초록
The niobium capacitor showed somewhat more unstable characteristics than the commercial tantalum capacitors, but is nonetheless considered applicable as a future substitute for tantalum capacitors. In this study, niobium powder was fabricated by metallothermic reduction process using K2NbF7 as the raw materials, KCl and KF as the diluents and Na as the reducing agent. The niobium particle size greatly decreased from 0.7um to 0.2um as the amount of diluent increased. However if a higher surface area of powder is required, more diluents need to be used in the said method in order to produce niobium powder. The niobium powder morphology and particle size are very sensitive to a amount of sodium excess. The particle size of niobium powder increased with a increasing amount of sodium excess. When more diluent and sodium are used, the niobium powder will be contaminated with more impurities such as Fe, Cr, Ni so on.
Abstract
The niobium capacitor showed somewhat more unstable characteristics than the commercial tantalum capacitors, but is nonetheless considered applicable as a future substitute for tantalum capacitors. In this study, niobium powder was fabricated by metallothermic reduction process using K2NbF7 as the raw materials, KCl and KF as the diluents and Na as the reducing agent. The niobium particle size greatly decreased from 0.7um to 0.2um as the amount of diluent increased. However if a higher surface area of powder is required, more diluents need to be used in the said method in order to produce niobium powder. The niobium powder morphology and particle size are very sensitive to a amount of sodium excess. The particle size of niobium powder increased with a increasing amount of sodium excess. When more diluent and sodium are used, the niobium powder will be contaminated with more impurities such as Fe, Cr, Ni so on.
참고문헌 (9)
- C. B. Hamilton, , Proc. Iowa. Acad. Sci., 68, pp.189~ (1961)
- M. Baba, , J. Phys. Chem. Solids, 66, pp.466~ (2005)
- JFE Mineral, , JFE Giho, 8, pp.63~ (2005), JFE Co. Ltd.
- V. I. Kontantinov, , Met. Acad. Nauk SSRI, 4, pp.47~ (1961)
- E. G. Hellier, "US Patent 2,950,185", ~, pp.특허 (1960)
- D. K. Bose, , Trans. Indian Inst. Met., 23, pp.1~ (1970)
- CIBA Limited, "Belgium Patent 625,173", ~, pp.특허 (1963)
- 윤재식, "K2NbF7로부터 Na 열환원 공정에 의한 니오븀 분말의 제조", 한국재료학회지, 19(7), pp.386~390 (2009), 한국재료학회
- A. N. Zelikman, "Metallurgy of rare metals. in: Israel programme for scientific translation", pp.136~ (1966), Jerusalem