하이브리드 선형이온원에 의한 유압 기어펌프용 Cr-DLC코팅막의 특성과 효율성능
Coatings Properties and Efficiency Performance of Cr-DLC Films Deposited by Hybrid Linear Ion Source for Hydraulic Gear Pump
0
조회
0
다운로드
0
인용
0
참고문헌
키워드
초록
This paper describes the results of the application of Cr-Diamond-like carbon (DLC) films for efficiency improvement through surface modification of spur gear parts in the hydraulic gear pump. Cr-DLC films were successfully deposited on SCM 415 substrates by a hybrid coating process using linear ion source (LIS) and magnetron sputtering method. The characteristics of the films were systematically investigated using FE-SEM,nano-indentation, sliding tester and AFM instrument. The microstructure of Cr-DLC films turned into the dense and fine grains with relatively preferred orientation. The thickness formed in our Cr buffer layer and DLC coating layer were obtained the 487 nm and 1.14 μm. The average friction coefficient of Cr-DLC films considerably decreased to 0.15 for 0.50 of uncoated SCM415 material. The hardness and surface roughness of Cr-DLC films were measured 20 GPa and 10.76 nm, respectively. And then, efficiency tests were performed on the hydraulic gear pump to investigate the efficiency performance of the Cr-DLC coated spur gear. The experimental results show that the volumetric and mechanical efficiency of hydraulic gear pump using the Cr-DLC spur gear were improved up to 2~5% and better efficiency improvement could be attributed to its excellent microstructure, higher hardness, and lower friction coefficient. This conclusion proves the feasibility in the efficiency improvement of hydraulic gear pump for industrial applications.
Abstract
This paper describes the results of the application of Cr-Diamond-like carbon (DLC) films for efficiency improvement through surface modification of spur gear parts in the hydraulic gear pump. Cr-DLC films were successfully deposited on SCM 415 substrates by a hybrid coating process using linear ion source (LIS) and magnetron sputtering method. The characteristics of the films were systematically investigated using FE-SEM,nano-indentation, sliding tester and AFM instrument. The microstructure of Cr-DLC films turned into the dense and fine grains with relatively preferred orientation. The thickness formed in our Cr buffer layer and DLC coating layer were obtained the 487 nm and 1.14 μm. The average friction coefficient of Cr-DLC films considerably decreased to 0.15 for 0.50 of uncoated SCM415 material. The hardness and surface roughness of Cr-DLC films were measured 20 GPa and 10.76 nm, respectively. And then, efficiency tests were performed on the hydraulic gear pump to investigate the efficiency performance of the Cr-DLC coated spur gear. The experimental results show that the volumetric and mechanical efficiency of hydraulic gear pump using the Cr-DLC spur gear were improved up to 2~5% and better efficiency improvement could be attributed to its excellent microstructure, higher hardness, and lower friction coefficient. This conclusion proves the feasibility in the efficiency improvement of hydraulic gear pump for industrial applications.
참고문헌 (16)
- N. Renevier, , Surf. Coat. Technol, 67, pp.142~144 (2001)
- J. Robertson, "Surface and Coating Technology", 50, pp.185~ (1992)
- 이충환, "플라즈마 스프레이 (LaSr)(CrCo)O3 코팅된 STS-430 합금의 고온 산화 거동 및 전기적 특성", 한국분말야금학회지, 16(3), pp.185~190 (2009), 한국분말야금학회
- J. Robertson, , Diamond & Related Materials, 2, pp.984~ (1993)
- J. Robertson, , Surface and Coating Technology, 50, pp.185~ (1992)
- 김왕렬, "Linear Ion Source를 이용한 Anode Voltage 변화에 따른 DLC박막특성", 한국표면공학회지, 42(4), pp.179~185 (2009), 한국표면공학회
- J. Ivantysyn, "Hydrostatic Pumps and Motors" (2001), Academia Book International
- S. Hogmark, "Modern Tribology Handbook New York" (2000), CRC Press
- K. R. Lee, , Thin Solid Films, 377, pp.261~ (2000)
- Wei Dai, , Diamond & Related Materials, 19, pp.1307~ (2010)
- Naoki Insu, , pp.940~ (2006), Powder Metallurgy World Congress Part2
- H. Walker, "Gear Pump Teeth", Automobile Eng, 478, pp.347~ (2005)
- 안효석, "Si 함유량에 따른 Si-DLC", DLC 코팅의 건조마찰 특성, 2007, pp.16(6), 212~216[DOI]
- W. Carlos, , Solid State Science, 11, pp.1778~ (2009)
- 김민수, "기울어진 GaAs(100) 기판 위에 성장된 InAs 박막 특성에 대한 As BEP 효과", 한국표면공학회지, 43(4), pp.176~179 (2010), 한국표면공학회
- Lu Long, "A Doctoral Dissertation of Gyeongsang National Univ", pp.105~ (2004), Gyeong Sang National Univ