로켓탄 추진기관 온도반복시험 균열 원인분석
Analysis of the Causes of Cracks in Rocket Propellant in Thermal Cycling Test
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Purpose: The purpose of this study is to derive solutions and prevent similar cases from occurring by analyzing the causes of cracks found in temperature cycling tests of rocket motor. Methods: By combining the results of the current state confirmation test, non-destructive test, domestic and foreign rocket motor comparison test, cutting test, and adhesion test according to the number of times to apply mold release agent, a Cause and Effect Diagram analysis was performed to derive the cause of cracks. Results: Through this study, 26 factors that could cause cracking in rocket motors during temperature cycling tests were identified. Through various additional test results, a total of five causes were identified, including chemical and structural design of the joint between the propellant and stress relief insert, omission of procedure in the manufacturing procedures, natural aging due to temperature, and load accumulation due to temperature changes. The fundamental cause was confirmed to be insufficient consideration of the release properties of the propellant and stress relief insert. Conclusion: During the design process, it was confirmed that this could be solved by structurally or chemically designing the insert so that it does not combine with the propellant, or by applying a mold release agent during the manufacturing process.
Abstract
Purpose: The purpose of this study is to derive solutions and prevent similar cases from occurring by analyzing the causes of cracks found in temperature cycling tests of rocket motor. Methods: By combining the results of the current state confirmation test, non-destructive test, domestic and foreign rocket motor comparison test, cutting test, and adhesion test according to the number of times to apply mold release agent, a Cause and Effect Diagram analysis was performed to derive the cause of cracks. Results: Through this study, 26 factors that could cause cracking in rocket motors during temperature cycling tests were identified. Through various additional test results, a total of five causes were identified, including chemical and structural design of the joint between the propellant and stress relief insert, omission of procedure in the manufacturing procedures, natural aging due to temperature, and load accumulation due to temperature changes. The fundamental cause was confirmed to be insufficient consideration of the release properties of the propellant and stress relief insert. Conclusion: During the design process, it was confirmed that this could be solved by structurally or chemically designing the insert so that it does not combine with the propellant, or by applying a mold release agent during the manufacturing process.
참고문헌 (12)
- Cerri, Sara, "Ageing behaviour of HTPB based rocket propellant formulations", Central European Journal of Energetic Materials, 6(2), pp.149~165 (2009)
- 구승환, "유도탄 ASRP 실사격 수행방안에 관한 연구", 한국산학기술학회논문지, 23(12), pp.118~124 (2022), 한국산학기술학회[DOI]
- Ho, Sook-Ying,, "Modified fracture mechanics approach in structural analysis of solid-rocket motors", Journal of Propulsion and Power, 14(4), pp.409~415 (1998)
- Iqbal, Muhammad Mazhar,, "Modeling the moisture effects of solid ingredients on composite propellant properties", Aerospace Science and Technology, 10(8), pp.695~699 (2006)
- Kim, Youngseub, "Introduction to defense quality management" (2010), Hyungseul publishing network
- Le, Anhduong Q., "Detectability of delaminations in solid rocket motors with embedded stress sensors", Journal of Propulsion and Power, 29(2), pp.299~304 (2013)
- 임다훈, "무인기용 발사장비의 추진와이어 파단 및 구조변형 방지를 위한 형상변경 사례", 품질경영학회지, 50(3), pp.533~543 (2022), 한국품질경영학회[DOI]
- 문근환, "고체 로켓 추진 기관의 신뢰성 분석을 위한 준-정량적 FMECA", 대한기계학회논문집 A, 39(6), pp.631~638 (2015), 대한기계학회
- Reeling Brouwer, G., "Development and deployment of diagnostic prognostic tactical solid rocket motor demonstrator", 47th AIAA, SAE, pp.ASEE Joint Propulsion Conference &Exhibit, 2011
- Tussiwand, Giuseppe, "Application of Embedded Sensors Technology to a Full-Scale Nozzleless Rocket Motor", 43rd AIAA, SAE, pp.ASEE Joint Propulsion Conference & Exhibit, 2007
- Wong, F. C, "Pseudodomain fracture analysis of instrumented analog rocket motors", Journal of Spacecraft and Rockets, 40(1), pp.92~100 (2003)
- Yoon, K. S., "A Studay on the Estimation of Shelf-life for 155mm propelling charge KM4A2using ASRP's data", J Korean Soc Qual Manag, 42(3), pp.291~300 (2014)