indenter. From in-situ observations, the Al2O3/SiC composite ceramic with 3 wt.%Y2O3 showed superior crack-healing ability than the 1 and 5 wt.% Y2O3 ceramics. The as-cracked specimen with 3 wt.% Y2O3showed strength recovery on heating for one hour at 1473 K in air, which may have been due to the lower crack-healing temperature on the addition of 3 wt.% Y2O3. The heat-resistance limit temperatures of the crack-healed Al2O3/SiC composite ceramics were 1073, 1373 and 873 K for 1, 3 and 5 wt.% Y2O3, respectively.
Abstract
Three Al2O3/SiC composite ceramics were prepared, which included 1, 3 or 5 wt.% Y2O3, and their high-temperature bending strengths and in-situ crack-healing behaviors examined. A surface elliptical-crack of about 100 ߦ in diameter was introduced in the specimens using a Vickers hardness indenter. From in-situ observations, the Al2O3/SiC composite ceramic with 3 wt.%Y2O3 showed superior crack-healing ability than the 1 and 5 wt.% Y2O3 ceramics. The as-cracked specimen with 3 wt.% Y2O3showed strength recovery on heating for one hour at 1473 K in air, which may have been due to the lower crack-healing temperature on the addition of 3 wt.% Y2O3. The heat-resistance limit temperatures of the crack-healed Al2O3/SiC composite ceramics were 1073, 1373 and 873 K for 1, 3 and 5 wt.% Y2O3, respectively.
참고문헌 (11)
- P.F. Becher, , J. Am. Ceram. Soc, 67(12), pp.267~269 (1984)
- K. Ando, , Fatigue Fract. Eng. Mater. Struct, 21(1), pp.119~122 (1998)
- K.W. Nam, , Mater. Sci. and Engng. A, 471(1), pp.102~105 (2007)
- F.F. Lange, , J. Am. Ceram. Soc., 53(5), pp.290~ (1970)
- M. Mimoto, , J. Mater. Sci. Lett, 15(22), pp.1976~1978 (1996)
- K. Ando, , Fatigue Fract. Eng. Mater. Struct., 27(7), pp.533~541 (2004)
- M. Ono, , Fatigue Fract. Eng. Mater. Struct., 30(7), pp.599~607 (2007)
- K. Ando, , J. Am. Ceram. Soc, 84(9), pp.2073~2078 (2001)
- K. Takahashi, , J. Am. Ceram. Soc, 88(3), pp.645~651 (2005)
- S.K. Lee, , J. Eur. Ceram. Soc, 25(15), pp.3495~3502 (2005)
- S.R. Choi, , Scr. Metall. Mater, 26, pp.1263~1268 (1992)