Fe계 나노결정립 분말 시트에 첨가된 CNT의 볼밀 공정에 따른 전자파 흡수 특성 변화
The Characteristic Changes of Electromagnetic Wave Absorption in Fe-based Nanocrystalline P/M Sheets Mixed with Ball-Milled Carbon Nanotubes
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Electromagnetic wave energies are consumed in the form of thermal energy, which is mainly caused by magnetic loss, dielectric loss and conductive loss. In this study, CNT was added to the nanocrystalline soft magnetic materials inducing a high magnetic loss, in order to improve the dielectric loss of the EM wave absorption sheet. Generally, the aspect ratio and the dispersion state of CNT can be changed by the pre-ball milling process, which affects the absorbing properties. After the various ball-milling processes, 1wt% of CNTs were mixed with the nanocrystalline Fe73Si16B7Nb3Cu1 base powder, and then further processed to make EM absorption sheets. As a result, the addition of CNT to Fe-based nanocrystalline materials improved the absorption properties. However, the increase of ball-milling time for more than 1h was not desirable for the powder mixture, because the ballmilling caused the shortening of CNT length and the agglomeration of the CNT flakes.
Abstract
Electromagnetic wave energies are consumed in the form of thermal energy, which is mainly caused by magnetic loss, dielectric loss and conductive loss. In this study, CNT was added to the nanocrystalline soft magnetic materials inducing a high magnetic loss, in order to improve the dielectric loss of the EM wave absorption sheet. Generally, the aspect ratio and the dispersion state of CNT can be changed by the pre-ball milling process, which affects the absorbing properties. After the various ball-milling processes, 1wt% of CNTs were mixed with the nanocrystalline Fe73Si16B7Nb3Cu1 base powder, and then further processed to make EM absorption sheets. As a result, the addition of CNT to Fe-based nanocrystalline materials improved the absorption properties. However, the increase of ball-milling time for more than 1h was not desirable for the powder mixture, because the ballmilling caused the shortening of CNT length and the agglomeration of the CNT flakes.
참고문헌 (15)
- J. R. Liu, , J. Appl. Phys., 37, pp.2737~ (2004)
- S. S. Kim, , IEEE Tans. Magn., 27, pp.5462~ (1991)
- J. R. Liu, , Appl. Phys. Lett., 88, pp.062503~ (2006)
- J. H. Choi, , Journal of The Korean Electromagnetic Engineering Society, 16, pp.842~ (2005)
- S. Yoshida, , J. Appl. Phys., 85, pp.4636~ (1999)
- T. Nakamura, , J. Appl. Phys., 88, pp.348~ (2000)
- Y. Yoshizawa, , IEEE Trans. Magn., 25, pp.3324~ (1989)
- G. Herzer, , IEEE Trans. Magn., 25, pp.3327~ (1989)
- B. Hornbostel, , Physica E, 40, pp.2425~ (2008)
- N. Darsono, , Appl. Surf. Sci., 254, pp.3412~ (2008)
- 이종일, "탄소나노튜브 복합체의 기술동향", Korean Chemical Engineering Research(HWAHAK KONGHAK), 46(1), pp.7~14 (2008), 한국화학공학회
- D. D. L. Chung, , Carbon, 39, pp.279~ (2001)
- A. Esawi, , Composites: part A, 38, pp.646~ (2007)
- 김선이, "나노결정 Fe73Si16B7Nb3Cu1 연자성분말과 숯분말 혼합 복합성형체의 전자파흡수 특성", 한국분말야금학회지, 16(4), pp.291~295 (2009), 한국분말야금학회
- Z. Tao, , Mater. Lett., 58, pp.3410~ (2004)