Fe계 나노결정립 분말과 페라이트 복합체의 전자파 흡수특성
Electromagnetic Wave Absorption Behavior of a Fe-based Nanocrystalline Alloy mixed with a Ferrite Powder
2
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
The electromagnetic (EM) wave absorption properties of the Fe73Si16B7Nb3Cu1 nanocrystalline powder mixed with 5 to 20 vol% of Ni-Zn ferrites has been investigated in a frequency range from 100MHz to 10GHz. Amorphous ribbons prepared by a planar flow casting process were pulverized and milled after annealing at 425 for 1 hour. The powder was mixed with a ferrite powder at various volume ratios to tape-cast into a 1.0mm thick sheet. Results showed that the EM wave absorption sheet with Ni-Zn ferrite powder reduced complex permittivity due to low dielectric constant of ferrite compared with nanocrystalline powder, while that with 5 vol% of ferrite showed relatively higher imaginary part of permeability. The sheet mixed with 5 vol% ferrite powder showed the best electromagnetic wave absorption properties at high frequency ranges, which resulted from the increased imaginary part of permeability due to reduced eddy current.
Abstract
The electromagnetic (EM) wave absorption properties of the Fe73Si16B7Nb3Cu1 nanocrystalline powder mixed with 5 to 20 vol% of Ni-Zn ferrites has been investigated in a frequency range from 100MHz to 10GHz. Amorphous ribbons prepared by a planar flow casting process were pulverized and milled after annealing at 425 for 1 hour. The powder was mixed with a ferrite powder at various volume ratios to tape-cast into a 1.0mm thick sheet. Results showed that the EM wave absorption sheet with Ni-Zn ferrite powder reduced complex permittivity due to low dielectric constant of ferrite compared with nanocrystalline powder, while that with 5 vol% of ferrite showed relatively higher imaginary part of permeability. The sheet mixed with 5 vol% ferrite powder showed the best electromagnetic wave absorption properties at high frequency ranges, which resulted from the increased imaginary part of permeability due to reduced eddy current.
참고문헌 (13)
- S. Sugimoto, , J. Alloys. Comp, 330, pp.301~ (2002)
- J. R. Liu, , J. Appl. Phys, 37, pp.2737~ (2004)
- 노태환, "FeSiCr 박편", 폴리머 복합 시트의 전자파 흡수 특성에 미치는 자성분말 입도의 영향, 2008, pp.46(1), 44~51[DOI]
- D. S. Li, , J. Alloys Compd, 408, pp.1429~ (2006)
- H. J. Cho, , Mater. Sci. Forum, 통권 : 534, pp.1345~ (2007)
- 홍순호, "연자성 나노결정합금 분말의 열처리 온도에 의한 전자파 흡수 특성의 영향", 한국분말야금학회지, 15(1), pp.18~22 (2008), 한국분말야금학회
- K. M. Lim, , J. Kor. Inst. Met & Mater, 41, pp.180~ (2003)
- Y. Yoshizawa, , J. Appl. Phys, 64, pp.6044~ (1988)
- F. Mazaleyrat, , J. Magn & Magn Mater, 215, pp.253~ (2000)
- [URL]
- S. P. Parker, "Encyclopedia of Physics", pp.232~ (1983), McGraw-Hill
- [URL]
- A. Hosoe, , SEI Tech. Rev, 54, pp.20~ (2002)