나노결정 Fe73Si16B7Nb3Cu1 연자성분말과 숯분말 혼합 복합성형체의 전자파흡수 특성
Electromagnetic Wave Absorption Properties of Fe73Si16B7Nb3Cu1-Based Nanocrystalline Soft Magnetic Powder Composite Mixed with Charcoal Powder
1
조회
0
다운로드
1
인용
0
참고문헌
키워드
초록
The electromagnetic wave absorption sheets were fabricated by mixing of Fe73Si16B7Nb3Cu1 nanocrystalline soft magnetic powder, charcoal powder and polymer based binder. The complex permittivity, complex permeability, and scattering parameter have been measured using a network analyzer in the frequency range of 10 MHz~10 GHz. The results showed that complex permittivity of sheets was largely dependent on the frequency and the amount of charcoal powder : The permittivity was improved up to 100 MHz, however the value was decreased above 1 GHz. The power loss of electromagnetic wave absorption data showed almost the same tendency as the results of complex permittivity. However, the complex permeability was not largely affected by the frequency, and the values were decreased with the addition of charcoal powder. Based on the results, it can be summarized that the addition of charcoal powder was very effective to improve the EM wave absorption in the frequency range of 10 MHz~1 GHz.
Abstract
The electromagnetic wave absorption sheets were fabricated by mixing of Fe73Si16B7Nb3Cu1 nanocrystalline soft magnetic powder, charcoal powder and polymer based binder. The complex permittivity, complex permeability, and scattering parameter have been measured using a network analyzer in the frequency range of 10 MHz~10 GHz. The results showed that complex permittivity of sheets was largely dependent on the frequency and the amount of charcoal powder : The permittivity was improved up to 100 MHz, however the value was decreased above 1 GHz. The power loss of electromagnetic wave absorption data showed almost the same tendency as the results of complex permittivity. However, the complex permeability was not largely affected by the frequency, and the values were decreased with the addition of charcoal powder. Based on the results, it can be summarized that the addition of charcoal powder was very effective to improve the EM wave absorption in the frequency range of 10 MHz~1 GHz.
참고문헌 (17)
- Taflove, A., , IEEE Trans. Microwave Theory Tech., 23, pp.888~ (1975)
- Jarupat, S., , J. Physiol Anthropol, 22, pp.61~ (2003)
- Abbas, S. M., , Composites: Part A, 37, pp.2148~ (2006)
- Zhihua, P., , Phys. Lett. A, 372, pp.3714~ (2008)
- Sangawar, V. S., , Bulletin of Materials Science, 29, pp.413~ (2006)
- Moon, K. S., , J. Appl. Poly. Sci., 77, pp.1294~ (2000)
- Yoshisa, S., , J. Appl. Phys., 85, pp.4636~ (1999)
- 홍순호, "연자성 합금 분말의 입자크기에 따른 전자파 흡수 특성 비교", 한국분말야금학회지, 14(4), pp.261~264 (2007), 한국분말야금학회
- 고재귀, "Ni-Cu-Zn Ferrite의 복합형 전파흡수체 특성 연구", 한국자기학회지, 17(6), pp.238~241 (2007), 한국자기학회
- Esawi, A., , Composites: Part A, 38, pp.646~ (2007)
- Yoshizawa, Y., , J. Appl. Phys., 64, pp.6044~ (1988)
- Petzold, J., , J. Magn. Magn. Mater., 242, pp.84~ (2002)
- Fenske, K., , Appl. Microwaves Wireless, 12, pp.92~ (2000)
- Davis, L. C., , J. Appl. Phys., 72, pp.1334~ (1992)
- Jung, J. C., , The Korean Society of Industrial Application, 5, pp.27~ (2006)
- Barba, A. A., , Poly. Bull., 57, pp.587~ (2006)
- Lee, K. S., , J. Korea Electromagnetic Engineering Society, 16, pp.228~ (2005)