Low-temperature crystallization at 700 oC of magnesium aluminate nanospinel Using nitrate precursors by masking-gel calcination process
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Nanoparticles MgAl2O4 spinel with the cubic crystal structure was successfully prepared through masking-gel calcination process, using aluminum and magnesium nitrates as spinel precursors and sugar as a masking-gel agent. Calcination treatment was performed at 600 o C, 700 o C, 800 o C, 900 o C, and 1000 o C. X-ray diffraction analysis, transmission electron microscopy and scanning electron microscopy studies were conducted to identify the crystalline phase and the microstructure of the spinel product. The metal nitrate precursors were found to crystallize completely as MgAl2O4 spinel at a low temperature of 700 o C having crystallite sizes below 15 nm. The average particle sizes of the spinel powder at that temperature were less than 75 nm. The microstructure analysis of the spinel sample at the calcination temperature of 1000 o C shows the particle sizes below 100 nm and high formation of agglomerates.
Abstract
Nanoparticles MgAl2O4 spinel with the cubic crystal structure was successfully prepared through masking-gel calcination process, using aluminum and magnesium nitrates as spinel precursors and sugar as a masking-gel agent. Calcination treatment was performed at 600 o C, 700 o C, 800 o C, 900 o C, and 1000 o C. X-ray diffraction analysis, transmission electron microscopy and scanning electron microscopy studies were conducted to identify the crystalline phase and the microstructure of the spinel product. The metal nitrate precursors were found to crystallize completely as MgAl2O4 spinel at a low temperature of 700 o C having crystallite sizes below 15 nm. The average particle sizes of the spinel powder at that temperature were less than 75 nm. The microstructure analysis of the spinel sample at the calcination temperature of 1000 o C shows the particle sizes below 100 nm and high formation of agglomerates.
참고문헌 (32)
- H. R. Zargar, , J. Alloys Compd, 507, pp.443~447 (2010)
- I. Ganesh, , CERIN, 37, pp.2237~2245 (2011)
- A. Saberi, , J. Alloys Compd, 462, pp.142~146 (2008)
- J. Chandradass, , J. Alloys Compd, 491, pp.L25~L28 (2010)
- N. M. Khalil, , J Alloys Compd, 496, pp.600~607 (2010)
- F. N. Cunha-Duncan, , J. Am. Ceram. Soc, 85, pp.2995~3003 (2002)
- Z. Zhihui, , Sci. Sintering, 36, pp.73~79 (2004)
- I. Ganesh, , CERIN, 35, pp.259~264 (2009)
- F. Tavangarian, , J. Alloys and Compd, 489, pp.600~604 (2010)
- S. Mukhopadhyay, , Ceramics-Silikáty, 48, pp.100~109 (2004)
- K. Prabhakaran, , Mater. Res. Bull, 44, pp.613~618 (2009)
- W. Liu, , Adv. Powder Technol, 24, pp.436~440 (2013)
- K. Maca, , Ceramics-Silikáty, 51, pp.94~97 (2007)
- E. Straßburger, , J. Euro. Ceram. Soc, 29, pp.267~273 (2009)
- I. E. Reimanis, , Proc. the Defense and Security Symp. on the Society of Photo-Optical Instrumentation Engineers (2004)
- O. Borrero-López, , J. Euro. Ceram. Soc, 32, pp.3143~3149 (2012)
- R. Cook, , Proc. the Defense and Security Symp. on the Society of Photo-Optical Instrumentation Engineers (2005)
- Tamar Kadosh, "In Situ Characterization of Spinel Nanoceramic Suspensions", Journal of the American Ceramic Society, 95(10), pp.3103~3108 (2012), Wiley[DOI]
- S. Kurien, , Indian Journal of Pure & Applied Physics, 42, pp.926~933 (2004)
- L. R. Ping, , Mater. Res. Bull, 36, pp.1417~1430 (2001)
- M. K. Naskar, , J. Am. Ceram. Soc, 88, pp.38~44 (2005)
- A. Banerjee, , CERIN, 35, pp.381~390 (2009)
- S. Pal, , Bull. Mater. Sci, 33, pp.451~456 (2010)
- Y. Safaei-Naeini, , Iranian J. Mater. Sci. Eng, 8, pp.23~28 (2011)
- Z. Ding, , Bulg. J. Phys, 30, pp.152~157 (2003)
- K. Y. Park, , Journal of Nanoparticle Research, 8, pp.1075~1081 (2006)
- R. Septawendar, , CERIN, 37, pp.3747~3754 (2011)
- Rifki Septawendar, "Effect of sugar and citric acid as precursors in ZrO2 nanopowder preparation at low calcination temperatures", Journal of Ceramic Processing Research, 13(3), pp.343~348 (2012), 세라믹공정연구센터[DOI]
- R. Septawendar, , Journal of the Australian Ceramic Society, 49, pp.101~108 (2013)
- Rifki Septawendar, "Nanocrystalline α-Al2O3 powder preparation with sucrose as a template through a chemical route", Journal of Ceramic Processing Research, 12(4), pp.365~370 (2011), 세라믹공정연구센터
- Y. C. Lee, , J. Am. Ceram. Soc, 90, pp.407~411 (2007)
- V. Santos, , Rev. Adv. Mater. Sci, 17, pp.62~70 (2008)