금속열환원 공정에서 반응온도가 니오븀 분말 특성에 미치는 영향
The Effect of Reduction Temperature on the Characteristic Variation of Niobium Powder During Metallothermic Reduction Process
1
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
Niobium powder was made from potassium heptafluoroniobite (K2NbF7) as the raw material using sodium (Na) as a reducing agent based on the hunter process. The apparatus for the experiment was designed and built specifically for the present study. The niobium particle size greatly increased as the reduction temperature increased from 710℃ to 800℃. The particle size was fairly uniform, varying from 0.09 μm to 0.4 ㎛ depending on the reduction temperatures. The niobium powder morphology and particle size are very sensitive to a reaction temperature in the metallothermic reduction process. The yield of niobium powder increased from 55% to 80% with a increasing a reaction temperature.
Abstract
Niobium powder was made from potassium heptafluoroniobite (K2NbF7) as the raw material using sodium (Na) as a reducing agent based on the hunter process. The apparatus for the experiment was designed and built specifically for the present study. The niobium particle size greatly increased as the reduction temperature increased from 710℃ to 800℃. The particle size was fairly uniform, varying from 0.09 μm to 0.4 ㎛ depending on the reduction temperatures. The niobium powder morphology and particle size are very sensitive to a reaction temperature in the metallothermic reduction process. The yield of niobium powder increased from 55% to 80% with a increasing a reaction temperature.
참고문헌 (13)
- D. Larry, , columbium(niobium) and tantalum, 21 (1999)
- C. A. Hampel, "Rare Metals Handbook" (1961), Reinhold
- C. J. Smithells, , Met. Ind. (Lond.), 38, pp.336~ (1931)
- Hamilton C. B., , Proc. Iowa. Acad. Sci., 통권 : 68, pp.189~ (1961)
- M. Baba, , J. Phys. Chem. Solids, 66, pp.466~ (2005)
- JFE Giho, "JFE Mineral", JFE Co. Ltd., 63~ (2005)
- Kontantinov V. I., , Poroskovaya Met. Acad. Nauk SSRI, 4, pp.47~ (1961)
- E. G. Hellier, "US Patent 2,950,185", ~ (1960)
- D. K. Bose, , Trans. Indian Inst. Met., 23, pp.1~ (1970)
- C. K. Gupta, , Trans. Indian Inst. Met., 22, pp.51~ (1969)
- K. Wayne, "U. S. Patent 2,927,855, March 8", ~ (1960)
- S. C. Jain, , Trans. Indian Inst. Met., 24, pp.1~ (1971)
- J. T. Kelly, "Canadian Patent 657,596", ~ (1963)