Effect of precursor ratios on the synthesis of MgAl2O4 nanoparticles by a reverse microemulsion method
2
조회
0
다운로드
2
인용
0
참고문헌
키워드
초록
The effect of the Mg/Al ratio on the synthesis of MgAl2O4 nanoparticles by a reverse micelle process has been investigated in order to identify the phase composition in this system. Our study shows that the precursor ratio has significant effects on the structure and composition of the resulting nanoparticles. From the XRD analysis, a well-crystallized MgAl2O4 phase was formed at Mg/Al = 0.5 whereas at Mg/Al = 1, the crystallization of the nanoparticles was sluggish with MgAl2O4 and θ-Al2O3phases co-existing. By optimizing the Mg/Al ratio in the micelle solution, the average particle size of MgAl2O4 nanoparticles as determined from SEM and TEM were found to be 18 and 14 nm, respectively. The FTIR spectra show the lower frequency bands are assigned to metal-oxygen bonds (M–O–M). The thermal behavior of the precursor powders was characterized by DTA-TGA analysis.
Abstract
The effect of the Mg/Al ratio on the synthesis of MgAl2O4 nanoparticles by a reverse micelle process has been investigated in order to identify the phase composition in this system. Our study shows that the precursor ratio has significant effects on the structure and composition of the resulting nanoparticles. From the XRD analysis, a well-crystallized MgAl2O4 phase was formed at Mg/Al = 0.5 whereas at Mg/Al = 1, the crystallization of the nanoparticles was sluggish with MgAl2O4 and θ-Al2O3phases co-existing. By optimizing the Mg/Al ratio in the micelle solution, the average particle size of MgAl2O4 nanoparticles as determined from SEM and TEM were found to be 18 and 14 nm, respectively. The FTIR spectra show the lower frequency bands are assigned to metal-oxygen bonds (M–O–M). The thermal behavior of the precursor powders was characterized by DTA-TGA analysis.
참고문헌 (28)
- M.F.M. Zawrat, "Synthesis and characterisation of nanocrystallite MgAl~2O~4 ceramic powders by use of molten salts", British ceramic transactions, 101, pp.71~74 (2002)
- X.L. Pan, , Surf. A, 179, pp.163~169 (2001)
- A. Laobuthee, , J. Eur. Ceram. Soc, 20, pp.91~97 (2000)
- T. Yano, , J. Am.Ceram.Soc., 12, pp.3355~3364 (1999)
- M.C.L. Patterson, , Proc. SPIE, 5078, pp.71~79 (2003)
- G. Ye, , J. Am. Ceram. Soc., 88, pp.3241~3244 (2005)
- N. Thanabodeekij, , Mater. Charact, 50, pp.325~337 (2003)
- E.H. Walker Jr, , Mater. Res. Bull., 37, pp.1041~1050 (2002)
- A. Wajler, , J. Eur. Ceram.Soc., 28, pp.2495~2500 (2008)
- A. Saberi, , J Alloy Compd, 462, pp.142~146 (2008)
- B. Alinejad, , Mater. Res. Bull., 43, pp.1188~1194 (2008)
- M.M. Amini, , Mater. Res. Bull., 42, pp.563~570 (2007)
- D.D. Jayaseelan, , J. Eur. Ceram. Soc., pp.4745~4749 (2007)
- I. Ganesh, , Ceram.Int., 31, pp.67~74 (2005)
- M.P. Pileni, "Reactivity in Reverse Micelles", pp.12~ (1989), Elsevier
- T. Sugimoto, , J. Phys. Chem. B, 107, pp.10753~10759 (2003)
- T.H. Chieng, , Polymer, 36, pp.1941~1946 (1995)
- T.F. Towey, , J. Chem. Soc. Faraday Trans, 86, pp.3757~3762 (1990)
- W. Jahn, , J. Phys. Chem., 92, pp.2294~2301 (1988)
- R. Bandyopadhyaya, , Langmuir, 13, pp.3610~3620 (1997)
- M.A. Lopez-Quintela, , J. Colloid Interf. Sci., 158, pp.446~451 (1993)
- K. Osseo-Asare, , Ceram. Trans, 12, pp.3~16 (1990)
- N. Munshi, , J.Colloid.interf.Sci., 190, pp.387~391 (1997)
- M.F. Zawrah, , Ceram. Int., 33, pp.969~978 (2007)
- G.J. Li, , Mater. Lett., 65, pp.3585~3588 (2007)
- J. Parmentier, , Mater. Res. Bull, 33, pp.1717~1724 (1998)
- E.G. Brame, "Infrared and Raman Spectroscopy" (1976), Part A, Marcel Dekker
- K. Vivekanandan, , Mater. Chem. Phys., 39, pp.284~289 (1995)