Effect of the reaction temperature on nanocrystallites MgAl2O4 spinel ceramic precursor
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
Mg-Al hydrotalcite (Mg6Al2(OH)16CO3·4H2O), the precursor of MgAl2O4 spinel, has been synthesized via a coprecipitation method, using AlCl3·6H2O and MgCl2·6H2O as the raw materials, and NaOH and Na2CO3 as the precipitators. The effect of the reaction temperature, from 50℃ to 90℃, on the Mg-Al hydrotalcite nanocrystallites was analyzed. The nanocrystallites were studied by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). It was confirmed that Mg-Al hydrotalcite nanocrystallites are pure and regularly hexagonal, having a typical hydrotalcite structure. The Mg-Al hydrotalcite crystals grow from about 30 nm to 100 nm with an increase in the reaction temperature from 50℃ to 90 ℃, and the crystal form also tends to perfect and regularly hexagonal.
Abstract
Mg-Al hydrotalcite (Mg6Al2(OH)16CO3·4H2O), the precursor of MgAl2O4 spinel, has been synthesized via a coprecipitation method, using AlCl3·6H2O and MgCl2·6H2O as the raw materials, and NaOH and Na2CO3 as the precipitators. The effect of the reaction temperature, from 50℃ to 90℃, on the Mg-Al hydrotalcite nanocrystallites was analyzed. The nanocrystallites were studied by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). It was confirmed that Mg-Al hydrotalcite nanocrystallites are pure and regularly hexagonal, having a typical hydrotalcite structure. The Mg-Al hydrotalcite crystals grow from about 30 nm to 100 nm with an increase in the reaction temperature from 50℃ to 90 ℃, and the crystal form also tends to perfect and regularly hexagonal.
참고문헌 (10)
- H. R. Zargar, "The influence of nano boehmite on spinel formation in the alumina-magnesia system at low temperatures", Journal of Ceramic Processing Research, 9(1), pp.46~51 (2008), 세라믹공정연구센터
- S. Mukhopadhyay, , Ceram. Int, 33(2), pp.175~186 (2007)
- S.W. Jang, , Journal of Ceramic Processing Research, 2(4), pp.189~192 (2001)
- Y. Yuan, , J. Sol-Gel Sci. Technol, 30, pp.223~227 (2004)
- J.J. Liu, , Chem. Commun, (4), pp.542~543 (2003)
- F. Li, , Chem. Mate, 16(8), pp.1597~1602 (2004)
- G. Martínez-Lozano, , J. Alloys Compd, 434, pp.816~819 (2007)
- N. Nhlapo, , J. Mater. Sci, 43(3), pp.1033~1043 (2008)
- R.L. Frost, , J. Therm. Anal. Cal, 82(3), pp.603~608 (2005)
- K. Parida, , J. Mol. Catal. A: Chem, 151(12), pp.185~192 (2000)