액중 전기선 폭발법에 의한 Ni-free Fe계 나노 합금분말의 제조: 1. 합금 wire의 직경 및 인가 전압의 영향
Fabrication of Ni-free Fe-based Alloy Nano Powder by Pulsed Wire Evaporation in Liquid: Part I. Effect of Wire Diameter and Applied Voltage
0
조회
0
다운로드
3
인용
0
참고문헌
키워드
초록
This study investigated the effect of wire diameter and applied voltage on the fabrication of Ni-free Fe-based alloy nano powders by employing the PWE (pulsed wire evaporation) in liquid, for high temperature oxidation-resistant metallic porous body for high temperature particulate matter (or soot) filter system. Three different diameter (0.1, 0.2, and 0.3 mm) of alloy wire and various applied voltages from 0.5 to 3.0 kV were main variables in PWE process, while X-ray diffraction (XRD), field emission scanning microscope (FE-SEM), and transmission electron microscope (TEM) were used to investigate the characteristics of the Fe-Cr-Al nano powders. It was controlled the number of explosion events, since evaporated and condensed nano-particles were coalesced to micron-sized secondary particles, when exceeded to the specific number of explosion events, which were not suitable for metallic porous body preparation. As the diameter of alloy wire increased, the voltage for electrical explosion increased and the size of primary particle decreased.
Abstract
This study investigated the effect of wire diameter and applied voltage on the fabrication of Ni-free Fe-based alloy nano powders by employing the PWE (pulsed wire evaporation) in liquid, for high temperature oxidation-resistant metallic porous body for high temperature particulate matter (or soot) filter system. Three different diameter (0.1, 0.2, and 0.3 mm) of alloy wire and various applied voltages from 0.5 to 3.0 kV were main variables in PWE process, while X-ray diffraction (XRD), field emission scanning microscope (FE-SEM), and transmission electron microscope (TEM) were used to investigate the characteristics of the Fe-Cr-Al nano powders. It was controlled the number of explosion events, since evaporated and condensed nano-particles were coalesced to micron-sized secondary particles, when exceeded to the specific number of explosion events, which were not suitable for metallic porous body preparation. As the diameter of alloy wire increased, the voltage for electrical explosion increased and the size of primary particle decreased.
참고문헌 (13)
- KIPO, "Automotive Exhaust Gas After-treatment", pp.73~ (2004)
- KIPO, "Automotive Exhaust Gas After-treatment", pp.90~ (2004)
- Y. Park, , Ceramist, 10, pp.58~ (2007)
- "Alantum"[URL]
- 이희민, "전기선폭발법에 의해 카본 코팅된 Cu 나노분말의 제조 및 특성 연구", 한국분말야금학회지, 16(4), pp.243~248 (2009), 한국분말야금학회
- 김창규, "산화구리 나노분말을 포함하는 에틸렌글리콜 용액의 열전특성에 관한 연구", 한국분말야금학회지, 17(4), pp.276~280 (2010), 한국분말야금학회
- 박중학, "전기폭발법에 의한 Ni 및 Ni-Cu 나노 금속 분말의 제조와 자기적 특성연구", 한국분말야금학회지, 10(2), pp.83~88 (2003), 한국분말야금학회
- 이근희, "동시 전기 폭발법에 의한 나노 합금 분말 제조에 관한 연구 II-Fe-Al alloy 분말 제조", 한국분말야금학회지, 11(2), pp.105~110 (2004), 한국분말야금학회
- Dmitrii V. Tichonov, "Morphology, Phase Contents, and Chemical Composition of Nanopowders Produced by the Electrical Explosion of Tin-Lead Alloy Wires", 한국분말야금학회지, 10(3), pp.157~160 (2003), 한국분말야금학회
- 박제신, "전기선 폭발법으로 제조된 Al-Cu 합금 나노분말을 이용한 다공성 나노 입자 제조", 한국분말야금학회지, 15(3), pp.234~238 (2008), 한국분말야금학회
- 박은주, "유체 내 전기선폭발법에 의한 은 나노입자 유체의 제조 및 특성", 한국분말야금학회지, 16(3), pp.217~222 (2009), 한국분말야금학회
- 이근희, "동시 전기 폭발법에 의한 나노 합금 분말 제조에 관한 연구Part I - 동시 전기 폭발을 위한 이론적 배경", 한국분말야금학회지, 11(1), pp.60~68 (2004), 한국분말야금학회
- 이창우, "전기폭발법에서 SMPS를 이용한 Cu 나노분말의 실시간 입자특성평가", 한국분말야금학회지, 10(4), pp.275~280 (2003), 한국분말야금학회